The effect of PbO addition with different concentrations on four synthesized zinc titanium borate glasses with the chemical formula xPbO-(75-x) B2O3-10ZnO-10BaO-5TiO2 (x = 30, 35, 40, and 45 mol%) was explored in this study. The partial PbO substitution for B2O3 increases the fabricated glasses' density by ≈ 20% from 5.31 to 6.37 g/cm3, respectively, with raising the PbO concentrations between 30 and 45 mol.%, respectively. Besides, the substitution mentioned above enhances the gamma-ray attenuation properties where the linear attenuation coefficient increased between 69.911 and 102.245 cm−1 (at 0.033 MeV), 0.341–0.415 cm−1 (at 1 MeV), and 0.200–0.262 cm−1 (at 10 MeV), increasing the PbO concentration between 30 and 45 mol.%, respectively. Simultaneously, increases in the PbO concentration within the fabricated glasses decrease the lead's equivalent thickness between 3.82 and 2.61 cm (at 0.033 MeV), 2.35–1.93 cm (at 1 MeV), and 2.81–2.14 cm (at 10 MeV). In contrast, substituting PbO for B2O3 compounds diminishes the fabricated glasses' mechanical properties, where the microhardness decreased by 13.5 % from 4.24 to 3.67 GPa. The lead equivalent thickness (Deq) values at 0.66 MeV were found equal to 2.410, 2.232, 2.078, and 1.945 cm, and at 1.112 MeV, these values were found equal to 2.222, 2.081, 1.956, and 1.829 cm for G1, G2, G3, and G4, respectively.

The present work aims to fabricate Na1+xZr2SixP3-xO12 compound at various calcination temperatures based on the zircon mineral. The fabricated compound was calcinated at 250, 500, and 1000°C. The effect of calcination temperature on the structure, crystal phase, and radiation shielding properties was studied for the fabricated compound. The X-ray diffraction diffractometer demonstrates that, the monoclinic crystal phase appeared at a calcination temperature of 250°C and 500°C is totally transformed to a high-symmetry hexagonal crystal phase under a calcination temperature of 1000°C. The radiation shielding capacity was also qualified for the fabricated compounds using the Monte Carlo N-Particle transport code in the γ-photons energy interval between 15keV and 122keV. The impacts of calcination temperature on the γ-ray shielding behavior were clarified in the present study, where the linear attenuation coefficient was enhanced by 218% at energy of 122keV, when the calcination temperature increased from 250 to 1000°C, respectively.