Search

Contains fulltext : 47746.pdf (publisher's version ) (Closed access), The objective of the study presented here was to investigate the bone inductive properties as well as release kinetics of rhTGF-beta1- and rhBMP-2-loaded Ti-fiber mesh and CaP cement scaffolds. Therefore, Ti-fiber mesh and porous CaP cement scaffolds were provided with these growth factors and inserted in subcutaneous and cranial implant locations in rats and rabbits. In vitro, a rapid release of rhTGF-beta1 was observed during the first 2 h of the Ti-fiber mesh scaffolds. During this time, more than 50% of the total dose of rhTGF-beta1 was released. Following this initial peak, a decline in the level of rhTGF-beta1 occurred. After 1 week, the entire theoretical initial dose was observed to have been released. This in contrast to the rhTGF-beta1 and rhBMP-2 release of the porous CaP cement scaffolds. Here, no substantial initial burst release was observed. The scaffolds showed an initial release of about 1% after 1 day, followed by an additional marginal release after 1 week. Histological analysis revealed excellent osteoconductive properties of non-loaded Ca-P material. Inside non-loaded Ti-mesh fiber scaffolds, also bone ingrowth occurred. Quantification of the bone ingrowth showed that bone formation was increased significantly in all scaffold materials by administration of rhTGF-beta1 and rhBMP-2. Consequently, we conclude that the release kinetics of growth factors from porous CaP cement differs from other scaffold materials, like metals and polymers. Nevertheless, orthotopic bone formation in a rabbit cranial defect model was stimulated in rhTGF-beta1- and rhBMP-2-loaded CaP cement and Ti-fiber mesh scaffolds compared with non-loaded implants.

Item does not contain fulltext, To evaluate the osteoinductive effects of recombinant human bone morphogenetic protein (rhBMP)-2 during the early stages of rat ectopic bone formation, we prepared two distinct carriers. Two carriers, insoluble bone matrix (IBM) and fibrous glass membrane (FGM) were combined with rhBMP-2 and implanted into the backs of rats to evaluate the osteoinductive effects of the two rhBMP-2 carrier systems. Insoluble bone matrix particle size was 320 to 620 microm. Fibrous glass membrane was constructed from unwoven glass fibers 1 microm in diameter. Alkaline phosphatase (ALP) activity and type II collagen were detected in IBM/rhBMP-2 at 5 days postimplantation. Calcium (Ca) was also detected in IBM/rhBMP-2 at 7 and 9 days postimplantation. In contrast, ALP and type II collagen were detected in FGM/rhBMP-2 at 7 days. Calcium was undetected, indicating that the bone formation in IBM/rhBMP-2 proceeded faster than in FGM/rhBMP-2 during the early stage of BMP-induced osteogenesis. In addition, mRNA expression level of KDR, a receptor for vascular endothelial growth factor, was also increased in IBM/rhBMP-2. To investigate the in vivo release profile of rhBMP-2, iodine 125 ((125)I)-labeled BMP-2-incorporating IBM and FGM implants were inserted into the back subcutis of mice. More than 60% of the rhBMP-2 was released from the IBM/rhBMP-2 carrier within 1 day after implantation, whereas 50% of the rhBMP-2 was released from the FGM/rhBMP-2 10 days postimplantation. These results indicated that osteo- and chondrogenesis depends highly upon the geometry of the carrier and the in situ retention of rhBMP-2 during the early stage of rhBMP-2 induced bone formation.

Item does not contain fulltext, On the basis of currently available knowledge, we hypothesize that the initial bone formation, as induced by bone morphogenetic protein (BMP), is influenced by the chemical composition and three-dimensional spatial configuration of the used carrier material. Therefore, in the current study, the osteoinductive properties of porous titanium (Ti) fiber mesh with a calcium phosphate (Ca-P) coating (Ti-CaP), insoluble bone matrix (IBM), fibrous glass membrane (FGM), and porous particles of hydroxy apatite (PPHAP) loaded with rhBMP-2 were compared in a rat ectopic assay model at short implantation periods. Twelve Ti-CaP, 12 IBM, 12 FGM, and 12 PPHAP implants, loaded with rhBMP-2, were subcutaneously placed in 16 Wistar King rats. The rats were sacrificed at 3, 5, 7, and 9 days post-operative, and the implants were retrieved. Histological analysis demonstrated that IBM and Ti-CaP had induced ectopic cartilage and bone formation by 5 and 7 days, respectively. However, in PPHAP, bone formation and cartilage formation were seen together at 7 days. At 9 days, in Ti-CaP, IBM, and PPHAP, cartilage was seen together with trabecular bone. At 9 days, in FGM, only cartilage was observed. Quantitative rating of the tissue response, using a scoring system, demonstrated that the observed differences were statistically significant (Wilcoxon rank sum test, p < 0.05). We conclude that IBM, CaP-coated Ti mesh, FGM, and PPHAP provided with rhBMP-2 can indeed induce ectopic bone formation with a cartilaginous phase in a rat model at short implantation periods. Considering the different chemical composition and three-dimensional spatial configuration of the carrier materials used, these findings even suggest that endochondral ossification is present in rhBMP-2-induced osteogenesis, even though the amount of cartilage may differ.

Item does not contain fulltext

Item does not contain fulltext, The osteoinductive properties of porous titanium fiber mesh, with or without a calcium phosphate coating and loaded with recombinant human bone morphogenic protein-2 (rhBMP-2) or rhBMP-2 and native bovine BMP (S-300) were investigated in a rat ectopic assay model. A total of 112 calcium phosphate-coated and 112 noncoated porous titanium implants, either loaded with rhBMP-2 and S-300 or loaded with rhBMP-2 alone, were subcutaneously placed in 56 Wistar-King rats. The rats were killed 5, 10, 20, and 40 days postoperatively, and the implants were retrieved.Histologic analysis demonstrated that all growth factor and carrier combinations induced ectopic cartilage and bone formation at 5 and 10 days, respectively. At 20 days, bone formation increased and was characterized by trabecular bone and bone marrow-like tissue. At 40 days, more lamellar bone and hemopoietic bone marrow-like tissue were present. At both times, more bone had been formed in calcium phosphate-coated implants than in noncoated samples. Further, in rhBMP-2 and S-300-loaded specimens, bone formation was higher than in rhBMP-2 only-loaded specimens. In rhBMP-2 only-loaded specimens, bone formation was mainly localized inside the mesh material, whereas in specimens loaded with both rhBMP-2 and S-300, the bone was localized inside and surrounding the titanium mesh. The histological findings were confirmed by calcium content and alkaline phosphatase activity measurements. In addition, all specimens showed osteocalcin expression as early as 5 days postoperatively.Our results show that the combination of titanium mesh with BMPs can induce ectopic bone formation and that this bone formation seems to be similar to "enchondral" ossification. In addition, a thin calcium phosphate coating can have a beneficial effect on the bone-inducing properties of a scaffold material. Finally, rhBMP-2 and native BMP act synergistically in ectopic bone induction.