Titanium carbide (TiC) thin films were prepared by non-reactive simultaneous double magnetron sputtering. After deposition, all samples were annealed at different temperatures under high-vacuum conditions. This paper mainly discusses the influence of deposition methods and annealing temperatures on microstructure, surface topography, bonding states and electrical resistivity of TiC films. XRD (X-ray diffraction) results show that TiC thin films can still form crystals without annealing, and the crystallinity of thin films is improved after annealing. The estimated grain size of the TiC films varies from 8.5 nm to 14.7 nm with annealing temperature. It can be seen from SEM (scanning electron microscope) images that surfaces of the films are composed of irregular particles, and when the temperature reaches to 800 °C, the shape of the particles becomes spherical. Growth rate of film is about 30.8 nm/min. Oxygen-related peaks were observed in XPS (X-ray photoelectron spectroscopy) spectra, which is due to the absorption of oxygen atoms on the surface of the film when exposed to air. Raman spectra confirm the formation of TiC crystals and amorphous states of carbon. Resistivity of TiC films decreases monotonically from 666.73 to 86.01 μΩ·cm with the increase in annealing temperature. In brief, the TiC thin films prepared in this study show good crystallinity, thermal stability and low resistivity, which can meet the requirements of metal gate applications.

Carbon rich Nano-crystalline grain size tantalum carbide (Ta-C) thin films were prepared by non- reactive simultaneously dual magnetron sputtering. The main purpose of the current work was to investigate the influence of deposition method, deposition power, film thickness and annealing temperature on structural, surface morphology and electrical resistivity of TaC thin films. The experimental result shows that the growth rate of film was about 6.7 nm min−1 and films are growth like spherical structure. The atomic percentage of elements in the films were very sensitive to the deposition power, which even if the small amount of increases in the deposition power of Ta lead the increase of Ta content. However, a small change in Ta percentage did not result in a change in film structure and surface morphology. Annealing temperature did not cause structural changes in the films, but lead small changes in the grain size (range from 7.0 to 9.1 nm) and surface roughness. Resistivity variation of deposited TaC films on the annealing temperature shows random behavior which may cause by the deposition method. Nevertheless, the resistivity of the film decreases first and then increases when the thickness increases from 79.2 nm to 134 nm. Minimum resistivity of film appears at the thickness of 79.2 nm, about 235.2 μΩ.cm. In the end, deposited TaC thin films shows good thermal stability and low enough resistivity for gate electrode application.