This study presents the investigation of the influence of heat treatment on microstructure, hardness and tensile properties of high-speed selective laser melted Ti6Al4V components. Heat treatment was performed to obtain an improved microstructure with enhanced hardness and tensile properties. It was found that the acicular martensitic α′ structure on the as-built sample lead to high hardness, yield strength and ultimate tensile strengths of 389±10 HV0.3, 949 ± 10 MPa and 1045 ± 3 MPa, respectively,with a low ductility of 5%. Heat treatment transformed the martensitic α′ structure into lamella α + β phases, with heat treatment at 1000 °C resultingin the most improved hardness and ductility from 389 ± 10 HV0.3 and 5% to 325 ± 20 HV0.3 and 13%, and a decrease in yield and ultimate tensile strength from 949 ± 10 MPa and 1045 ± 13MPa to 835 ± 11 MPa and 911 ± 5 MPa, respectively.

The following article looks at using scanning electron microscopy- electron back scatter diffraction techniques to study recrystallisation structures produced through hot rolling of 436 ferritic stainless steel. Characterisation of recrystallisation textures was undertaken through analysis of misorientation angle distribution diagrams, orientation distribution function maps, inverse pole figures and Taylor factor maps. These techniques were applied in a case study where typical industrial hot rolling conditions were simulated through uniaxial compression tests in a Bähr Dilatometer 850D, whereby the effect of strain rate and interpass time on recrystallisation structures was investigated.