Perovskite-type oxides La1-xCaxFeO3 (x = 0.0–1.0) were synthesized using combustion technique. The samples have been investigated using scanning electron microscopy (SEM), energy-dispersive X-ray (EDX) spectroscopy, Fourier transform infrared (FT-IR) spectroscopy, ultraviolet–visible diffuse reflectance spectroscopy (DRS), X-ray powder diffraction (XRPD) using Rietveld refinement, thermogravimetric analysis (TGA) and dielectric spectroscopy. The SEM images showed spherical-shaped agglomerates having a non-uniform distribution of size. The EDX results suggested that the experimental chemical composition was in good accordance with the nominal values. FT-IR revealed multiple peaks in the range of 580–510 cm−1 due to asymmetric stretching of the octahedron. The reflectance spectra showed characteristic d → d transitions arising from the Fe 3d and the highest optical band gap energy ( E g ) of 2.57 eV was exhibited by LaFeO3, while the lowest E g (1.41 eV) was shown by La1-xCaxFeO3 with x = 0.6. The results suggest that these samples are suitable for photocatalytic applications. From phase evaluation of the diffraction patterns, it was found that five distinct phases exist in the series. A phase transformation from orthorhombic ( Pnma ) to cubic ( P m 3 ¯ m ) was found when x was increased from 0.4 to 0.6. TGA showed that LaFeO3 was the most stable with a residual mass of ~ 97 wt% at 900 ∘ C compared to CaFeO3 (~ 70 wt% at 900 ∘ C ). The evaluation of frequency-dependent (20 Hz–20 MHz) dielectric properties agreed with the Maxwell–Wagner two-layer model. After Ca2+ substitution, tan δ at 20 Hz significantly reduced from ~ 103 for x = 0 to ~ 100 for x = 1.0. The high polarization observed was due to e− hopping between Fe2+ ↔ Fe3+. The electrical models of the samples show non-Debye type relaxation behavior, while the ac conductivity enhanced with increasing frequency which was in accordance with Koop's phenomenological theory. [ABSTRACT FROM AUTHOR]

Epoxy composites were prepared by doping nano Zirconia Toughened Alumina (ZTA) which were synthesized by solution combustion method into epoxy resin and hardener. Initially ZTA nanopowder was characterized to check its purity, morphology and to confirm its metal-oxide bonding using XRD, SEM and FTIR respectively. The thermal properties such as TGA and DTG were also analysed. The polymer composites were obtained by uniformly dispersing ZTA nanopowder into epoxy using an ultrasonicator. Polymer composites of various concentrations viz, 0.5, 1, 1.5, 2 and 2.5 wt% were synthesized, all concentrations were prepared on weight basis. All the polymer composites were tested for compression properties, flexural properties and tensile properties. Best results for all the mechanical properties were obtained for epoxy with 1.5 wt% ZTA composites. Electrical properties such as breakdown voltage and breakdown strength were analysed and outstanding results were observed for epoxy with 2.5 wt% ZTA composite. [ABSTRACT FROM AUTHOR]