Search

Development of L10 FePd thin films with large bulk perpendicular magnetic anisotropy and a low damping constant may permit superior scaling of next-generation ultra-high density magnetic memory elements. The buffer layer influences the L10-order parameter, static and dynamic magnetic properties of FePd and demands consideration for the design of high anisotropy strength and low damping films. In this report, we systematically investigate the perpendicular magnetic anisotropy and damping constant of the FePd thin films engineered through the Cr/(Pt, Ru, Ir, Rh), Mo/Ir, and Ir buffer layers. We observed that the Ir(001), Cr(001)/Ir(001), Cr(001)/Pt(001), Cr(001)/Rh(001), and Cr(001)/Ru(001) buffer layers can induce highly oriented (001) FePd films while the Mo/Ir buffer layer does not. Of all the buffer layers, the largest perpendicular magnetic anisotropy Ku ∼ 1.2 MJ/m3 and damping constant α ∼ 0.005 were achieved for the Cr/Pt buffered FePd sample, consistent with a high ordering parameter S ∼ 0.82. The Cr/Ru buffered FePd sample shows the lowest α ∼ 0.008, despite having a lower S ∼ 0.64 and a lower Ku ∼ 0.9 MJ/m3. These film-level properties would be sufficient for the engineering of devices that require thermally stable, sub-10 nm lateral size elements with low damping for applications of low energy-delay magnetic memory devices. [ABSTRACT FROM AUTHOR]

Bulk perpendicular magnetic anisotropy materials are proposed to be a promising candidate for next-generation ultrahigh density and ultralow energy-consumption spintronic devices. In this work, we experimentally investigate the structure, thermal stability, and magnetic properties of FePd thin films seeded by an Ru layer. An fcc-phase Ru layer induces the highly-ordered L10-phase FePd thin films with perpendicular magnetic anisotropy (Ku ∼10.1 Merg/cm3). The thermal stability of FePd samples is then studied through the annealing process. It is found that a Ku ∼6.8 Merg/cm3 can be obtained with an annealing temperature of 500 °C. In addition, the Gilbert damping constant α, an important parameter for switching current density, is determined as a function of the testing temperature. We observe that α increases from 0.006 to 0.009 for the as-deposited FePd sample and from 0.006 to 0.012 for the 400 °C-annealed FePd sample as the testing temperature changes from 25 °C to 150 °C. These results suggest that Ru-seeded FePd provides great potential in scaling perpendicular magnetic tunnel junctions below 10 nm for applications in ultralow energy-consumption spintronic devices. [ABSTRACT FROM AUTHOR]

Nitrochlorobenzene compounds (NCBs) are of key interest in environmental monitoring due to their high toxicity. To better understand the presence and fate of NCBs in aquatic environments, an in-situ sampling technique of diffusive gradients in thin films (DGT) based on hydrophilic-lipophilic-balanced (HLB) resin, combined with gas chromatography, was developed to measure four typical NCBs, e.g. meta-chloronitrobenzene (MNCB), para-chloronitrobenzene (PNCB), ortho-chloronitrobenzene (ONCB), and 2,4-dinitrochlorobenzene (CDNB). The diffusion coefficients of MNCB, PNCB, ONCB, and CDNB in agarose-based gel were firstly determined in diffusion cell experiments and ranged from 7.19 × 10−6 to 7.49 × 10−6 cm/s. The capacities of HLB-DGT for MNCB, PNCB, ONCB, and CDNB were higher than 114.65, 117.52, 117.72, and 37.58 μg/cm2, respectively. The HLB-DGT performance on NCBs determination was demonstrated to be independent of natural fluctuations in pH (3–9), ionic strength (0.001–0.5 M), and dissolved organic matter concentrations (0–20 mg/L) and of deployment time (0–120 h). In the field application, the DGT-based method to measure NCBs not only proved to be accurate and effective, but also performed better than the grab sampling method under the variable conditions. This study demonstrates that the newly developed in-situ method based on DGT can provide an attractive alternative for the routine monitoring of NCBs in aquatic environments. Image 1 • A newly in situ method based on DGT for NCBs measurement is presented. • The diffusion coefficients of NCBs through agarose-gel are firstly reported. • The DGT method is independent of a wide range of environmental factors. • The DGT method is robust, effective, and highly sensitive. [ABSTRACT FROM AUTHOR]

Fe4N thin films with (001) texture were prepared by reactive sputtering on MgO substrates, utilizing either a Cr or Ag buffer layer to facilitate the epitaxial growth. X-ray diffraction, atomic force microscopy, and vibrating sample magnetometry measurements show that the Fe4N thin film grown on the Ag buffer layer is superior to that grown on the Cr buffer layer. The point contact Andreev reflection measurement was then conducted, and the spin polarizations were determined to be 61.1% and 81.3% for Fe4N thin films with Cr and Ag buffer layers, respectively. The 81.3% spin polarization is significantly higher than the ratio reported previously for Fe4N and is comparable with that of state-of-the-art Heusler alloys. This result is in agreement with the theoretical prediction on the discrepancy between the two differently defined spin polarizations for Fe4N. Moreover, our study indicates that an optimized growth process for Fe4N thin films is crucial for achieving a high spin polarization and that true half-metallicity could potentially be realized with Fe4N. The high spin polarization of Fe4N combined with its low fabrication temperature and simple composition makes Fe4N a competitive candidate to be a half-metallic ferromagnet in spintronic devices. [ABSTRACT FROM AUTHOR]