The demand for high-strength steel welds, as observed in civil and transport engineering, is related to a mass reduction in vehicles. Container-type trucks are examples of this kind of transport means because their boxes are able to be produced using Hardox grade steels. Therefore, this study reflects on the properties of welds in the MAG welding of Hardox 450, obtained through an innovative micro-jet cooling process with helium. This joining technology aims to reduce the formation of defects and to obtain a joint with very good assumed mechanical properties. Structural components of grade steel require welds with acceptable mechanical parameters with respect to operational loading conditions. That is, this study focuses on selecting welding parameters for the Hardox 450 steel and determining the weld quality with respect to microstructural observations and mechanical tests, such as the Charpy, tensile and fatigue tests. Weld fracturing under increasing monotonic force was examined and was strongly related to both stress components, i.e., axial and shear. The joint response under fatigue was expressed through differences in the fracture zones, i.e., at a stress value lower than the proportional limit, and weld degradation occurred in the shear and axial stress components. The data indicate that the hourglass specimen, with the weld in the centre zone of the measurement section, can be directly used to determine a weld response under cyclic loading. The impact test results showed attractive behaviour in the tested joint, as represented by 47 J at −20 °C. The recommended MAG welding parameters for Hardox 450 steel are low-oxygen when using an Ar + 18% CO2 shielding mixture. The collected results can be directly used as a guide to weld thin-walled structures (6 mm) made of Hardox grade steel, while the data from mechanical tests can support the modelling, designing and manufacturing of components made from this kind of steel grade. [ABSTRACT FROM AUTHOR]

The demand for high-strength steel welds, as observed in civil and transport engineering, is related to a mass reduction in vehicles. Container-type trucks are examples of this kind of transport means because their boxes are able to be produced using Hardox grade steels. Therefore, this study reflects on the properties of welds in the MAG welding of Hardox 450, obtained through an innovative micro-jet cooling process with helium. This joining technology aims to reduce the formation of defects and to obtain a joint with very good assumed mechanical properties. Structural components of grade steel require welds with acceptable mechanical parameters with respect to operational loading conditions. That is, this study focuses on selecting welding parameters for the Hardox 450 steel and determining the weld quality with respect to microstructural observations and mechanical tests, such as the Charpy, tensile and fatigue tests. Weld fracturing under increasing monotonic force was examined and was strongly related to both stress components, i.e., axial and shear. The joint response under fatigue was expressed through differences in the fracture zones, i.e., at a stress value lower than the proportional limit, and weld degradation occurred in the shear and axial stress components. The data indicate that the hourglass specimen, with the weld in the centre zone of the measurement section, can be directly used to determine a weld response under cyclic loading. The impact test results showed attractive behaviour in the tested joint, as represented by 47 J at −20 °C. The recommended MAG welding parameters for Hardox 450 steel are low-oxygen when using an Ar + 18% CO2 shielding mixture. The collected results can be directly used as a guide to weld thin-walled structures (6 mm) made of Hardox grade steel, while the data from mechanical tests can support the modelling, designing and manufacturing of components made from this kind of steel grade.

The paper is focused on testing the weld of the S960MC steel produced at the micro-jet cooling under static and fatigue loading at critical parameters. This kind of material was in the form of a sheet with a thickness equal to 2 mm. The joint was obtained using three different types of welding wires: EDFK 1000, Union NiMoCr and Union X96 at the same parameters of the process. The joints were examined using non-destructive and destructive tests. The results from non-destructive experiments enable us to assess the quality of the welds directly before the joining process. In contrast, the destructive one allows following welds behavior under different loading conditions with their critical parameters. The bending experiments confirmed the good plastic properties of the weld, expressed by no cracks in the region tested in many variants of the joint manufactured. The results from static tests indicated a significant reduction of mechanical parameters of the weld in comparison to the base metal, expressed by 50% differences. Fatigue data have enabled us to follow the welding behavior at the increasing amplitude of axial stress up to fracture at constant amplitude value covering the following values of stress 650 MPa–100 MPa. Variations of total energy are presented at different values of several cycles up to fracture. Fracture regions are collected for analysis of the joint region features under cyclic loading. They have indicated differences in weld cracking depended on the stress level. Finally, the Wöhler S-N curve of the weld was determined, indicating the value of the fatigue limit of the weld tested, i.e., 100 MPa. The weld at the Union NiMoCr welding wire was indicated as the joint having the highest resistance on static and fatigue loadings.

The material selected for this investigation was low alloy weld metal deposit after TIG welding with various amount of oxygen in weld metal deposit (WMD). After TIG process it is difficult to get proper amount of oxygen in WMD on the level much lower than 350 ppm. The highest impact toughness of low alloy WMD corresponds with the amount of oxygen in WMD above 350 ppm. In the paper focuses on low alloy steel after innovate welding method with micro-jet cooling that could be treated as a chance on rising amount of oxygen in weld. Weld metal deposit (WMD) was carried out for TIG welding with micro-jet cooling with various amount of oxygen in WMD. In that paper various gas mixtures (gas mixtures Ar-O2 and Ar-CO2) were tested for micro-jet cooling after TIG welding. An important role in the interpretation of the results can give methods of artificial intelligence.

The paper focuses on low alloy steel after innovate welding method with micro-jet cooling. Weld metal deposit (WMD) was carried out for welding and for MIG and MAG welding with micro-jet cooling. This method is very promising mainly due to the high amount of AF (acicular ferrite) and low amount of MAC (self-tempered martensite, retained austenite, carbide) phases in WMD. That structure corresponds with very good mechanical properties, ie. high impact toughness of welds at low temperature. Micro-jet cooling after welding can find serious application in automotive industry very soon. Until that moment only argon, helium and nitrogen were tested as micro-jet gases. In that paper first time various gas mixtures (gas mixtures Ar-CO2) were tested for micro-jet cooling after welding.

This paper presents results of experimental research concerning the impact of an innovative method of micro-jet cooling on the padding weld performed with MIG welding. Micro-jet cooling is a novel method patented in 2011. It enables to steer the parameters of weld cooling in a precise manner. In addition, various elements which may e.g. enhance hardness or alter tribological properties can be entered into its top surface, depending on the applied cooling gas. The material under study was steel 20MnCr5, which was subject to the welding process with micro-jet cooling and without cooling. Nitrogen was used as a cooling gas. The main parameter of weld assessment was wear intensity. The tests were conducted in a tribological pin-on-disc type position. The following results exhibit growth at approximately 5% in wear resistance of padding welds with micro-jet cooling.

The material selected for this investigation was low alloy steel weld metal deposit (WMD) after MIG welding with micro-jet cooling. The present investigation was aimed as the following tasks: obtained WMD with various amount of acicular ferrite and further analyze impact toughness of WMD in terms of acicular ferrite amount in it. Weld metal deposit (WMD) was first time carried out for MIG welding with micro-jet cooling of compressed air and gas mixture of argon and air. Until that moment only argon, helium and nitrogen were tested as micro-jet gases for MIG/MAG processes. An important role in the interpretation of the results can give methods of artificial intelligence.

The material selected for this investigation was low alloy steel weld metal deposit (WMD) after MAG welding with micro-jet cooling. The present investigation was aimed as the following tasks: analyze impact toughness of WMD in terms of micro-jet cooling parameters. Weld metal deposit (WMD) was first time carried out for MAG welding with micro-jet cooling of compressed air and gas mixture of argon and air. Until that moment only argon, helium and nitrogen and its gas mixture were tested for micro-jet cooling.

A paper presents the possibility of laser welding using micro-jet cooling. The effect of micro-jet cooling on microstructure and mechanical properties of the weld metal deposit was carried out. New welding process was analyzed for use in the automotive industry. Studies have confirmed the positive effect of cooling micro-jet cooling both for the MIG welding and laser welding.

The paper offers mathematical equations of the influence of micro-jet cooling on structure and impact toughness properties of metal weld deposit. Weld metal deposit (WMD) was carried out for standard MIG welding and for MIG welding with micro-jet cooling. This new method is very promising mainly due to the high amount of AF (acicular ferrite) and low amount of MAC (selftempered martensite, retained austenite, carbide) phases in WMD. That structure corresponds with very good mechanical properties ie. good impact toughness of welds at low temperature. Micro-jet cooling after welding can find serious application in automotive industry very soon. Until that moment only argon, helium, nitrogen and gas mixtures of argon were tested for micro-jet cooling after welding. The best results of mechanical properties of WMD in presented welding method correspond with micro-jet argon cooling. [ABSTRACT FROM AUTHOR]

The paper is focused on testing the weld of the S960MC steel produced at the micro-jet cooling under static and fatigue loading at critical parameters. This kind of material was in the form of a sheet with a thickness equal to 2 mm. The joint was obtained using three different types of welding wires: EDFK 1000, Union NiMoCr and Union X96 at the same parameters of the process. The joints were examined using non-destructive and destructive tests. The results from non-destructive experiments enable us to assess the quality of the welds directly before the joining process. In contrast, the destructive one allows following welds behavior under different loading conditions with their critical parameters. The bending experiments confirmed the good plastic properties of the weld, expressed by no cracks in the region tested in many variants of the joint manufactured. The results from static tests indicated a significant reduction of mechanical parameters of the weld in comparison to the base metal, expressed by 50% differences. Fatigue data have enabled us to follow the welding behavior at the increasing amplitude of axial stress up to fracture at constant amplitude value covering the following values of stress 650 MPa–100 MPa. Variations of total energy are presented at different values of several cycles up to fracture. Fracture regions are collected for analysis of the joint region features under cyclic loading. They have indicated differences in weld cracking depended on the stress level. Finally, the Wöhler S-N curve of the weld was determined, indicating the value of the fatigue limit of the weld tested, i.e., 100 MPa. The weld at the Union NiMoCr welding wire was indicated as the joint having the highest resistance on static and fatigue loadings. [ABSTRACT FROM AUTHOR]