Search

Due to their excellent thermophysical properties and high stability, inorganic salts and Forsalt mixtures are considered promising thermal energy storage materials for applications operating at high temperatures. A mixture of binary salts, such as CaCl2 (58 wt.%)-LiCl (42 wt.%), was investigated in this work to understand their thermal properties and stability for use in TES systems. Thermophysical properties, such as onset melting and crystallization temperature, enthalpy of fusion, and crystallization enthalpy, were all investigated experimentally via the use of a simultaneous thermal analyzer. The experimental findings demonstrated a suitable onset melting temperature of 488 °C and a solidification temperature of 480 °C. The heat of fusion was observed as 206 J/g, whereas the heat of crystallization was recorded as 180 J/g. Thermal repeatability tests indicated little variations in melting temperature; however, fusion enthalpies changed significantly over the course of 30 heating-cooling cycles. Additionally, the results obtained from the thermogravimetric analysis showed relatively weak thermal stability with considerable mass changes. This might be caused by the salts decomposing at elevated temperatures. In order to validate this, a high-temperature in-situ X-ray diffraction technique was used to verify the thermal instability of the binary salt mixture with and without thermal cycling. The thermal decomposition of parent salts and the subsequent formation of new phases with the formation of voids were shown to be the cause of thermal instability. It is concluded that the binary mixture of chloride salt showed suitable thermal properties but relatively weak thermal stability, which may limit its use in practical applications. [ABSTRACT FROM AUTHOR]

For thermal energy storage, the most promising method that has been considered is latent heat storage associated with molten salt mixtures as phase-change material (PCM). The binary salt mixture lithium chloride—lithium hydroxide (LiCl–LiOH) with a specific composition can store thermal energy. However, to the best of our knowledge, there is no information on their thermal stability in previous literature. The key objectives of this article were to investigate the thermophysical properties, thermal repeatability, and thermal decomposition behavior of the chosen binary salt mixture. FactSage software was used to determine the composition of the binary salt mixture. Thermophysical properties were investigated with a simultaneous thermal analyzer (STA). The thermal results show that the binary salt 32 mol% LiCl-68 mol% LiOH melts within the range of 269 °C to 292 °C and its heat of fusion is 379 J/g. Thermal repeatability was tested with a thermogravimetric analyzer (TGA) for 30 heating and cooling cycles, which resulted in little change to the melting temperature and heat of fusion. Thermal decomposition analysis indicated negligible weight loss until 500 °C and showed good thermal stability. Chemical and structural instability was verified by X-ray diffraction (XRD) by analysing the binary salt system before and after thermal treatment. A minor peak corresponding to lithium oxide was observed in the sample decomposed at 700 °C which resulted from the decomposition of LiOH at high temperature. The morphology and elemental distribution examinations of the binary salt mixture were carried out via scanning electron microscopy (SEM) coupled with energy dispersive spectroscopy (EDS). X-ray photoelectron spectroscopy was conducted for surface analysis, and their elemental composition verified the chemical stability of the binary salt mixture. Overall, the results confirmed that the binary salt mixture is a potential candidate to be used as thermal energy storage material in energy storage applications of up to 500 °C. [ABSTRACT FROM AUTHOR]