Search

Introduction: Peri-implantitis is an inflammatory process around dental implants that is characterised by bone loss that may jeopardize the long-term survival of osseo integrated dental implants. The aim of this study was to create a surface coating on titanium abutments that possesses cellular adhesion and anti-microbial properties as a post-implant placement strategy for patients at risk of peri-implantitis., Materials and Methodsmethods: Titanium alloy Grade V stubs were coated with gold particles and then subjected to ceramic conversion treatment (CCT) at 620 °C for 3, 8 and 80 h. The surface characteristics and chemistry were assessed using scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), and X-ray diffraction (XRD) analysis. The leaching profile was investigated by inductively coupled plasma mass spectroscopy (ICP-MS) for all groups after 7, 14 and 28 days in contact with distilled water. A scratch test was conducted to assess the adhesion of the gold coating to the underlying titanium discs. Two bacterial species (Staphylococcus aureus (SA) & Fusobacterium nucleatum (FN)) were used to assess the antibacterial behaviour of the coated discs using a direct attachment assay test. The potential changes in surface chemistry by the bacterial species were investigated by grazing angle XRD., Results: The gold pre-coated titanium discs exhibited good stability of the coating especially after immersion in distilled water and after bacterial colonisation as evident by XRD analysis. Good surface adhesion of the coating was demonstrated for gold treated discs after scratch test analysis, especially titanium, following a 3-hour (3 H) ceramic conversion treatment. All coated discs exhibited significantly improved antimicrobial properties against both tested bacterial species compared to untreated titanium discs., Conclusions: Ceramic conversion treated titanium with a pre-deposited gold layer showed improved antimicrobial properties against both SA and FN species than untreated Ti-C discs. Scratch test analysis showed good adherence properties of the coated discs the oxide layer formed is firmly adherent to the underlying titanium substrate, suggesting that this approach may have clinical efficacy for coating implant abutments., (Copyright © 2024 The Authors. Published by Elsevier Inc. All rights reserved.)

A correlative imaging methodology was developed to accurately quantify bone formation in the complex lattice structure of additive manufactured implants. Micro computed tomography (μCT) and histomorphometry were combined, integrating the best features from both, while demonstrating the limitations of each imaging modality. This semi-automatic methodology registered each modality using a coarse graining technique to speed the registration of 2D histology sections to high resolution 3D μCT datasets. Once registered, histomorphometric qualitative and quantitative bone descriptors were directly correlated to 3D quantitative bone descriptors, such as bone ingrowth and bone contact. The correlative imaging allowed the significant volumetric shrinkage of histology sections to be quantified for the first time (~15 %). This technique demonstrated the importance of location of the histological section, demonstrating that up to a 30 % offset can be introduced. The results were used to quantitatively demonstrate the effectiveness of 3D printed titanium lattice implants.

We present a novel route for producing a new class of titanium foams for use in biomedical implant applications. These foams are hierarchically porous, with both the traditional large (>300μm) highly interconnected pores and, uniquely, wall struts also containing micron scale (0.5-5μm) interconnected porosities. The fabrication method consists of first producing a porous oxide precursor via a gel casting method, followed by electrochemical reduction to produce a metallic foam. This method offers the unique ability to tailor the porosity at several scales independently, unlike traditional space-holder techniques. Reducing the pressure during foam setting increased the macro-pore size. The intra-strut pore size (and percentage) can be controlled independently of macro-pore size by altering the ceramic loading and sintering temperature during precursor production. Typical properties for an 80% porous Ti foam were a modulus of ∼1GPa, a yield strength of 8MPa and a permeability of 350 Darcies, all of which are in the range required for biomedical implant applications. We also demonstrate that the micron scale intra-strut porosities can be exploited to allow infiltration of bioactive materials using a novel bioactive silica-polymer composite, resulting in a metal-bioactive silica-polymer composite., (Copyright © 2010 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.)