Search

Surface treatment of implants facilitates osseointegration, with nanostructured surfaces exhibiting accelerated peri-implant bone regeneration. This study compared bone-to-implant contact (BIC) in implants with hydroxyapatite (HA), sand-blasted and acid-etched (SLA), and SLA with calcium (Ca)-coated (XPEED®) surfaces. Seventy-five disk-shaped grade 4 Ti specimens divided into three groups were prepared, with 16 implants per group tested in New Zealand white rabbits. Surface characterization was performed using X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), digital microscopy, and a contact angle analyzer. Cell viability, proliferation, and adhesion were assessed using MC3T3-E1 cells. Apatite formation was evaluated using modified simulated body fluid (m-SBF) incubation. After 4 weeks of healing, the outcomes reviewed were BIC, bone area (BA), removal torque tests, and histomorphometric evaluation. A microstructure analysis revealed irregular pores across all groups, with the XPEED group exhibiting a nanostructured Ca-coated surface. Surface characterization showed a crystalline CaTiO3 layer on XPEED surfaces, with evenly distributed Ca penetrating the implants. All surfaces provided excellent environments for cell growth. The XPEED and SLA groups showed significantly higher cell density and viability with superior osseointegration than HA (p < 0.05); XPEED exhibited the highest absorbance values. Thus, XPEED surface treatment improved implant performance, biocompatibility, stability, and osseointegration. [ABSTRACT FROM AUTHOR]

Background: Aloe vera was used to enhance defense mechanisms, and it has a variety of components that affected on periodontal healing and other oral condition .It was used also around dental implants to control inflammation from bacteria contamination. Vascular endothelial growth factor(VEGF) is of particular interest because of its ability to induce neovascularization (angiogenesis), VEGF also acts to recruit and activate osteoclasts as well as stimulate osteoblast chemotaxis, differentiation, and matrix mineralization. Aim of study: The objective of this research was to illustrate the biological actions of topical application of aloe vera and growth factor VEGF on implant tissue contact surface which is involved in osseointegration . Materials and Method: Commercially pure Titanium(cpTi) implants with aloe vera /and VEGF,were placed in the tibia of (24) New Zealand white rabbits, Mechanical test (torque removal test) was performed as an indicator for the presence of osseointegration and bone implant contact (BIC)measurement as a test for the property of bone-implant interface. Histological investigation was performed on all the implants of both control and experimental groups at (1,2, and 6weeks) healing intervals. Results: Findings illustrated that removal torque mean and BIC values in experimental implant showed high value in comparison to control. Histological results show an early bone deposition and early maturation in combination group . Conclusions: Bone formation &maturation was accelerated by adding biological materials and using a combination of Aloe Vera and VEGF is a powerful tool for enhancement of osseointegration. [ABSTRACT FROM AUTHOR]

Titanium surface is an important factor in achieving osseointegration during the early wound healing of dental implants in alveolar bone. The purpose of this study was to evaluate sandblasted-etched surface implants to investigate the osseointegration. In the present study, we used two different types of sandblasted-etched surface implants, an SLA™ surface and a Nanoblast Plus™ surface. Roughness and chemical composition were evaluated by a white light interferometer microscope and X-ray photoelectron spectroscopy, respectively. The SLA™ surface exhibited the higher values (Ra 3.05 μm) of rugosity compared to the Nanoblast Plus™ surface (Ra 1.78 μm). Both types of implants were inserted in the femoral condyles of ten New Zealand white rabbits. After 12 weeks, histological and histomorphometric analysis was performed. All the implants were osseointegrated and no signs of infection were observed. Histomorphometric analysis revealed that the bone–implant contact % (BIC) ratio was similar around the SLA™ implants (63.74 ± 13.61) than around the Nanoblast Plus™ implants (62.83 ± 9.91). Both implant surfaces demonstrated a favorable bone response, confirming the relevance of the sandblasted-etched surface on implant osseointegration. [ABSTRACT FROM AUTHOR]

Silane-coating strategy has been used to bind biological compounds to the titanium surface, thereby making implant devices biologically active. However, it has not been determined if the presence of the silane coating itself is biocompatible to osseointegration. The aim of the present study was to evaluate if silane-coating affects bone formation on titanium using a rabbit model. For this, titanium screw implants (3.75 by 6 mm) were hydroxylated in a solution of H2SO4/30% H2O2 for 4 h before silane-coating with 3-aminopropyltriethoxysilane (APTES). A parallel set of titanium screws underwent only the hydroxylation process to present similar acid-etched topography as a control. The presence of the silane on the surface was checked by x-ray photoelectron spectroscopy (XPS), with scanning electron microscopy (SEM) and atomic force microscopy (AFM). A total of 40 titanium screws were implanted in the tibia of ten New Zealand rabbits in order to evaluate bone-to-implant contact (BIC) after 3 weeks and 6 weeks of healing. Silane-coated surface presented higher nitrogen content in the XPS analysis, while micro- and nano-topography of the surface remained unaffected. No difference between the groups was observed after 3 and 6 weeks of healing (p > 0.05, independent t-test), although an increase in BIC occurred over time. These results indicate that silanization of a titanium surface with APTES did not impair the bone formation, indicating that this can be a reliable tool to anchor osteogenic molecules on the surface of implant devices. [ABSTRACT FROM AUTHOR]

Background: Various surface treatments have been tested for titanium implants aiming at increasing their surface biocompatibility and their biological characteristics, but also the efficiency of the implant surface will have to be improved to drastically decrease peri-implantite and mucosite. In fact, the peri-implantitis and peri-implant mucositis have a high incidence in clinical practice. The nanofabrication techniques that offer the possibility to achieve the implant surface that reduces bacterial colonization could influence the osteointegration. The aim of this research was to evaluate the bone response to titanium implants coated with a bifunctional molecule with antimicrobic activity consisting of a combination of silver ions covalently bound to titanium dioxide nanoparticles. Methods: A total of 36 implants were inserted into 18 older New Zealand white male rabbits. They had two different surfaces. The implants Control group was characterized by an acid-etched and sandblasted surface treatment, and the Test implants had an acid-etched and sandblasted surface coated with a silver ion covalently bound to titanium dioxide nanoparticles in the solution. Results: No statistically significant difference of the bone density was evidenced between Control and Test implants at two weeks (p-value = 0.623), four weeks (p-value = 0.339), and eight weeks (p-value = 0.461). Moreover, no statistically significant difference of the bone-implant contact percentage was evidenced between Control and Test implants at two weeks (p-value = 0.938), four weeks (p-value = 0.307), and eight weeks (p-value = 0.294). The effectiveness of the present investigation demonstrated no adverse effects on osseointegration, and no statistically significant differences were observed in the bone density and percentage of bone-implant contact between Test and Control implants at all the experimental time points (two, four, and eight weeks). Conclusions: Titanium implants coated with the silver-anatase solution bind very well to the bone and did not have an adverse effect on the bone tissue in a rabbit model. These facts suggest possible clinical applications for the silver composition. [ABSTRACT FROM AUTHOR]