Photoacoustic phase and amplitude spectra of YBa2Cu3O7– d samples synthesised 18 years ago were measured and numerically analysed. The value of thermal diffusivity obtained on the aged samples was lower than the values obtained for fresh samples. Far infrared spectra of YBa2Cu3O7– d samples synthesised 18 years ago were recorded and analysed enabling determination of reflectivity peak phonon frequencies present at room temperature. X-ray diffraction analysis and far infrared reflectivity measurements enabled determination of a slight change of the oxygen content with time. The YBa2Cu3O7– d samples synthesised 18 years ago still remained superconducting, which was confirmed by resistivity measurements of the samples between 50 K and room temperature where the critical temperature was reduced from 93 to 73 K. Atomic force microscopy, scanning electron microscopy and energy dispersive X-ray microanalytical measurements were also performed confirming the composition of the sample.

This research is focused on structural and electrical characterisation of tin oxide (SnO2) applied as a thick film and investigation of its properties as gas sensitive material. Micron sized SnO2 powder was milled in an agate mill for six hours to fabricate SnO2 nanopowder, which was afterwards sieved by 325 mesh sieve and characterized by XRD and SEM. This powder was used as functional part in the production of thick film tin oxide paste containing a resin vehicle with 4 wt. % nanosize glass frits acting as permanent binder. The glass frits where additionally milled for twelve hours in the agate mills to nanosized powder and sieved by a 325 mesh sieve as well. The achieved thick film paste was screen printed on alumina and fired at 850oC peak temperature for 10 minutes in air. After the sintering process, thick film samples where characterized by X-ray powder diffraction (XRD) and scanning electron microscopy (SEM). The reflectivity was measured on the same samples by UV-VIS spectrophotometer: the band gap was determined from the slope of reflectance. After that a matrix of different interdigitated electrode structure of PdAg paste was printed and sintered using the mentioned sintering conditions. The tin oxide thick film was printed over the interdigitated electrodes as a top layer and sintered again under the same conditions. The total electrical resistance was measured as a function of the electrode spacing and temperature. A negative temperature coefficient (NTC) was identified and measured in the range from room temperature (27degC) to 180degC in a climate chamber. Finally the samples were placed into a gas reactor with NOx and CO gas and the resistance was measured in the same temperature range (27degC-200degC).