Search

This paper describes the application of cold spray to the deposition of a diamond grade pre-coated with Cu and Ni. This is the first time that pre-coated diamond powders are used as the sole feedstock without the addition of binders (ductile phases) in cold spraying. The experimental results showed that it was possible to manufacture thick metal–diamond composite coatings onto an Al alloy substrate with high diamond fraction in the coating and without phase change. Results from this paper also have demonstrated a new methodology for the deposition of metal–diamond/ceramic composite coating with the cold spray technique.

Diamond-reinforced metal matrix composites (DMMC) have great potential for wear-resistance applications due to the superior hardness of the diamond component. Cold spray as an emerging coating technique is able to fabricate coatings or bulk materials without exceeding the material melting point, thereby significantly lowering the risk of oxidation, phase transformation, and excessive thermal residual stress. In this paper, thick DMMC coatings were deposited onto aluminum alloy substrate via cold spray of three feedstock powders: copper-clad diamond and pure copper, and their mixtures. It was found that, due to its low processing temperature, cold spray is able to prevent graphitization of the diamond in the DMMC coatings. Further to that, the original diamond phase was almost completely retained in the DMMC coatings. In case of the coatings fabricated from copper-clad diamond powders only, its mass fraction reached 43 wt.%, i.e. value higher than in any previous studies using conventional pre-mixed powders. Furthermore, it was found that the added copper content powders acted as a buffer, effectively preventing the fracture of the diamond particles in the coating. Finally, the wear test on the coatings showed that the cold sprayed DMMC coatings had excellent wear-resistance properties due to the diamond reinforcement.

This paper describes the application of cold spray to the deposition of a diamond grade pre-coated with Cu and Ni. This is the first time that pre-coated diamond powders are used as the sole feedstock without the addition of binders (ductile phases) in cold spraying. The experimental results showed that it was possible to manufacture thick metal–diamond composite coatings onto an Al alloy substrate with high diamond fraction in the coating and without phase change. Results from this paper also have demonstrated a new methodology for the deposition of metal–diamond/ceramic composite coating with the cold spray technique.

Diamond-reinforced metal matrix composites (DMMC) have great potential for wear-resistance applications due to the superior hardness of the diamond component. Cold spray as an emerging coating technique is able to fabricate coatings or bulk materials without exceeding the material melting point, thereby significantly lowering the risk of oxidation, phase transformation, and excessive thermal residual stress. In this paper, thick DMMC coatings were deposited onto aluminum alloy substrate via cold spray of three feedstock powders: copper-clad diamond and pure copper, and their mixtures. It was found that, due to its low processing temperature, cold spray is able to prevent graphitization of the diamond in the DMMC coatings. Further to that, the original diamond phase was almost completely retained in the DMMC coatings. In case of the coatings fabricated from copper-clad diamond powders only, its mass fraction reached 43 wt.%, i.e. value higher than in any previous studies using conventional pre-mixed powders. Furthermore, it was found that the added copper content powders acted as a buffer, effectively preventing the fracture of the diamond particles in the coating. Finally, the wear test on the coatings showed that the cold sprayed DMMC coatings had excellent wear-resistance properties due to the diamond reinforcement.

This paper describes the application of cold spray to the deposition of a diamond grade pre-coated with Cu and Ni. This is the first time that pre-coated diamond powders are used as the sole feedstock without the addition of binders (ductile phases) in cold spraying. The experimental results showed that it was possible to manufacture thick metal–diamond composite coatings onto an Al alloy substrate with high diamond fraction in the coating and without phase change. Results from this paper also have demonstrated a new methodology for the deposition of metal–diamond/ceramic composite coating with the cold spray technique.