Search

An isostatic hot-pressing technique for the fabrication of dense W samples' is presented. The samples’ microstructure and chemical content were analyzed. The most compact samples were received at 5 GPa pressure and 1500 and 2000 °C temperatures, with densities of 18.50 and 19.07 g/cm3, respectively. It has been established that high temperature exposure has a positive effect on both the microstructure and density. It is shown that as the sintering temperature increases, the porosity of the samples decreases from 32.31% to 0.94%, and their relative density increases from 67.69% to 99.06%. The crystal structure investigation revealed that all the samples contain the main body-centered cubic W phase, and the availability of the WO2 phase is observed just after the temperature of sintering increases above 1000 °C, which is confirmed by the appearance of 111 and 22-2 reflections. A study of the shielding effectiveness against gamma-radiation was carried out using the Phy-X/PSD software. A gamma-ray source of Co60 with energies of 0.8–2.5 MeV was applied for the calculations. The results were calculated for the sample with the highest density (19.07 g/cm3) and compared with the calculations for Pb. The W shielding effectiveness main parameters are determined: linear attenuation coefficient (at 0.8 MeV–1.46 cm-1), mean free path (at 2.5 MeV–1.2 cm) and half value layer (at 2.5 MeV–0.86 cm). These values turned out to be higher than for Pb, which makes shields based on W promising for use in the field of radiation protection.

The results of studies on the wettability properties and preparation of porous anodic alumina (PAA) membranes with a 3.3 ± 0.2 μm thickness and a variety of pore sizes are presented in this article. The wettability feature results, as well as the fabrication processing characteristics and morphology, are presented. The microstructure effect of these surfaces on wettability properties is analyzed in comparison to outer PAA surfaces. The interfacial contact angle was measured for amorphous PAA membranes as-fabricated and after a modification technique (pore widening), with pore sizes ranging from 20 to 130 nm. Different surface morphologies of such alumina can be obtained by adjusting synthesis conditions, which allows the surface properties to change from hydrophilic (contact angle is approximately 13°) to hydrophobic (contact angle is 100°). This research could propose a new method for designing functional surfaces with tunable wettability. The potential applications of ordinary alumina as multifunctional films are demonstrated.

The W–Cu composites with nanosized grain boundaries and high effective density were fabricated using a new fast isostatic hot pressing method. A significantly faster method was proposed for the formation of W–Cu composites in comparison to the traditional ones. The influence of both the high temperature and pressure conditions on the microstructure, structure, chemical composition, and density values were observed. It has been shown that W–Cu samples have a polycrystalline well-packed microstructure. The copper performs the function of a matrix that surrounds the tungsten grains. The W–Cu composites have mixed bcc-W (sp. gr. Im 3¯ m) and fcc-Cu (sp. gr. Fm 3¯ m) phases. The W crystallite sizes vary from 107 to 175 nm depending on the sintering conditions. The optimal sintering regimes of the W–Cu composites with the highest density value of 16.37 g/cm3 were determined. Tungsten–copper composites with thicknesses of 0.06–0.27 cm have been fabricated for the radiation protection efficiency investigation against gamma rays. It has been shown that W–Cu samples have a high shielding efficiency from gamma radiation in the 0.276–1.25 MeV range of energies, which makes them excellent candidates as materials for radiation protection.

The paper discusses the formation of Ta2O5 pillars with Ni tips during thin porous anodic alumina through-mask anodization on Si/SiO2 substrates. The tantalum nanopillars were formed through porous masks in electrolytes of phosphoric and oxalic acid. The Ni tips on the Ta2O5 pillars were formed via vacuum evaporation through the porous mask. The morphology, structure, and magnetic properties at 4.2 and 300 K of the Ta2O5 nanopillars with Ni tips have been studied using scanning electron microscopy, X-ray diffraction, and vibrating sample magnetometry. The main mechanism of the formation of the Ta2O5 pillars during through-mask anodization was revealed. The superparamagnetic behavior of the magnetic hysteresis loop of the Ta2O5 nanopillars with Ni tips was observed. Such nanostructures can be used to develop novel functional nanomaterials for magnetic, electronic, biomedical, and optical nano-scale devices.