Search

Introduction: Polyetheretherketone, also known as PEEK, is a semicrystalline thermoplastic material with many advantages. Since its grey material, it has to veneering with composite resin to enhance its aesthetic appeal. Bonding PEEK and composite veneers poses challenges due to its inert surface. Aim: To assess and compare the Shear Bond Strength (SBS) between various polyetheretherketone materials and veneering composites following various surface treatments. Materials and Methods: The in-vitro study was conducted at KSR Dental College and Hospital in Tiruchengode, Tamil Nadu, India, over a period of three months from December 2022 to February 2023. A total of 108 PEEK discs were prepared for the study, divided into three groups: unfilled PEEK, 30% carbon reinforced PEEK, and 10% carbon + 10% graphite + 10% Polytetrafluoroethylene (PTFE) reinforced PEEK. The specimens underwent different surface treatments, including no treatment, sandblasting with 110 um alumina particles, and acid etching with 98% sulphuric acid. Additionally, 108 composite discs were prepared and bonded to the PEEK specimens using adhesive and resin cement. The bonded specimens were immersed in distilled water for 24 hours, and the Shear Bond Strength (SBS) was determined using a universal testing machine. Statistical analysis was performed using one-way ANOVA, and mean values were compared using posthoc tests. Results: The results indicated significant variation in SBS among the three groups without treatment (p=0.011) and after sandblasting with 110 um alumina (p=<0.001). The 30% carbon reinforced PEEK exhibited the highest SBS regardless of the surface treatments. Conclusion: Among the tested materials, 30% carbon reinforced PEEK demonstrated the highest SBS, regardless of the surface treatments. Acid etching yielded the highest SBS among the various surface treatments, irrespective of the type of PEEK material used. [ABSTRACT FROM AUTHOR]

With rapid industrialization, there is an ever-increasing demand for iron oxides, calcium oxides, aluminum oxides, silica, and zeolites as raw materials for various industries, but reserves of such metal oxides are continuously diminishing. Therefore, there is an urgent need to explore new alternatives for such value-added minerals. One such material is incense stick ash (ISA), which is among the most unexplored byproducts from residential and holy places. Currently, ISA is of no use and it is disposed of in millions of tons (MTs) in rivers and other water bodies in India due to its sacred value. The major chemical composition of ISA is calcium, silica, alumina, ferrous minerals, magnesium, and traces of Na, K, P, Ti, etc. Major fractions of ISA, i.e., 50–60%, are made up of calcium and magnesium oxides; 20–30% of ISA is made up of silica, alumina, and ferrous minerals, as revealed by X-ray fluorescence spectroscopy (XRF). In the present research work, methods of recovery of value-added micro and nano minerals from ISA are suggested, using cost-effective techniques and an eco-friendly approach. Firstly, magnetic fractions were recovered by a magnetic separation method; then, alumina, silica, and calcium oxides were synthesized from non-magnetic fractions. The confirmation of the synthesized and extracted nanomaterials was done by Fourier transform infrared spectroscopy (FTIR), particle size analyzer (PSA), X-ray diffraction (XRD), field emission scanning electron microscopy with electron diffraction spectroscopy (FESEM-EDS), and transmission electron microscopy (TEM). The purity of synthesized particles varied from 40–80%. In the future, ISA will prove to be an alternative resource material for Fe, Ca, Si, C, Al, and zeolites, which will minimize solid waste pollution and water pollution arising due to the disposal of ISA into water bodies. [ABSTRACT FROM AUTHOR]