Superconducting electronics often require high-density microwave interconnects capable of transporting signals between temperature stages with minimal loss, cross talk, and heat conduction. We report the design and fabrication of superconducting 53 wt% Nb-47 wt% Ti (Nb47Ti) FLexible coAXial ribbon cables (FLAX). The ten traces each consist of a ${\oslash}$ 0.076 mm NbTi inner conductor insulated with PFA (${ \oslash }$ 0.28 mm) and sheathed in a shared 0.025 mm thick Nb47Ti outer conductor. The cable is terminated with G3PO coaxial push-on connectors via stainless steel capillary tubing (${ \oslash }$ 1.6 mm, 0.13 mm thick) soldered to a coplanar wave guide transition board. The 30 cm long cable has 1 dB of loss at 8 GHz with $-$ 60 dB nearest neighbor forward cross talk. The loss is 0.5 dB more than commercially available superconducting coax likely due to impedance mismatches caused by manufacturing imperfections in the cable. The reported cross talk is 30 dB lower than previously developed laminated NbTi-on-Kapton microstrip cables. We estimate the heat load from 1 K to 90 mK to be 20 nW per trace, approximately half the computed load from the smallest commercially available superconducting coax from CryoCoax. [ABSTRACT FROM AUTHOR]

Large arrays of superconducting devices such as microwave kinetic inductance detectors require high density interconnects from higher temperatures with minimal heat load, low loss, and negligible crosstalk capable of carrying large and overlapping bandwidth signals. We report the fabrication of superconducting 53 wt% Nb-47 wt% Ti (Nb-47Ti) microstrip transmission lines laminated onto flexible polyimide substrates with lengths up to 40 cm and up to ten traces. The 50 Ω traces terminate in G3PO coaxial push-on connectors. We found transmission losses of 2.5 dB and a nearest-neighbor forward crosstalk of -25 dB at 8 GHz on a typical 5 trace, 1.8-cm-wide, 0.198-mm-thick, 22-cm-long flex cable at 30 mK. A simple two-port analytical model and subsequent Sonnet simulations indicate that this loss is mainly due to a complex impedance mismatch from wirebonds at the end connector without which the insertion loss would be <;2.7 dB/m. This is about six times worse than the transmission measured in Coax Company, Ltd.'s smallest (Ø 0.86 mm) Nb-47Ti coaxial cables, possibly from differences in the low temperature loss properties of polyimide laminates versus PTFE or from unaccounted resistive losses in the copper adapter coaxes of our tested device. Heat flow calculations from literature data show that the 0.198-mm-thick flex cables tested have roughly equivalent thermal conductance per trace below 4 K compared to the Ø 0.86 mm Nb-47Ti coaxial cables. [ABSTRACT FROM AUTHOR]