Cu 2 ZnSnS 4 (CZTS) thin films were prepared by sulfurizing precursors deposited by electroplating. The precursors (Cu/Sn/Zn stacked layers) were deposited by electroplating sequentially onto Mo-coated glass substrates. Aqueous solutions containing copper sulfate for Cu plating, tin sulfate for Sn plating and zinc sulfate for Zn plating were used as the electrolytes. The precursors were sulfurized by annealing with sulfur at temperatures of 300, 400, 500 and 600 °C in an N 2 gas atmosphere. The X-ray diffraction peaks attributable to CZTS were detected in thin films sulfurized at temperatures above 400 °C. A photovoltaic cell using a CZTS thin film produced by sulfurizing an electroplated Sn-rich precursor at 600 °C exhibited an open-circuit voltage of 262 mV, a short-circuit current of 9.85 mA/cm 2 and an efficiency of 0.98%.

Stacked precursors of Cu, Sn, and Zn were fabricated on glass/Mo substrates by electron beam evaporation. Six kinds of precursors with different stacking sequences were prepared by sequential evaporation of Cu, Sn, and Zn with substrate heating. The precursors were sulfurized at temperatures of 560 °C for 2 h in an atmosphere of N2 + sulfur vapor to fabricate Cu2ZnSnS4 (CZTS) thin films for solar cells. The sulfurized films exhibited X-ray diffraction peaks attributable to CZTS. Solar cells using CZTS thin films prepared from six kinds of precursors were fabricated. As a result, the solar cell using a CZTS thin film produced by sulfurization of the Mo/Zn/Cu/Sn precursor exhibited an open-circuit voltage of 478 mV, a short-circuit current of 9.78 mA/cm2, a fill factor of 0.38, and a conversion efficiency of 1.79%.