The red-emitting perovskite material has received widespread attention as a long-wavelength optical gain media. But the easy phase change in the air limits its practical application. Herein, red CsPbBr x I3âˆ' x /SiO2 quantum dots (QDs) are prepared by a ligand-mediated hot injection method in which 3-aminopropyl-triethoxysilane (APTES) is used instead of the usual oleylamine (OAm) ligand. Through the hydrolysis of amino groups, a thin silicon layer is formed on the QD surface, improving the stability and without causing the aggregation of QDs. We find that the ratio of I/Br and the size of QDs can be tuned by adjusting the APTES amount. Moreover, this ligand-mediated synthesis effectively passivates the surface defects, so the photoluminescence quantum yield is remarkably improved, and the carrier lifetime is prolonged. The amplified spontaneous emission is achieved under 532 nm nanosecond laser excitation. Compared with the original CsPbBrI2-OAm QD films, the threshold of CsPbBr x I3âˆ' x /SiO2 QD films is reduced from 403.5 to 98.7 ÎĽ J cmâˆ'2, and the radiation stability is significantly enhanced. Therefore, this material shows great potential in the random laser field. [ABSTRACT FROM AUTHOR]

All inorganic cesium lead halide perovskite (CsPbX3; X = Cl, Br, or I) quantum dots (QDs) have received widespread attention as a class of favorable optical gain materials. The key issue of CsPbX3 perovskites is their instability under light or exposure to air. Notably, the inherent phase instability of CsPbI3 QDs severely restricts the development of red-light emission. Herein, we propose a simple method to post-process CsPbBr3 QDs with a ZnI2 solution. The prepared CsPbBryI3−y (named CPBI-z, where z corresponds to the photoluminescence peaks' position) QDs exhibit adjustable photoluminescence in the range of 550–640 nm. The photoluminescence quantum yield is increased from 73.3% to 97.2% as the surface defects of QDs are passivated by I− and Zn2+. Compared with the pristine CsPbBr3 QDs, the post-processed QDs are more stable under ultraviolet irradiation and in the air. Aside from that, under 532 nm nanosecond laser excitation, CPBI-z QD films exhibit excellent amplified spontaneous emission performance. The CPBI-640 QD film shows a low threshold, 102 μJ cm−2 for red stable amplified spontaneous emission. [ABSTRACT FROM AUTHOR]