Search

On 11 March 2011, the day of the unforgettable disaster of the 9 magnitude Tohoku earthquake and quickly followed by the devastating Tsunami, a damageable amount of radionuclides had dispersed from the Fukushima Daiichi’s damaged nuclear reactors. Decontamination of the dispersed radionuclides from seawater and soil, due to the huge amounts of coexisting ions with competitive functionalities, has been the topmost difficulty. Ferric hexacyanoferrate, also known as Prussian blue (PB), has been the most powerful material for selectively trapping the radioactive cesium ions; its high tendency to form stable colloids in water, however, has made PB to be impossible for the open-field radioactive cesium decontamination applications. A nano/nano combinatorial approach, as is described in this study, has provided an ultimate solution to this intrinsic colloid formation difficulty of PB. Cellulose nanofibers (CNF) were used to immobilize PB via the creation of CNF-backboned PB. The CNF-backboned PB (CNF/PB) was found to be highly tolerant to water and moreover, it gave a 139 mg/g capability and a million (106) order of magnitude distribution coefficient (Kd) for absorbing of the radioactive cesium ion. Field studies on soil and seawater decontaminations in Fukushima gave satisfactory results, demonstrating high capabilities of CNF/PB for practical applications., National Science Foundation (U.S.) (DMR-1507806)

Nitrogen-doped porous activated carbon monoliths (NDP-ACMs) have long been the most desirable materials for supercapacitors. Unique to the conventional template based Lewis acid/base activation methods, herein, we report on a simple yet practicable novel approach to production of the three-dimensional NDP-ACMs (3D-NDP-ACMs). Polyacrylonitrile (PAN) contained carbon nanotubes (CNTs), being pre-dispersed into a tubular level of dispersions, were used as the starting material and the 3D-NDP-ACMs were obtained via a template-free process. First, a continuous mesoporous PAN/CNT based 3D monolith was established by using a template-free temperature-induced phase separation (TTPS). Second, a nitrogen-doped 3D-ACM with a surface area of 613.8 m²/g and a pore volume 0.366 cm³/g was obtained. A typical supercapacitor with our 3D-NDP-ACMs as the functioning electrodes gave a specific capacitance stabilized at 216 F/g even after 3000 cycles, demonstrating the advantageous performance of the PAN/CNT based 3D-NDP-ACMs., National Science Foundation (U.S.) (DMR-1507806)

An efficient three-dimensional (3D) hybrid material of nitrogen-doped graphene sheets (N-RGO) supporting molybdenum disulfide (MoS2) nanoparticles with high-performance electrocatalytic activity for hydrogen evolution reaction (HER) is fabricated by using a facile hydrothermal route. Comprehensive microscopic and spectroscopic characterizations confirm the resulting hybrid material possesses a 3D crumpled few-layered graphene network structure decorated with MoS2 nanoparticles. Electrochemical characterization analysis reveals that the resulting hybrid material exhibits efficient electrocatalytic activity toward HER under acidic conditions with a low onset potential of 112 mV and a small Tafel slope of 44 mV per decade. The enhanced mechanism of electrocatalytic activity has been investigated in detail by controlling the elemental composition, electrical conductance and surface morphology of the 3D hybrid as well as Density Functional Theory (DFT) calculations. This demonstrates that the abundance of exposed active sulfur edge sites in the MoS2 and nitrogen active functional moieties in N-RGO are synergistically responsible for the catalytic activity, whilst the distinguished and coherent interface in MoS 2 /N-RGO facilitates the electron transfer during electrocatalysis. Our study gives insights into the physical/chemical mechanism of enhanced HER performance in MoS2/N-RGO hybrids and illustrates how to design and construct a 3D hybrid to maximize the catalytic efficiency.

Izumi Kanayama,1 Hirofumi Miyaji,1 Hiroko Takita,2 Erika Nishida,1 Maiko Tsuji,3 Bunshi Fugetsu,4,5 Ling Sun,4,5 Kana Inoue,1 Asako Ibara,1 Tsukasa Akasaka,6 Tsutomu Sugaya,1 Masamitsu Kawanami1 1Department of Periodontology and Endodontology, 2Support Section for Education and Research, Graduate School of Dental Medicine, Hokkaido University, Sapporo, Japan; 3Mitsubishi Gas Chemical Company, Inc., Tokyo, Japan; 4Division of Frontier Research, Research Department, Creative Research Institution Sousei, 5Graduate School of Environmental Science, 6Department of Biomedical, Dental Materials and Engineering, Graduate School of Dental Medicine, Hokkaido University, Sapporo, Japan Background: Graphene oxide (GO) is a single layer carbon sheet with a thickness of less than 1 nm. GO has good dispersibility due to surface modifications with numerous functional groups. Reduced graphene oxide (RGO) is produced via the reduction of GO, and has lower dispersibility. We examined the bioactivity of GO and RGO films, and collagen scaffolds coated with GO and RGO. Methods: GO and RGO films were fabricated on a culture dish. Some GO films were chemically reduced using either ascorbic acid or sodium hydrosulfite solution, resulting in preparation of RGO films. The biological properties of each film were evaluated by scanning electron microscopy (SEM), atomic force microscopy, calcium adsorption tests, and MC3T3-E1 cell seeding. Subsequently, GO- and RGO-coated collagen scaffolds were prepared and characterized by SEM and compression tests. Each scaffold was implanted into subcutaneous tissue on the backs of rats. Measurements of DNA content and cell ingrowth areas of implanted scaffolds were performed 10 days post-surgery.Results: The results show that GO and RGO possess different biological properties. Calcium adsorption and alkaline phosphatase activity were strongly enhanced by RGO, suggesting that RGO is effective for osteogenic differentiation. SEM showed that RGO-modified collage

To investigate the influence of immobilized graphene oxide (GO) on host structures, it was incorporated into calcium alginate and macroporous alginic beads, and acridine orange (AO) was used as a typical dye pollutant to eliminate. Characterizations demonstrated GO was well encapsulated and had promoted both beads more porous yet to a varying extent. Kinetics studies exhibited the addition of GO resulted in adsorptions with shorter equilibrium time and faster initial adsorption rate, and the adsorbents with higher equilibrium capacities. Isotherm studies indicated the hybrid absorbents following Langmuir-type adsorptive behavior had higher maximum adsorption capacities than those without GO. In addition, GO would contribute dominantly to the removal of AO under highly acidic condition whereas alginate/alginic part became failure.

Graphene oxide (GO) is a single layer carbon sheet with a thickness of less than 1 nm. GO has good dispersibility due to surface modifications with numerous functional groups. Reduced graphene oxide (RGO) is produced via the reduction of GO, and has lower dispersibility. We examined the bioactivity of GO and RGO films, and collagen scaffolds coated with GO and RGO. METHODS:GO and RGO films were fabricated on a culture dish. Some GO films were chemically reduced using either ascorbic acid or sodium hydrosulfite solution, resulting in preparation of RGO films. The biological properties of each film were evaluated by scanning electron microscopy (SEM), atomic force microscopy, calcium adsorption tests, and MC3T3-E1 cell seeding. Subsequently, GO- and RGO-coated collagen scaffolds were prepared and characterized by SEM and compression tests. Each scaffold was implanted into subcutaneous tissue on the backs of rats. Measurements of DNA content and cell ingrowth areas of implanted scaffolds were performed 10 days post-surgery. RESULTS: The results show that GO and RGO possess different biological properties. Calcium adsorption and alkaline phosphatase activity were strongly enhanced by RGO, suggesting that RGO is effective for osteogenic differentiation. SEM showed that RGO-modified collagen scaffolds have rough, irregular surfaces. The compressive strengths of GO- and RGO-coated scaffolds were approximately 1.7-fold and 2.7-fold greater, respectively, when compared with the non-coated scaffold. Tissue ingrowth rate was 39% in RGO-coated scaffolds, as compared to 20% in the GO-coated scaffold and 16% in the non-coated scaffold. CONCLUSION: In summary, these results suggest that GO and RGO coatings provide different biological properties to collagen scaffolds, and that RGO-coated scaffolds are more bioactive than GO-coated scaffolds.

Graphene oxide (GO) is a single layer carbon sheet with a thickness of less than 1 nm. GO has good dispersibility due to surface modifications with numerous functional groups. Reduced graphene oxide (RGO) is produced via the reduction of GO, and has lower dispersibility. We examined the bioactivity of GO and RGO films, and collagen scaffolds coated with GO and RGO. METHODS:GO and RGO films were fabricated on a culture dish. Some GO films were chemically reduced using either ascorbic acid or sodium hydrosulfite solution, resulting in preparation of RGO films. The biological properties of each film were evaluated by scanning electron microscopy (SEM), atomic force microscopy, calcium adsorption tests, and MC3T3-E1 cell seeding. Subsequently, GO- and RGO-coated collagen scaffolds were prepared and characterized by SEM and compression tests. Each scaffold was implanted into subcutaneous tissue on the backs of rats. Measurements of DNA content and cell ingrowth areas of implanted scaffolds were performed 10 days post-surgery. RESULTS: The results show that GO and RGO possess different biological properties. Calcium adsorption and alkaline phosphatase activity were strongly enhanced by RGO, suggesting that RGO is effective for osteogenic differentiation. SEM showed that RGO-modified collagen scaffolds have rough, irregular surfaces. The compressive strengths of GO- and RGO-coated scaffolds were approximately 1.7-fold and 2.7-fold greater, respectively, when compared with the non-coated scaffold. Tissue ingrowth rate was 39% in RGO-coated scaffolds, as compared to 20% in the GO-coated scaffold and 16% in the non-coated scaffold. CONCLUSION: In summary, these results suggest that GO and RGO coatings provide different biological properties to collagen scaffolds, and that RGO-coated scaffolds are more bioactive than GO-coated scaffolds.

Novel cubic Ag@AgX@Graphene (X = Cl, Br) nanocomposites are facilely manipulated by means of a graphene oxide (GO) sheet-assisted assembly protocol, where GO sheets act as an amphiphilic template for hetero-growth of AgX nanoparticles. A morphology transformation of AgX nanoparticles from sphere to cube-like shape was accomplished by involving GO. With further UV irradiation, the reduction of GO to graphene and the generation of Ag nanocrystals on AgX occur simultaneously. We have demonstrated that the thus-produced Ag@AgX@Graphene nanocomposites could be employed as stable plasmonic photocatalysts to decompose acridine orange as a typical dye pollutant under sunlight irradiation. Compared with the bare quasi-spherical Ag@AgX, such graphene-interfaced cubic Ag@AgX nanocomposites display distinctly higher adsorptive capacity, smaller crystal size and reinforced electron-hole pair separation owing to the interfacial contact between Ag@AgX and graphene sheet components, resulting in an enhanced photocatalytic decomposition performance. This investigation provides new possibilities for the development of morphology-controlled plasmonic photocatalysts and facilitates their practical application in environmental issues., First published online 15 Aug 2013

Mass production of solution-based graphene derived from the precursor graphene oxide is a challenging step toward achieving industrialization of graphene. Inspired by a classical reducing method performed in the textile and paper making industries, we report here a rapid, cost-effective, and safer approach to the facile production of graphene that employs thiourea dioxide (TDO) as the green reductant. Graphene oxide was converted into high quality graphene within 30 minutes with TDO as the reductant under moderate reaction conditions. The C/O ratio of the TDO reduced graphene was ～5.9 with the yield of graphene from graphene oxide > 99%. This is better than the reduction efficiency under the identical experimental conditions by using L-ascorbic acid as the reductant which required a reaction time of about 48 hours. This simple and effective procedure should offer an alternative route to the mass production of solution-based graphene for practical applications.