Search

As part of the validation effort to evaluate the consistency of a new cold in-place recycling using foamed asphalt (CIR–foam) mix design process for the Iowa Department of Transportation, the dynamic modulus and repeated load tests were conducted to evaluate the performance characteristics of CIR–foam mixtures over a wide range of loading and temperature conditions. The main objective of this research is to study the impacts of the foamed asphalt contents and reclaimed asphalt pavement (RAP) material characteristics on dynamic modulus and flow number. Dynamic modulus and repeated load tests were conducted on CIR–foam mixtures with RAP materials collected from seven different CIR project sites located throughout Iowa. Dynamic modulus values of the RAP materials varied depending on the sources and foamed asphalt contents. Coarse RAP materials with a small amount of residual asphalt content exhibited a higher modulus value at 4.4°C but exhibited a lower dynamic modulus value at 37.8°C than fine RAP materials with a large amount of residual asphalt content. Flow numbers were varied significantly depending on their RAP sources and foamed asphalt contents. Fine RAP materials with a hard residual asphalt binder exhibited a higher flow number than coarse RAP materials with a soft residual binder. The relative rankings of RAP materials in terms of the flow number did not change when the foamed asphalt was increased from 1.0 to 3.0%, which supports the repeated load test being consistent in evaluating a rutting potential of RAP materials. [ABSTRACT FROM AUTHOR]

The main objective of this study is to validate a new mix design procedure for cold in-place recycling using foamed asphalt (CIR-foam) developed for the Iowa Department of Transportation. First, reclaimed asphalt pavement (RAP) materials were collected from seven different CIR construction sites located across the state of Iowa. To determine the consistency of a new CIR-foam mix design procedure, the mix design was performed seven times using these RAP materials. The test specimens were prepared using gyratory compactor rather than Marshall hammer because it produced more consistent mixtures for various foamed asphalt contents and curing conditions. The indirect tensile strength test was performed on the vacuum-saturated specimens prepared using each of seven RAP material sources for five different foamed asphalt contents (1.0, 1.5, 2.0, 2.5, and 3.0%), given a fixed moisture content of 4.0%. As the foamed asphalt content increased from 1.0 to 3.0% at 0.5% increments, air voids in the CIR-foam mixtures decreased gradually. The indirect tensile strength of CIR-foam specimens cured for two days at 60°C was significantly higher than that of CIR-foam specimens cured for three days at 40°C. Based on the new mix design procedure, the optimum foamed asphalt contents were consistently found at values between 1.5 and 2.5% for all seven different RAP materials. The stiffer residual asphalt required more foamed asphalt, whereas the higher residual asphalt content did not require a smaller amount of foamed asphalt. The raveling test result was very sensitive to the curing time and the foamed asphalt content, such that RAP materials with a large amount of stiff residual asphalt would exhibit more potential for raveling. [ABSTRACT FROM AUTHOR]