Search

Binary AsxSe100−x alloys from the border of a glass-forming region (65 < x < 70) subjected to nanomilling in dry and dry–wet modes are characterized by the XRPD, micro-Raman scattering (micro-RS) and revised positron annihilation lifetime (PAL) methods complemented by a disproportionality analysis using the quantum–chemical cluster modeling approach. These alloys are examined with respect to tetra-arsenic biselenide As4Se2 stoichiometry, realized in glassy g-As65Se35, glassy–crystalline g/c-As67Se33 and glassy–crystalline g/c-As70Se30. From the XRPD results, the number of rhombohedral As and cubic arsenolite As2O3 phases in As-Se alloys increases after nanomilling, especially in the wet mode realized in a PVP water solution. Nanomilling-driven amorphization and reamorphization transformations in these alloys are identified by an analysis of diffuse peak halos in their XRPD patterning, showing the interplay between the levels of a medium-range structure (disruption of the intermediate-range ordering at the cost of an extended-range one). From the micro-RS spectroscopy results, these alloys are stabilized by molecular thioarsenides As4Sen (n = 3, 4), regardless of their phase composition, remnants of thioarsenide molecules destructed under nanomilling being reincorporated into a glass network undergoing a polyamorphic transition. From the PAL spectroscopy results, volumetric changes in the wet-milled alloys with respect to the dry-milled ones are identified as resulting from a direct conversion of the bound positron–electron (Ps, positronium) states in the positron traps. Ps-hosting holes in the PVP medium appear instead of positron traps, with ~0.36–0.38 ns lifetimes ascribed to multivacancies in the As-Se matrix. The superposition of PAL spectrum peaks and tails for pelletized PVP, unmilled, dry-milled, and dry–wet-milled As-Se samples shows a spectacular smoothly decaying trend. The microstructure scenarios of the spontaneous (under quenching) and activated (under nanomilling) decomposition of principal network clusters in As4Se2-bearing arsenoselenides are recognized. Over-constrained As6·(2/3) ring-like network clusters acting as pre-cursors of the rhombohedral As phase are the main products of this decomposition. Two spontaneous processes for creating thioarsenides with crystalline counterparts explain the location of the glass-forming border in an As-Se system near the As4Se2 composition, while an activated decomposition process for creating layered As2Se3 structures is responsible for the nanomilling-driven molecular-to-network transition. [ABSTRACT FROM AUTHOR]

Polyamorphic transformations driven by high-energy mechanical ball milling (nanomilling) are recognized in a melt-quenched glassy alloy of tetra-arsenic triselenide (As4Se3). We employed XRPD analysis complemented by thermophysical heat-transfer and micro-Raman spectroscopy studies. A straightforward interpretation of the medium-range structural response to milling-driven reamorphization is developed within a modified microcrystalline model by treating diffuse peak-halos in the XRPD patterns of this alloy as a superposition of the Bragg-diffraction contribution from inter-planar correlations, which are supplemented by the Ehrenfest-diffraction contribution from inter-atomic and/or inter-molecular correlations related to derivatives of thioarsenide As4Sen molecules, mainly dimorphite-type As4Se3 ones. These cage molecules are merely destroyed under milling, facilitating the formation of a polymerized network with enhanced calorimetric heat-transfer responses. Disruption of intermediate-range ordering, due to weakening of the FSDP (the first sharp diffraction peak), accompanied by an enhancement of extended-range ordering, due to fragmentation of structural entities responsible for the SSDP (the second sharp diffraction peak), occurs as an interplay between medium-range structural levels in the reamorphized As4Se3 glass alloy. Nanomilling-driven destruction of thioarsenide As4Sen molecules followed by incorporation of their remnants into a glassy network is proved by micro-Raman spectroscopy. Microstructure scenarios of the molecular-to-network polyamorphic transformations caused by the decomposition of the As4Se3 molecules and their direct destruction under grinding are recognized by an ab initio quantum-chemical cluster-modeling algorithm. [ABSTRACT FROM AUTHOR]

Multifunctional nanocomposites from an equimolar As4S4/Fe3O4 cut section have been successfully fabricated from coarse-grained bulky counterparts, employing two-step mechanochemical processing in a high-energy mill operational in dry- and wet-milling modes (in an aqueous solution of Poloxamer 407 acting as a surfactant). As was inferred from the X-ray diffraction analysis, these surfactant-free and surfactant-capped nanocomposites are β-As4S4-bearing nanocrystalline–amorphous substances supplemented by an iso-compositional amorphous phase (a-AsS), both principal constituents (monoclinic β-As4S4 and cubic Fe3O4) being core–shell structured and enriched after wet milling by contamination products (such as nanocrystalline–amorphous zirconia), suppressing their nanocrystalline behavior. The fluorescence and magnetic properties of these nanocomposites are intricate, being tuned by the sizes of the nanoparticles and their interfaces, dependent on storage after nanocomposite fabrication. A specific core–shell arrangement consisted of inner and outer shell interfaces around quantum-confined nm-sized β-As4S4 crystallites hosting a-AsS, and the capping agent is responsible for the blue-cyan fluorescence in as-fabricated Poloxamer capped nanocomposites peaking at ~417 nm and ~442 nm, while fluorescence quenching in one-year-aged nanocomposites is explained in terms of their destroyed core–shell architectures. The magnetic co-functionalization of these nanocomposites is defined by size-extended heterogeneous shells around homogeneous nanocrystalline Fe3O4 cores, composed by an admixture of amorphous phase (a-AsS), nanocrystalline–amorphous zirconia as products of contamination in the wet-milling mode, and surfactant. [ABSTRACT FROM AUTHOR]

Copyright of Tunel is the property of Ceska Tunelarska Asociace ITA-AITES, z.s and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)

The melt‐quenched glassy‐crystalline As70Se30 alloys subjected to nanomilling in dry and combined dry‐wet modes are probed by positron annihilation lifetime (PAL) spectroscopy. Modified Positronics approach parameterizing conversion of Ps‐hosting holes in positron trapping sites is applied to identify volumetric changes in the polyvinylpyrrolidone (PVP) stabilized alloys in respect to dry‐milled ones. Under transition from wet‐ to dry‐milled arsenoselenide probes, positron traps with defect‐specific lifetime ascribed to multiatomic vacancies in As–Se network appear instead of Ps‐decaying sites preferentially in PVP environment, these changes occurring in the oxidized arsenoselenide matrix. [ABSTRACT FROM AUTHOR]

StopBac is an innovative silver‐impregnated antimicrobial dressing specifically designed to reduce surgical site infections and enhance healing. The primary objective of this study was to compare infection healing rate at 30 days after surgery between primarily closed surgical wounds covered with StopBac and those covered with Cosmorpor, a standard surgical dressing. Between 1.3.2023 and 30.4.2023, we conducted a prospective screening of all patients undergoing surgical operations within a single surgical department. Patients were randomised into either the Cosmopor group or the StopBac group. Outcome measures were superficial and deep surgical site infections and healed wounds. Data concerning patient and surgical factors were prospectively collected and analysed. The analysis comprised 275 patients, divided into two groups: 140 patients in the StopBac group and 135 in the Cosmopor group. The StopBac dressing was associated with a reduced rate of infection, with an odds ratio of 0.288 (p < 0.001), and an increased likelihood of wound healing at 30 days after surgery. The odds ratio for healing at 30 days was 4.661 (p < 0.001). StopBac was associated with a lower incidence of surgical wound infections and a higher probability of healing at 30 days after surgery, when compared with standard dressing. [ABSTRACT FROM AUTHOR]