Abstract The distribution of strain in hard mode oriented lamellar stacks of the two-phase γ-TiAl/α 2 -Ti 3 Al alloy Ti-45Al-2Nb-2Mn (at.%)-0.8 vol% TiB 2 was measured at several temperatures up to 633 °C by in situ micropillar compression, complemented by electron backscatter diffraction orientation mapping and digital image correlation strain mapping of a thermally stable surface Pt speckle pattern. Post-mortem transmission electron microscopy further identified the finest scale deformation structures. It was found that slip and twinning transverse to the lamellae operates within discreet bands that zigzag across the lamellar structure. The shear strain within each band is approximately constant across the pillar width. This is inconsistent with current energetic models for transverse twin formation in γ-TiAl, which assume independent, non-interacting twins. This is explained using a mathematical formulation for the stress required to operate this transverse mechanical twinning as a function of strain. This study has elucidated how the multi-scale combination of several transverse twinning systems on different {111} planes in γ-TiAl lamellae can relieve the elastic stresses generated at a lamellar interface by the primary (highest Schmid factor) twinning system. It is thought that the facilitation of this mechanism will promote the ductilisation of lamellar γ-TiAl alloys. This is crucial for an increased damage tolerance and ease of component manufacture, leading to a more widespread use of γ-TiAl alloys. Graphical abstract Image 1 [ABSTRACT FROM AUTHOR]

In this paper the occurrence of twinning parallel to the lamellae during compression at 700 °C of a polycrystalline nearly lamellar commercial γ-TiAl alloy, Ti-45Al-2Nb-2Mn(at%)-0.8 vol% TiB 2 , has been studied and shown to lead to the formation of cracks at colony boundaries. However, the occurrence of this longitudinal twinning mode was less common by at least a factor of ten in tests at room temperature. Furthermore, the debonding of colony boundaries caused by the shear strain of longitudinal twinning is exacerbated when the same γ-TiAl variant favourably oriented for twinning occurs repeatedly in the lamellar structure. This effect was caused by the preferential nucleation of certain γ-TiAl variants in the presence of TiB 2 boride reinforcement. It is shown that the boride additions increase the probability of double, triple or even higher order multiply stacked γ-variants. This increases the resulting shear strain that must be accommodated and hence the probability of crack nucleation. [ABSTRACT FROM AUTHOR]

The occurrence of longitudinal twinning in the engineering alloy Ti-45Al-2Nb-2Mn (at.%)-0.8 vol.% TiB 2 has been studied by measuring the changes in crystallographic orientation within individual lamellae during microcompression. Twinning in this alloy appeared to be a nucleation-limited process with the twins growing from lamellar boundaries at resolved shear stresses as low as 100 MPa, consistent with observations elsewhere. However, instead of forming twins ~ 10–200 nm in thickness, as in polysynthetically twinned crystals, the longitudinal twins in this alloy were initiated at a lamellar boundary and then spread through the whole lamella. [ABSTRACT FROM AUTHOR]