Search

Abstract The green methodologies of nanoparticles with plant extracts have received an increase of interest. Copper oxide nanoparticles (CuO NPs) have been utilized in a many of applications in the last few decades. The current study presents the synthesis of CuO NPs with aqueous extract of Morinda citrifolia as a stabilizing agent. The leaf extract of Morinda citrifolia was mixed with a solution of copper sulphate (CuSO4·5H2O) and sodium hydroxide as a catalyst. UV–visible spectroscopy, FTIR, XRD, SEM, TEM, and EDAX analysis were performed to study the synthesized CuO NPs. Particle size distribution of the synthesized CuO NPs have been measured with dynamic light scattering. The CuO NPs synthesized were highly stable, sphere-like, and have size of particles from 20 to 50 nm. Furthermore, as-formed CuO NPs shown strong antibacterial activity against the Gram-positive bacteria (Bacillus subtilis, and Staphylococcus aureus), and Gram-negative bacteria (Escherichia coli). CuO NPs revealed a similar trend was analysed for antifungal activity. The zone of inhibition for the fungi evaluated for Aspergillus flavus (13.0 ± 1.1), Aspergillus niger (14.3 ± 0.7), and Penicillium frequentans (16.8 ± 1.4). According to the results of this investigation, green synthesized CuO NPs with Morinda citrifolia leaf extract may be used in biomedicine as a replacement agent for biological applications.

Novel multinary nanocomposite using solvothermal method synthesized and studied for their use in supercapacitors and photocatalysis to degrade pollutants using characterization techniques XRD, SEM, EDX, FTIR, Raman, UV–Vis, Zeta potential and photoluminescence spectroscopy whereas electrochemical testing via EIS, CV and GCD analysis. Average crystalline size of 20.81 nm measured from XRD whereas EDX confirms GO suppression within nanocomposite. Mixed matrix like morphology is observable from SEM micrographs. The composite exhibited a band gap of 2.78 eV that could degrade MB dye at 94 % under direct sunlight consistent with first-order kinetics. Multiple distinctive peaks in FTIR spectra indicates various functional groups exsistence in the material alongwith zeta potential value of −17.9 mV. Raman spectra reveals D-band shifting to value 1361 cm−1 while the G-band shifts to 1598 cm−1 relative to GO. Furthermore electrochemical performance evaluated revealing electron transfer rate value 4.88 × 10−9 cms−1 with maximum capacitance about 7182 Fg-1 at a scan rate of 10 mVs−1 respectively. Power density ranges from 3591.18 to 2163 W/kg and energy density from 299 to 120 Wh/Kg as measured from GCD analysis. These findings indicates that novel multinary nanocomposite holds potential as an electrode material in supercapacitors and as a sunlight-driven photocatalyst for the degradation of water-borne organic pollutants.

Cu3SbSe4 is a potential p-type thermoelectric material, distinguished by its earth-abundant, inexpensive, innocuous, and environmentally friendly components. Nonetheless, the thermoelectric performance is poor and remains subpar. Herein, the electrical and thermal transport properties of Cu3SbSe4 were synergistically optimized by S alloying. Firstly, S alloying widened the band gap, effectively alleviating the bipolar effect. Additionally, the substitution of S in the lattice significantly increased the carrier effective mass, leading to a large Seebeck coefficient of ~730 μVK−1. Moreover, S alloying yielded point defect and Umklapp scattering to significantly depress the lattice thermal conductivity, and thus brought about an ultralow κlat ~0.50 Wm−1K−1 at 673 K in the solid solution. Consequently, multiple effects induced by S alloying enhanced the thermoelectric performance of the Cu3SbSe4-Cu3SbS4 solid solution, resulting in a maximum ZT value of ~0.72 at 673 K for the Cu3SbSe2.8S1.2 sample, which was ~44% higher than that of pristine Cu3SbSe4. This work offers direction on improving the comprehensive TE in solid solutions via elemental alloying.