Search

Abstract In this study, synthesis and assessment of the corrosion inhibition of four new binary heterocyclic pyrimidinones on CS in 1.0 M hydrochloric acid solutions at various temperatures (30–50 °C) were investigated. The synthesized molecules were designed and synthesized through Suzuki coupling reaction, the products were identified as 5-((5-(3,4,5-trimethoxyphenyl)furan-2-yl)methylene)pyrimidine-2,4,6(1H,3H,5H)-trione (HM-1221), 2-thioxo-5-((5-(3,4,5-trimethoxyphenyl)furan-2-yl)methylene)dihydropyrimidine-4,6(1H,5H)-dione (HM-1222), 1,3-diethyl-2-thioxo-5-((5-(3,4,5-trimethoxyphenyl)furan-2-yl)methylene)dihydropyrimidine-4,6(1H,5H)-dione (HM-1223) and 1,3-dimethyl-5-((5-(3,4,5-trimethoxyphenyl)furan-2-yl)methylene)pyrimidine-2,4,6(1H,3H,5H)-trione (HM-1224). The experiments include weight loss measurements (WL), electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization (PDP). From the measurements, it can be shown that the inhibition efficiency (η) of these organic derivatives increases with increasing the doses of inhibitors. The highest η recorded from EIS technique were 89.3%, 90.0%, 92.9% and 89.7% at a concentration of 11 × 10−6 M and 298 K for HM-1221, HM-1222, HM-1223, and HM-1224, respectively. The adsorption of the considered derivatives fit to the Langmuir adsorption isotherm. Since the ΔG o ads values were found to be between − 20.1 and − 26.1 kJ mol−1, the analyzed isotherm plots demonstrated that the adsorption process for these derivatives on CS surface is a mixed-type inhibitors. Scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDX), atomic force microscope (AFM) and Fourier- transform infrared spectroscopy (FTIR) were utilized to study the surface morphology, whereby, quantum chemical analysis can support the mechanism of inhibition. DFT data and experimental findings were found in consistent agreement. Graphical Abstract

Abstract Copper-nickel alloys are the preferred material for desalination facilities and condensers and heat exchangers that use saltwater as a coolant. The eco-friendly compounds especially Carob fruit extract (CFE) has emerged as excessive green corrosion inhibitor for alloys. Cu-Ni alloys are widely used in various industries due to their excellent corrosion resistance. However, their performance can be compromised in aggressive environments like seawater (which is approximately 3.5% NaCl). To evaluate the corrosion behavior of these alloys and the effectiveness of corrosion inhibitors, researchers often employ weight loss, potentiodynamic polarization, and impedance spectroscopy techniques. The results showed that CFE exhibited a good ability to decrease the CR of alloys in 3.5% NaCl solution. The inhibition efficacy (IE) was reached to 92.6% and ̴ 83.2% at 300 ppm dose of CFE for Cu-10Ni alloy and Cu-30Ni alloy, respectively. The CR increases with temperature rising, but the addition of CFE reduces the CR, and the reduction depends on the dose of the extract. Adsorption of the extract gives a good fit to Langmuir, Temkin, and Freundlich isotherms model. The free adsorption energies of CFE on Cu-10Ni and Cu-30Ni alloys were 17.61 and 15.86 kJ mol−1, respectively, suggesting that CFE was weakly held to both alloys. The presence of a protective film on the alloys surface is confirmed by using scanning electron microscopy (SEM), energy dispersive X-ray (EDX) spectroscopy and atomic force microscope (AFM). The study suggests that utilizing affordable, natural substances as green corrosion inhibitors presents a new strategy for promoting both resource efficiency and environmental sustainability.

Abstract Aluminum corrosion inhibitors “{[CuI (CN)2(phen) CuII (CN)2(phen)]5H2O},(MOF1) and {[CuI(CN)2(phen)CuII(CN)2(phen)]5H2O}@TiO2 (MOF1@TiO2) were studied in one molar HCl solution”. The ML results for three different temperatures (25–45 °C) were compared with the results of PDP and EIS analyses. The adsorption of inhibitors on Al surfaces has been calculated and discussed by a Langmuir isotherm. The inhibitors that were created showed great effectiveness, with a noticeable increase in their inhibitory efficiency as the dosage was raised and the temperature was lowered. Inhibition efficiency each amounted to 88.6%, 84.5% at 400 ppm and 25 °C for MOF1@TiO2 and MOF1, respectively. Analyzing the polarization curves of synthesized inhibitors revealed that they were mixed-type inhibitors. Al was found to be surface inhibited when coated with a thin film of inhibitors, and “Al's surface morphology was assessed by different techniques such as scanning electron microscopy (SEM), energy dispersive X-ray (EDX) and atomic force microscope (AFM)”. “Theoretical models like quantum chemical and molecular dynamics simulation authenticated the experimental observation”. The MOFs exhibit exceptional corrosion resistance against Al when exposed to acidic environments, according to several tests.

In this study, we deployed green Melilotus officinalis extract (MOE) as a corrosion inhibitor for copper. The anticorrosion properties of MOE for Cu in 1 M HNO 3 were investigated by various experimental and numerical techniques, including potentiodynamic polarization (PDP), electrochemical impedance spectroscopy (EIS), and a weight loss (WL) method at different temperatures. Additionally, scanning electron microscopy (SEM) coupled with energy-dispersive X-ray analysis (EDX) and atomic force microscopy (AFM) were utilized to examine the surface morphology of Cu with and without the extract. By contrasting the inhibition effectiveness with and without the extract, the inhibition efficiency (% IE) was observed. The WL method revealed that 300 ppm of the extract had an IE of 93.8% for Cu immersed in one molar HNO 3 solution. The MOE was classified as a mixed type according to the PDP study since it delayed both cathodic and anodic processes, with a cathodic predominance. At 25-45 °C, MOE's free adsorption energies were 23.1-21.5 kJ mol -1 , showing that mixed-type adsorption occurred on the Cu surface. Additionally, the Langmuir adsorption isotherm and the adsorption data from the WL tests of MOE showed a good match. The extract could adsorb spontaneously onto the metal surface, according to the thermodynamic conditions. Analysis of the corrosion product using different techniques revealed that a protective layer had formed on the metal's surface. Hence, MOE had a good corrosive inhibitive effect on Cu in HNO 3 solution. It turned out that all the methods used gave consistent results., Competing Interests: There are no conflicts to declare., (This journal is © The Royal Society of Chemistry.)

In the present work, Verbena Officinalis (VO) leaf extract was used as potential corrosion inhibitor for the corrosion of carbon steel (CS) in 0.5 M H 2 SO 4 medium. Further, the corrosion inhibiting nature of VO leaf extract towards the CS was evaluated using mass loss (ML), potentiodynamic polarization (PDP), electrical impedance spectroscopy (EIS) and surface morphological analyses using atomic force microscope (AFM) and X-ray photoelectron spectroscopy (XPS) techniques. Calculation of activation energy E a ∗ using Arrhenius equation shows the increase in activation energy when adding the VO leaf extract in 0.5 M H 2 SO 4 medium and the maximum activation energy ( E a ∗  = 49.9 kJ mol -1 ) was observed for 1000 mg L -1 VO leaf extract in acid medium. The negative free energy values suggested the spontaneous and the stability of the adsorbed layer of VO leaf extract on the CS surface. Using EIS measurements, high percent inhibitory effectiveness of 91.1% for 1000 ppm solutions was achieved. With an increase in VO leaf extract dose, the double layer capacitance (C dl ) values fall while the values of charge transfer (R ct ) increase. This showed that a protective layer of VO leaf extract on CS surface was formed. The polarization curves showed that the VO leaf extract acts as a mixed-type inhibitor. It is discovered that the adsorption of VO leaf extract molecules adhering to the CS surface followed the Langmuir isotherm. The anti-corrosion action of VO leaf extract is fully demonstrated by some surface techniques., (© 2024. The Author(s).)