Search

Extracellular matrix (ECM) products have the potential to improve cellular attachment and promote tissue‐specific development by mimicking the native cellular niche. In this study, the therapeutic efficacy of an ECM substratum produced by bone marrow stem cells (BM‐MSCs) to promote bone regeneration in vitro and in vivo were evaluated. Fluorescence‐activated cell sorting analysis and phenotypic expression were employed to characterize the in vitro BM‐MSC response to bone marrow specific ECM (BM‐ECM). BM‐ECM encouraged cell proliferation and stemness maintenance. The efficacy of BM‐ECM as an adjuvant in promoting bone regeneration was evaluated in an orthotopic, segmental critical‐sized bone defect in the rat femur over 8 weeks. The groups evaluated were either untreated (negative control); packed with calcium phosphate granules or granules+BM‐ECM free protein and stabilized by collagenous membrane. Bone regeneration in vivo was analyzed using microcomputed tomography and histology. in vivo results demonstrated improvements in mineralization, osteogenesis, and tissue infiltration (114 ± 15% increase) in the BM‐ECM complex group from 4 to 8 weeks compared to mineral granules only (45 ± 21% increase). Histological observations suggested direct apposition of early bone after 4 weeks and mineral consolidation after 8 weeks implantation for the group supplemented with BM‐ECM. Significant osteoid formation and greater functional bone formation (polar moment of inertia was 71 ± 0.2 mm4 with BM‐ECM supplementation compared to 48 ± 0.2 mm4 in untreated defects) validated in vivo indicated support of osteoconductivity and increased defect site cellularity. In conclusion, these results suggest that BM‐ECM free protein is potentially a therapeutic supplement for stemness maintenance and sustaining osteogenesis. [ABSTRACT FROM AUTHOR]

Critically sized bone defects are often compounded by infectious complications. The standard of care consists of bone autografts with systemic antibiotics. These injuries and treatments lead to donor site morbidity, antibiotic resistant strains of bacteria, and often end stage amputation. This study proposes an alternative to the autograft using a porous, hydroxyapatite (HA) scaffold evaluated with and without infection and antibiotics. Twenty‐four New Zealand white rabbits received either our HA scaffold or a pulverized autograft (PBA) within a surgically created critical‐sized defect in the femur. The two grafts were evaluated in either septic or aseptic defects and with or without antibiotic treatment. The HA scaffolds were characterized with micro computed tomography. Post‐euthanasia, micro computed tomography, histology, and white blood cells component analysis were completed. The HA had significantly greater (p <.001) mineralization to total volume than the PBA groups with 27.56% and 14.88%, respectively, and the septic HA groups were significantly greater than the aseptic groups both with and without antibiotics (p =.016). The bone quality denoted by bone mineral density was also significantly greater (p <.001) in the HA groups (67.01 ± 0.38 mgHA/cm3) than the PBA groups (64.66 ± 0.85 mgHA/cm3). The HA scaffold is a viable alternative to the bone autograft in defects with and without infection as shown by the quality and quantity of bone. [ABSTRACT FROM AUTHOR]

Purpose: The frequency of alveolar ridge resorption and crestal bone loss emphasizes the clinical need for bone graft substitutes to improve local bone quality prior to dental implant placement. Microcomputed tomography has been extensively employed to estimate bone quality more objectively (ie, quantitatively) by relating it to architectural parameters. In the present study, the mechanical properties of open cellular fully interconnected bilayer hydroxyapatite scaffolds, which mimicked the cortical shell/trabecular core architecture of human bone, were investigated for suitability as bone graft substitutes for maxillofacial reconstruction. Materials and Methods: Hydroxyapatite scaffolds with different architectures were fabricated using polymeric template pore sizes of 450 or 340 µm for the inner trabecular cores and 200 or 250 µm for the outer cortical shells in three different core-to-shell volume ratios. The architectural and mechanical properties and fluid permeability of the scaffolds were compared to reported values for maxillofacial bone. Results: Whereas the elastic moduli of the scaffolds were comparable, their compressive strength was observed to be in the lower range of human mandibular trabecular bone. The microcomputed tomography architectural indices for the scaffolds were comparable to those of human trabecular bone at different locations in the human body, including the maxilla and mandible. Scaffold compressive strength, elastic modulus, and fluid conductance were 0.3 to 2.3 MPa, 40.9 to 668.1 MPa, and 8.8 to 49.9 × 10-10 m3s-1Pa-1, respectively. Conclusion: Open-pore bilayer scaffolds can be fabricated to exhibit sufficient mechanical integrity for maxillofacial bone graft applications to match specific bone site architecture while providing sufficient permeability to sustain bone regeneration. [ABSTRACT FROM AUTHOR]

To examine the effect of scaffold pore size on bone regeneration within hydroxyapatite scaffolds in large segmental defects, this study evaluated two porous interconnected architectures having similar porosity and strut thickness but different pore sizes. Using a 10 mm segmental rabbit radius defect model, a bilayer scaffold architecture mimicking the cortical-cancellous organization of bone (pore size 200 µm outer layer, 450 µm inner layer) was compared to a purely trabecular-like architecture (pore size 340 µm) and an untreated defect. Bone regeneration was measured using micro-computed tomography and histology after four and eight weeks of in vivo implantation, and the mechanical strength of the defect site after eight weeks’ implantation was assessed using flexural testing. Although both bilayer and trabecular architectures promoted bone growth, the trabecular scaffolds were observed to have more uniform new bone distribution within the scaffold interior at four weeks and greater bone regeneration overall after eight weeks’ implantation (149 ± 9 mm3 compared to 121 ± 8 mm3 in the bilayer and 66 ± 14 mm3 in the defect). Additionally, the trabecular scaffolds were observed to exhibit significantly greater flexural strength (124% increase) and toughness (388% increase) when compared to the empty defects after eight weeks’ implantation. It was concluded from this study that a larger uniform pore size led to greater functional bone regeneration over a longer implantation period for large segmental defects. [ABSTRACT FROM AUTHOR]

The goal of this in vivo study was to evaluate the osteoinductive and angio-inductive properties of a porous hydroxyapatite (HAp) scaffold with immobilized recombinant bone morphogenetic protein-2 (rhBMP-2) on the surface. It was hypothesized in this study that the use of a rhBMP-2 incorporated polyelectrolyte coating on the HAp scaffold would allow for controlled exposure of rhBMP-2 into the tissue and would provide a sound platform for tissue growth. The scaffolds were characterized for porosity and interconnectivity using pycnometry, scanning electron microscopy and micro-ct. These scaffolds were then divided into the following four groups: (a) HAp scaffold (n-HAp group), (b) rhBMP-2 physically adsorbed on HAp scaffold (HAp-BMP-2 Group), (c) polyelectrolyte coating on HAp scaffold without rhBMP-2 (HAp-PEI Scaffold Group), and (d) polyelectrolyte coating tethered with rhBMP-2 on HAp scaffold (HAp-PEI-BMP-2 Scaffold Group). Using 18 skeletally matured New Zealand white rabbits, these scaffolds were evaluated in a nonload bearing femoral condyle plug model. The negative controls for this study have defects that were left untreated and the positive controls have defects that were filled with autologous bone graft harvested from epsilateral iliac crest. Bone induction, vessel growth, and scaffold-bone contact were analyzed after 8-week implantation using micro-CT and histomorphometry. It was concluded from this study that the use of scaffold with an attached rhBMP-2 increased the vascularization around the implant when compared with the uncoated n-HAp scaffold, a necessary step of bone regeneration. The open-pore HAp scaffold was also concluded to provide a platform for tissue growth, drug loading, and tissue interaction. © 2012 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 2012. [ABSTRACT FROM AUTHOR]

The objective of this research was to investigate the bone formation and angio-conductive potential of hydroxyapatite (HA) scaffolds closely matched to trabecular bone in a canine segmental defect after 3 and 12 weeks post implantation. Histomorphometric comparisons were made between naturally forming trabecular bone (control) and defects implanted with scaffolds fabricated with micro-size (M-HA) and nano-size HA (N-HA) ceramic surfaces. Scaffold architecture was similar to trabecular bone formed in control defects at 3 weeks. No significant differences were identified between the two HA scaffolds; however, significant bone in-growth was observed by 12 weeks with 43.9 +/- 4.1% and 50.4 +/- 8.8% of the cross-sectional area filled with mineralized bone in M-HA and N-HA scaffolds, respectively. Partially organized, lamellar collagen fibrils were identified by birefringence under cross-polarized light at both 3 and 12 weeks post implantation. Substantial blood vessel infiltration was identified in the scaffolds and compared with the distribution and diameter of vessels in the surrounding cortical bone. Vessels were less numerous but significantly larger than native cortical Haversian and Volkmann canals reflecting the scaffold architecture where open spaces allowed interconnected channels of bone to form. This study demonstrated the potential of trabecular bone modeled, highly porous and interconnected, HA scaffolds for regenerative orthopedics., (Copyright 2008 Wiley Periodicals, Inc.)

To meet the challenge of regenerating bone lost to disease or trauma, biodegradable scaffolds are being investigated as a way to regenerate bone without the need for an auto- or allograft. Here, we have developed a novel microsphere-based chitosan/nanocrystalline calcium phosphate (CaP) composite scaffold and investigated its potential compared to plain chitosan scaffolds to be used as a bone graft substitute. Composite and chitosan scaffolds were prepared by fusing microspheres of 500-900 microm in diameter, and porosity, degradation, compressive strength, and cell growth were examined. Both scaffolds had porosities of 33-35% and pore sizes between 100 and 800 . However, composite scaffolds were much rougher and, as a result, had 20 times more surface area/unit mass than chitosan scaffolds. The compressive modulus of hydrated composite scaffolds was significantly higher than chitosan scaffolds (9.29 +/- 0.8 MPa vs. 3.26 +/- 2.5 MPa), and composite scaffolds were tougher and more flexible than what has been reported for other chitosan-CaP composites or CaP scaffolds alone. Using X-ray diffraction, scaffolds were shown to contain partially crystalline hydroxyapatite with a crystallinity of 16.7% +/- 6.8% and crystallite size of 128 +/- 55 nm. Fibronection adsorption was increased on composite scaffolds, and cell attachment was higher on composite scaffolds after 30 min, although attachment rates were similar after 1 h. Osteoblast proliferation (based on dsDNA measurements) was significantly increased after 1 week of culture. These studies have demonstrated that composite scaffolds have mechanical properties and porosity sufficient to support ingrowth of new bone tissue, and cell attachment and proliferation data indicate composite scaffolds are promising for bone regeneration.