Abstract: The effect of neutron-irradiation damage has been mainly simulated using high-energy ion bombardment. A recent MIT report (PSFC/RR-10-4, An assessment of the current data affecting tritium retention and its use to project towards T retention in ITER, Lipschultz et al., 2010) summarizes the observations from high-energy ion bombardment studies and illustrates the saturation trend in deuterium concentration due to damage from ion irradiation in tungsten and molybdenum above 1 displacement per atom (dpa). While this prior database of results is quite valuable for understanding the behavior of hydrogen isotopes in plasma facing components (PFCs), it does not encompass the full range of effects that must be considered in a practical fusion environment due to short penetration depth, damage gradient, high damage rate, and high primary knock-on atom (PKA) energy spectrum of the ion bombardment. In addition, neutrons change the elemental composition via transmutations, and create a high radiation environment inside PFCs, which influences the behavior of hydrogen isotope in PFCs, suggesting the utilization of fission reactors is necessary for neutron-irradiation. Under the framework of the US–Japan TITAN program, tungsten samples (99.99at.% purity from A.L.M.T. Co.) were irradiated by fission neutrons in the High Flux Isotope Reactor (HFIR), Oak Ridge National Laboratory (ORNL), at 50 and 300°C to 0.025, 0.3, and 2.4dpa, and the investigation of deuterium retention in neutron-irradiated tungsten was performed in the Tritium Plasma Experiment (TPE), the unique high-flux linear plasma facility that can handle tritium, beryllium and activated materials. This paper reports the recent results from the comparison of ion-damaged tungsten via various ion species (2.8MeV Fe2+, 20MeV W2+, and 700keV H−) with that from neutron-irradiated tungsten to identify the similarities and differences among them. [Copyright &y& Elsevier]

Abstract: With the Japan–US joint research project Tritium, Irradiations, and Thermofluids for America and Nippon (TITAN), an initial set of tungsten samples (99.99% purity, A.L.M.T. Co.) were irradiated by high flux neutrons at 323K to 0.025dpa in High Flux Isotope Reactor (HFIR) at Oak Ridge National Laboratory (ORNL). Subsequently, one of the neutron-irradiated tungsten samples was exposed to a high-flux deuterium plasma (ion flux: 5×1021 m−2 s−1, ion fluence: 4×1025 m−2) in the Tritium Plasma Experiment (TPE) at Idaho National Laboratory (INL). The deuterium retention in the neutron-irradiated tungsten was 40% higher in comparison to the unirradiated tungsten. The observed broad desorption spectrum from neutron-irradiated tungsten and associated TMAP modeling of the deuterium release suggest that trapping occurs in the bulk material at more than three different energy sites. [Copyright &y& Elsevier]