Search

Copyright of Journal of Natural Fibers is the property of Taylor & Francis Ltd and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)

The high content of lignin is the major disadvantage for kenaf fiber separation. In order to remove lignin effectively as well as to improve the dispersion of kenaf fibers, a novel degumming process with steam explosion followed by Fenton treatment was applied in the present study. Fibers prepared by traditional chemical degumming process and raw kenaf samples were employed as control. The fiber microstructure, chemical composition, and physical and mechanical properties were characterized and analyzed in this paper. The results revealed that steam explosion coupled with Fenton treatment could effectively remove the gum materials from kenaf bast, which performed noticeably effectively in lignin removal. The refined dry fibers showed a clean and smooth surface. The average fineness of the refined dry fibers degummed by the novel process was measured to be higher than 70 dtex, which is much better than fibers prepared by the traditional chemical degumming process. It can be concluded that the novel degumming process of combined steam explosion and Fenton treatment is feasible and effective for kenaf degumming. [ABSTRACT FROM AUTHOR]

Degumming is the dominant method to isolate cellulosic fibers in the textile industry. High content of lignin is the principle obstacle in bast-fibers degumming. In order to remove lignin efficiently, the treatment using steam explosion coupled with Fenton oxidation was conducted on kenaf bast in this study. The influence and mechanism of the combined treatment of steam explosion and Fenton oxidation were studied. Fiber microstructure, composition proportion and distribution, cellulose Segal crystallinity and polymerization as well as residual lignin structure were analyzed. The results showed that the pretreatment of steam explosion could sufficiently extract most of the hemicellulose from kenaf bast. Also, the Fenton oxidation followed by alkaline boiling could effectively remove the lignin from the fiber, especially from the fiber surface. The refined dry fibers produced only remained 8.82% of hemicellulose and 9.36% of lignin. And the whole treatment process didn’t change the cellulose crystalline structure but could gradually degrade hemicellulose, lignin and other amorphous gummy matter as well as disordered areas in cellulose, leading to the increase of fiber Segal crystallinity from 62.02 to 70.12%. Part of cellulose was damaged with the increase of degumming intensity, resulting in the decrease of the polymerization degree of cellulose. Meanwhile, the structure of residual lignin changed during the degumming stages of steam explosion, Fenton oxidation and alkaline boiling. All the results revealed that the treatment of combined steam explosion and Fenton oxidation is significantly effectual for isolating bast-fibers. [ABSTRACT FROM AUTHOR]

Kudzu is cosmopolitan and low-cost as a source of fiber, food, medicine, and fuel. However, it is not well utilized as a kind of fiber due to the degumming problem. In order to take full advantage of the kudzu resource in the world and expand the application field of kudzu fiber, this study deals with preparation of kudzu fiber by combined steam explosion and chemical degumming. Kudzu fibers are characterized by scanning electron microscopy, Fourier transform infrared spectroscopy, and X-ray diffraction. It is found that kudzu fiber after combined degumming has a clean surface with most nonfibrous composition removed and fibers dispersed; the cellulose I structure of kudzu cellulose did not change after treatment but its crystallinity increased. These results suggest this combined degumming is feasible for preparing kudzu fiber. It will probably provide theoretical basis for subsequent utilization of kudzu fibers. [ABSTRACT FROM PUBLISHER]

To enhance the degumming effect of steam explosion on kenaf fiber, different chemical reagents including hydrogen peroxide (H2O2), sulfuric acid (H2SO4), and sodium hydroxide (NaOH) presoak combined with steam explosion were used and compared in this article. Distilled water coupled with steam explosion treatment and kenaf raw samples were used as control. The fiber morphology, chemical composition, crystalline structure, degree of fineness, and breaking tenacity of kenaf fibers after treatment were studied. The results showed that hydrogen peroxide (H2O2) performs better on removing lignin. It not only splits fibers, but also keeps the fiber's tenacity during steam explosion treatment. Dilute sulfuric acid (H2SO4) performs better on hemicellulose removal, but it damages the fiber cellulose during steam explosion treatment and cause the fiber strength decrease a lot. Sodium hydroxide (NaOH) performs the best on removing hemicellulose and lignin, and splits fiber well. However, the breaking tenacity of the fiber is lower than the fiber pretreated by H2O2. Besides, NaOH is a pollutant to the environment. In conclusion, H2O2 could be considered as the most promising reagent to be used in combined presoak-steam explosion system. [ABSTRACT FROM AUTHOR]

The study of the main chemical composition degradation, especially cellulose degradation at high temperatures and within high moisture environments, provides important information that can guide biomass processing using steam explosion (STEX) and other similar treatments. In this paper, kenaf bast was treated using STEX at pressures of 0.5, 1.0, and 1.5 MPa. The chemical composition change and the infrared spectra were investigated. The crystalline index and degree of polymerization of kenaf cellulose were also quantified. It was found that pectin and hemicellulose could be easily degraded with the STEX treatment, while lignin only exhibited slight decomposition; cellulose degraded at 1.5 MPa STEX treatment on the kenaf. Research also indicates that cellulose with a low molecular weight can be removed with a low-pressure STEX treatment. By coupling STEX with chemical degumming process, the high-quality kenaf fiber with 7.12% residue gum content and 134.5 Nm fineness can be obtained. [ABSTRACT FROM AUTHOR]

Ramie provides the longest and strongest natural fiber in textile industry, but its traditional degumming process is costly and requires a large amount of alkali, which causes serious environmental concerns. In the current work, a steam explosion (STEX) treatment followed by sodium percarbonate (SP) soak degumming process was investigated. Microstructure, chemical composition and mechanical properties of the refined ramie fibers were comprehensively characterized. The residual gum content was below 5%, the fineness was higher than 1600 Nm (6.25 dtex), the breaking tenacity was 5.4 cN/dex, and the whiteness was above 50%. All of the properties met the requirements of Chinese national standard, and the breaking tenacity and whiteness were notably better than those of the fibers degummed traditionally. In addition, environmental impacts of the new degumming process were evaluated. Only 50% chemicals were needed for the new process, and chemical oxygen demand (COD) of the waste reduced to 35% of the traditional method. Therefore, the new method was more environment-friendly and economically feasible. It has great potential for industry applications. [ABSTRACT FROM AUTHOR]