A newly synthesized, single-step silicone acrylate formulation cured by conventional radiation produced a reflection spectrum that showed an unusual interference pattern for a single-step coating. The acrylate was prepared by transesterification of silicate oligomer with ω-functionalized acrylic alcohol. The reflectance spectrum was analyzed by means of the Fourier transformation, followed by a separation of variables and constrained conditions. The separation of variables was based on the refractive index as a function of the layer depth, which revealed the coating was non-uniform in refractive index. An interface within the coating was independently observed by microscopy, showing that the coating separated into two layers, supporting the numerical analysis. Although the coating was manufactured by a single-step coating process, the two-layer structure that was formed is normally constructed with multiple coating processes, such as applications of a primer and a top coat. Experiments varying the formulation components show that the new silicone acrylate and an aliphatic di-functional acrylic ester were essential components for the formation of the two-layer structure. Outdoor weathering results are presented after 1 year of testing in Florida and Arizona, which showed better performance than conventional coating systems. [ABSTRACT FROM AUTHOR]

Many natural exposure sites have been developed to ensure the reliability of materials intended for outdoor use. However, the effects of local climate on aging have not been completely understood. This study aimed to elucidate the regional characteristics of natural aging. Non-stabilized and stabilized polycarbonates were monitored in terms of their appearance (yellowing and loss of gloss) during natural weathering at five exposure sites (Tokyo, Kagoshima, Okinawa, Florida, and Arizona) in conjunction with climate fluctuation for up to 24 months. Three approaches were employed to characterize the natural aging behaviors: (i) modeling the rate function of degradation, (ii) evaluating the contribution ratio of individual degradational factors, and (iii) estimating the "synchronicity" by cross-correlation analysis with the climate dataset. The aging rates were the highest in Arizona and lowest in Kagoshima among the five exposure sites. First, prediction curves were constructed from the degradation rate function (variables: UV irradiation, temperature, and humidity), and these curves were found to agree well with the measured aging behaviors. Second, the exposure data in Arizona demonstrated strong temperature dependence, while those in Okinawa and Florida had stronger dependence on UV irradiation compared to other sites. Lastly, the synchronicity between UV irradiation and temperature was the highest in Arizona and lowest in Kagoshima, which can explain the significantly faster deterioration in Arizona and the slow deterioration in Kagoshima. [ABSTRACT FROM AUTHOR]