Search

We investigate the evolution of microstructure and mechanical properties of sputter-deposited Al/Nb multilayers with miscible fcc/bcc type interface and individual layer thickness, h, of 1–200 nm, subjected to helium ion irradiations: 100 keV He+ ions and a fluence of 6×1016/cm2. Helium bubbles, 1–2 nm in diameter, are observed. When h is greater than 25 nm, hardnesses of irradiated multilayers barely change, whereas radiation hardening is more significant at smaller h. Transmission electron microscopy and scanning transmission electron microscopy studies reveal the formation of a thin layer of Nb3Al intermetallic phase along the Al/Nb interface as a consequence of radiation induced intermixing. The dependence of radiation hardening on h is interpreted by using a composite model considering the formation of the hard Nb3Al intermetallic layer. [ABSTRACT FROM AUTHOR]

Abstract: Ferritic–martensitic steel T91 was previously irradiated in the Materials Open Test Assembly (MOTA) program of the Fast Flux Test Reactor Facility (FFTF) at 413°C up to 184dpa. The microstructure was analyzed by small angle neutron scattering (SANS) and transmission electron microscopy (TEM). Both SANS and TEM revealed a large fraction of voids with an average size of 29–32nm leading to a calculated void swelling of 1.2–1.6% based on the volume fraction of the voids in the sample. SANS gave no indication of second phase particles having formed under irradiation in the material. Using TEM, one zone was found where a few G-phase particles were analyzed. Quantities were however too low to state reliable particle densities. No alpha prime (α′) or Laves phase were observed in any of the investigated zones. [Copyright &y& Elsevier]

Abstract: The accumulation of radiation-induced defect clusters and He bubble formation in He+ ion irradiated nanocrystalline TiO2 and Fe–TiO2 multilayer thin films were investigated using transmission electron microscopy (TEM). Prior to ion irradiation it was found that the crystallinity of TiO2 layers depends on the individual layer thickness: While all TiO2 layers are amorphous at 5nm individual layer thickness, at 100nm they are crystalline with a rutile polymorph. After He+ irradiation up to ∼6dpa at room temperature, amorphization of TiO2 layers was not observed in both nanocrystalline TiO2 single layers and Fe–TiO2 multilayers. The suppression of radiation-induced amorphization in TiO2 is interpreted in terms of a high density of defect sinks in these nano-composites in the form of Fe–TiO2 interphase boundaries and columnar grains within each layer with nano-scale intercolumnar porosity. In addition, a high concentration of He is believed to be trapped at these interfaces in the form of sub-nanometer-scale clusters retarding the formation of relatively larger He bubbles that can be resolved in TEM. [Copyright &y& Elsevier]

The authors have studied the influence of deposition rate on the formation of growth twins in sputter-deposited 330 austenitic stainless steel thin films. Transmission electron microscopy shows that the volume fraction of twinned grains increases with increasing deposition rate, whereas the average columnar grain size and twin spacing stay approximately unchanged. These experimental results agree qualitatively with their analytical model that predicts deposition rate dependent formation of growth twins. The film hardness increases monotonically with increasing volume fraction of twinned grains. [ABSTRACT FROM AUTHOR]

In this research, innovative thermal spray deposition (Process I) and conventional hot extrusion processing (Process II) methods have been used to produce thin walled tubing (∼0.5 mm wall thickness) out of 14YWT, a nanostructured ferritic alloy. The effects of processing methods on the microstructure, mechanical properties and irradiation response have been investigated by using scanning electron microscopy (SEM), transmission electron microscopy (TEM) and, micro- and nano-hardness techniques. It has been found that these two processes have a significant effect on the microstructure and mechanical properties of the as-fabricated 14YWT tubes. Even though both processing methods yield the formation of various size Y-Ti-O particles, the conventional hot extrusion method results in a microstructure with smaller, homogenously distributed nano-oxides (NOs, Y-Ti-O particles < 5 nm) with higher density. Therefore, Process II tubes exhibit twice the hardness of Process I tubes. It has also been found that these two tremendously different initial microstructures strongly affect irradiation response in these tubes under extremely high dose ion irradiations up to 1100 peak dpa at 450 °C. The finer, denser and homogenously distributed NOs in the Process II tube result in a reduction in swelling by two orders of magnitude. On the other hand, inhomogeneity of the initial microstructure in the Process I tube leads to large variations in both swelling and irradiation induced hardening. Moreover, hardening mechanisms before and after irradiation were measured and compared with detailed calculations. This study clearly indicates the crucial effect of initial microstructure on radiation response of 14YWT alloys. [ABSTRACT FROM AUTHOR]

Abstract: Using in situ transmission electron microscopy, we studied the stability of growth twins. We observed the rapid migration of incoherent twin boundaries (ITBs), indicating that nanotwins are unstable. Topological analysis and atomistic simulations are adopted to explore detwinning mechanisms. The results show that: (i) the detwinning process is accomplished via the collective glide of multiple twinning dislocations that form an ITB; (ii) detwinning can easily occur for thin twins, and the driving force is mainly attributed to a variation of the excess energy of a coherent twin boundary; (iii) shear stresses enable ITBs to migrate easily, causing the motion of coherent twin boundaries; and (iv) the migration velocity depends on stacking fault energy. The results imply that detwinning becomes the dominant deformation mechanism for growth twins of the order of a few nanometers thick. [Copyright &y& Elsevier]

A nanostructured ferritic alloy (NFA), 14YWT, was produced in the form of thin walled tubing. The stability of the nano-oxides (NOs) was determined under 3.5 MeV Fe +2 irradiations up to a dose of ∼585 dpa at 450 °C. Transmission electron microscopy (TEM) and atom probe tomography (APT) show that severe ion irradiation results in a ∼25% reduction in size between the unirradiated and irradiated case at 270 dpa while no further reduction within the experimental error was seen at higher doses. Conversely, number density increased by ∼30% after irradiation. This ‘inverse coarsening’ can be rationalized by the competition between radiation driven ballistic dissolution and diffusional NO reformation. No significant changes in the composition of the matrix or NOs were observed after irradiation. Modeling the experimental results also indicated a dissolution of the particles. [ABSTRACT FROM AUTHOR]

The heavy-ion irradiation behavior of bulk zirconium-niobium multilayered composites was investigated up to large doses. Multilayers with an average individual layer thicknesses ranging between 15 and 80 nm were synthesized by accumulative roll bonding technique. The irradiation was performed with a defocused 7 MeV Zr2+ ion beam at 500 °C. The maximum dose achieved was ∼145 dpa at the depth of ∼1.5 μm from the irradiated surface. Sub-surface microstructural damage and the chemical redistribution were characterized by transmission electron microscopy and energy dispersive spectroscopy, respectively. Irrespective of the layer thicknesses, the irradiation condition caused layer instability and the extent of damage varied with the dose levels. Doses lesser than ∼60 dpa caused layer fragmentation and greater than ∼60 dpa resulted in layer dissolution. The chemical mixing of layers occur to a depth of ∼1 μm, consuming multiple bi-layer periods. Despite the elevated irradiation temperature (500 °C) and a slightly positive heat of mixing (+6 kJ/mol), no phase separation was observed and single-phase was retained in the mixed region. The results demonstrate that chemical mixing was facilitated by the liquid phase miscibility of Zr and Nb, which propelled the interdiffusion within the thermal spikes towards mixing. [ABSTRACT FROM AUTHOR]