Magnetic and structural properties of Ni–Mn–Al thin films are investigated. It is demonstrated that the annealed film shows L21 phase at room temperature. Magnetometry measurements reveal that the annealed film is ferromagnetic and a first order transition in magnetization versus temperature measurement confirms that the martensite to austenite transition occurs around room temperature. Transmission electron microscopy measurements confirm that this structural change occurs just below room temperature. The splitting of Mn 2p3/2 level in x-ray photoelectron spectroscopy core level spectra of the annealed Ni–Mn–Al film, confirms that the origin of magnetism is definitely correlated with the local magnetic moment at the Mn atoms. [ABSTRACT FROM AUTHOR]

• B2 structured Ni-Mn-Al thin film has been successfully deposited by Co-sputtering. • Observation of large exchange bias field at low temperature. • Field induced FM ordering at temperature ~50 K. • The negative interface exchange constant. • AFM coupling between the coexisting phases. In the present work exchange bias in Mn rich Ni-Mn-Al film has been studied. The film has been deposited by cosputtering from the targets of Ni, Mn and Al. It exhibits an antiferromagnetic B2 phase at room temperature. At low temperature, magnetization versus temperature (M - T) measurement shows a bifurcation among ZFC and FC curves. Hysteresis (M-H) loops measurements reveal the occurrence of exchange bias phenomenon at low temperature. Large H EB of 2.2 kOe for 20 kOe cooling field has been observed. There occurs a field induced ordering at temperature ~50 K reflected as coinciding ZFC (zero-field cooled) and FC (field-cooled) curves at large magnetic field. AC susceptibility measurement indicates the occurrence of cluster glass behaviour at low temperature. The exchange constant obtained from the best fit to the experimental data was found to be Ji ≈ −2 meV. The negative interface exchange constant indicates AFM coupling occurs among the coexisting phases. Exchange bias phenomenon may be associated to the coexistence of antiferromagnetic and ferromagnetic like ordering at low temperature. Cooling field dependence of H EB and coercive field H C indicate that an increase in anisotropy and growth of ferromagnetic clusters occurs at high magnetic field. [ABSTRACT FROM AUTHOR]