Search

Purpose: The objective of this study was to fabricate PLA-based porous scaffold by 3D printing technology and to evaluate their cytotoxicity and biocompatibility under in vitro conditions in respect to bone tissue engineering., Material and Methods: Pure PLA in filamentous form was processed via 3D printing technology of fused filament fabrication into porous scaffolds. The structure and porosity of scaffolds were measured by metrotomography. PLA scaffolds were pre-treated by human serum, foetal bovine serum and complete cell culture medium to enhance bio-attractivity of the scaffold's surface for the adherence of the cells. Cells were enzymatically isolated from the periosteum of the proximal tibia and then expanded in monolayer. Periosteum-derived osteoprogenitors (PDOs) were seeded on the pre-treated PLA scaffolds and subsequent cell proliferation was measured by commercially available cell proliferation assay. Adherence of PDOs on the PLA scaffold was confirmed by scanning electron microscopy (SEM)., Results: Prepared scaffolds had well-defined structure and were characterized by uniform distribution of pores. They were non-toxic and biocompatible with PDOs, however, PLA scaffold with the periosteum-derived progenitor cells was significantly better in the group of scaffolds pre-treated with normal human serum., Conclusions: The obtained PLA porous scaffolds favored attachment of periosteum derived progenitors and proliferation, furthermore, cells penetrated into the scaffold through the interstitial pores which was meaningful for cytocompatibility evaluation.

Additive manufacturing has a great potential for creating hard tissue substitutes, such as bone and cartilage, or soft tissues, such as vascular and skin grafts. This study is a pilot study for 3D printing of a new material mixture potentially used as a tubular substitute for urethra replacement. This new mixture is a blend of polylactic acid (PLA) and polyhydroxybutyrate (PHB). The basic aspect that affects the 3D printing process is correct material preparation and setting of 3D printer parameters. Selection of material and printing parameters depend on printing technology. The printing technology affects material behavior during printing process. The goal of preprocessing and 3D printing process is to provide stabile conditions during manufacturing to obtain usable printed samples. The study deals with preparation of material before 3D printing - material drying. Moisture in material affects material degradation and viscosity during printing. According to this, it is necessary to verify recommended drying parameters. Verification was performed by printing strand samples from dried and non-dried material and also by calculating and comparing respective viscosities that change in time. Printed strand clearly show that non-dried material degrades in less than 10 min, what leads to inappropriate application in short-time printing. Dried material shows significant stability and degrades slightly during selected time span. For metrological verification of material stability two sample types were designed and manufactured - a cubic sample which represents basic scaffold structures and a tubular one that serves as urethra substitution. Obtained results showed appropriate usability of selected technology and printing parameters for PLA / PHB material blend., (Copyright © 2018 Elsevier B.V. All rights reserved.)