Search

Ceramic coatings were successfully fabricated on Mg-7Li alloy in Na2SiO3 electrolyte by microarc oxidation (MAO). The phase composition, formation mechanism and infrared emissivity of the coatings were investigated. Results show that the surface of MAO coating exists some micropores with a diameter of 2-6μm due to electric breakdown. The MAO coating with 13μm thickness is mainly composed of MgO, Li2O2 and Mg2SiO4. The infrared emissivity of the MAO coating is higher than that of bare Mg-7Li alloy, mainly because the coating consisting of ionic crystals has lower lattice vibration symmetry and larger dipole moment.

The aim of this study is to describe the remineralization effect of the nano-HA on artificial caries. The artificial dental caries are made by using sour solution, and constructing an artificial mouth' plaque culture system in vitro respectively. The scanning electron microscope (SEM) and the optical microscope are used to observe the surface of enamel specimens. The effect of remineralization is assessed with the polarized light microscopy (PLM) and the confocal laser scanning microscope (CLSM) by measuring three lesion parameters (area, total and average fluorescence). The SEM analysis shows that the cavities and defects of enamel surface are decreased and many mineral salts are sedimentated, which indicate that the nano-HA could promote remineralization for the demineralized enamel. The inhibitory effect of the spherical nano-HA on dental caries is detected in the artificial mouth test. The CLSM shows that demineralization of enamel is reduced by adding the spherical nano-HA in artificial mouth. The results show that the spherical nano HA have a remineralization effect on the artificial dental caries dramatically, and can prevent and decrease caries.

Chitosan fibers(CSf) andCaSiO3 were incorporated into a poly (L-lactic acid)/hydroxyapatite (PLLA/HA) matrix as reinforcements to prepare scaffold composites with adequate strength and high porosity for bone tissue engineering combined with emulsion freeze drying technique. The structural morphology of the composites was observed by scanning electron microscope (SEM). The porosity was tested by liquid substitute method. The mechanical property was measured. The effects of addition of CSf and CaSiO3 on composites were also discussed. Simulated body fluid (SBF) experiments were conducted to assess the bioactivity of the composites. The chemical components of resultants on surfaces after the immersion in SBF were analyzed by fourier transform infrared spectroscopy (FTIR). The results show that the composites with high connectivity have pore sizes of 100~250μm, a porosity of 60%~80%, compressive strength of 3.5~8.0MPa. In the SBF tests, Chitosan fiber reinforced PLLA/HA-CaSiO3 composite degraded stably, meanwhile, the formation of a layer of bone-like apatite on the surfaces of the samples indicated a good bioactivity. Studies suggest the feasibility of using CSf reinforced PLLA /HA-CaSiO3 composite for bone tissue engineering.

The Nano-HA powder was prepared by chemical precipitation. Magnesium powders were used to make porous ultramicron HA ceramic, and the biological properties of which were investigated by hemolysis rate and cytotoxicity tests. The experimental results shows that the hemolysis rate of the nano-HA powder and porous ultramicron HA ceramic were all less than 5% and none of them showed cytotoxicity. The results indicated that nano-HA and porous ultramicron HA ceramic were provided with good biocompatibility.

The objective of this study was to investigate the inhibitory effect of the synthetic nanohydroxyapatite (HA) on dental caries. The nano-HA was synthesized by using the depositing reaction of Ca (H2PO4)2. The artificial dental caries was made by using sour solution and inoculating Streptococcus mutans (S.mutans) to the Sprague-Dawley (SD) rat’s mouth respectively. After mineralization of solution of nano-HA for 10 days, the hardness of enamel was measured. The inhibitory effect of the synthetic nano-HA on dental caries was detected by gargling way to rinse the rat tooth with the solution of nano-HA in the animal test. Transmission electron microscopy (TEM) revealed that the dried HA particles were needle-like with ф5-20nm×60nm and the sintered HA particles were spherical with less than 100nm. The remineralized test indicated that the solution of nano-HA with different shapes enhanced the hardness of artificial caries and improved the remineralization of artificial caries. The animal test showed that the dried nano-HA had the inhibitory effect on dental caries. The good absorptive effect of the nano-HA on both the saliva protein and the glucans leads to the development of interventions that could reduce or modify bacterial colonization of tooth surfaces.

The aim of this study is to describe the remineralization effect of the nano-HA toothpaste on artificial caries. The artificial dental caries is made using sour solution. The demineralized teeth specimen is put into five kinds of toothpaste solution respectively for 5 days and 10 days, which are: solution of containing needle like nano-HA, solution of containing spherical nano-HA, solution of general HA, fluorine sodium solution and physiological saline. The hardness of specimen is measured and the surface morphology is characterized by SEM. The remineralized test indicates that the nano-HA toothpaste can enhance the hardness of artificial caries and improve the remineralization of artificial caries. The SEM analysis shows that the cavities and defects of enamel surface are decreased and many mineral salts are sedimentated, which indicate that the nano-HA could promote remineralization for the demineralized enamel.

The purpose of this study is to examine the inhibitory effects of nano-HA on the caries-inducing properties of a four-organism bacterial consortium in vitro. A series of in vitro anticarious experiments have been carried out by using a continuous culture system. Streptococcus mutans, Streptococcus sanguis, Actinomyces viscosus, Lactobacillus rhamnosus have been chosen as the experimental bacteria. After 48 hours, the dental plaque surface structure is observed with the scan electron microscope and the bacterial colonization was evaluated on dental plaque. The results show that Spherical nano-HA and mixed nano-HA are proved to be effective in anticarious experiments, and especially spherical nano-HA is more striking. It is able to damage the formation of biofilms (dental plaque), postpone or end the process of acid generation of bacteria metabolism. After 7 days, the demineralization of the enamel has been detected by using TEM. The spherical nano-HA might have a remineralization to early caries to prevent and decrease caries.

The hydroxyapatite (HA) particle with different morphologies were prepared by adding a certain additive into Ca(H2PO4)2·H2O and controlling the bathing and sintering temperature, and the pure needle-like HA sol were obtained when the bathing temperature was 70°C. The experimental results show that the degree of crystallization of HA increase and the particles tend to accumulate with increasing of the drying and sintering temperatures. The particles of HA were spheroid, which diameters were of less than 100nm when they were sintered at the temperature of 700°C. The effect of nano-hydroxyapatite on remineralization of early enamel caries were studied too. The hardness of dismineralized enamel was increased when dismineralized enamel was remineralized by nano-hydroxyapatite. The SEM analysis shows that the interspace of enamel surface were decreased and the many mineral salts were sedimentated, which indicated that the nano-hydroxyapatie could promote remineralization for the dismineralized enamel.