This study presents an unexplored method to produce formaldehyde-free MDF. Steam exploded Arundo donax L. (STEX-AD) and untreated wood fibers (WF) were mixed at different mixing rates (0/100, 50/50, and 100/0, respectively) and two series of boards were manufactured, with 4 wt% of pMDI, based on dry fibers, and self-bonded. The mechanical and physical performance of the boards was analyzed as a function of the adhesive content and the density. The mechanical performance and dimensional stability were determined by following European standards. The material formulation and the density of the boards had a significant effect on both mechanical and physical properties. The boards made solely of STEX-AD were comparable to those made with pMDI, while the panels made of WF without adhesive were those that performed the worst. The STEX-AD showed the ability to reduce the TS for both pMDI-bonded and self-bonded boards, although leading to a high WA and a higher short-term absorption for the latter. The results presented show the feasibility of using STEX-AD in the manufacturing of self-bonded MDF and the improvement of dimensional stability. Nonetheless, further studies are needed especially to address the enhancement of the internal bond (IB). [ABSTRACT FROM AUTHOR]

Physical, mechanical, and formaldehyde emission properties were studied for medium density fiberboard (MDF) produced with oak (75%) and pine (25%) fibers that had been mechanically refined in the presence of calcite particles. The calcite slurry was prepared at two levels of solids, 1.5% and 3% (10 and 20 kg·m-3). Chips were cooked for 4 min at 185 °C, under 8 bar vapor pressure in an Andritz defibrillator. 1.8% liquid paraffin, 0.72% ammonium sulphate solution, and 11% urea-formaldehyde were added by percentage based on oven-dried wood fibers in the blowline at the exit of the defibrator. The fibers were dried to 11% moisture content. MDF boards (2100 mm × 2800 mm × 18 mm) were created using a continuous hotpress process. The addition of calcite in the course of MDF production resulted in improved physical properties, such as thickness swelling (ThS 24 hours) and water absorption (WA 24 hours). MDF boards prepared with calcite exhibited higher internal bond (IB), modulus of rupture (MOR), and modulus of elasticity (MOE). Resistance to axial withdrawal of screw also was increased by addition of 3% calcite. In addition, the lowest levels of formaldehyde emission were observed for MDF prepared with calcite at the 3% level. [ABSTRACT FROM AUTHOR]