Search

Holmium (Ho 3+ ) substituted W-type hexagonal ferrites (BaCo 2 Fe 16 O 27 ) were prepared by sol gel auto-combustion technique. The precursors were prepared by Ba 2+ , Fe 3+ nitrates solutions with citric acid as chelating agent. The prepared powder was sintered at 950 °C for 8 h to produce a single phase of W-type hexa ferrite with corresponding crystallite size ranging from 34 nm to 44 nm. The thermal decomposition of nitrate-citrate gel of as-prepared powder was investigated by TGA and DTA. The FTIR spectral study reveals the presence of two absorption bands which are characteristics of hexaferrites. DC electrical resistivity increases from 3.01×10 9 to 5.69×10 10 (ohm-cm). The real and imaginary parts of dielectric constant (ɛʹ, ϵ״) and dielectric loss tangent (tan δ) are determined in the frequency range of 20 Hz–1 MHz. It was observed that both real and imaginary parts of the dielectric constant and tanδ decrease with the increase of frequency on the basis of Wagner and Koop's theory. [ABSTRACT FROM AUTHOR]

The sol–gel auto-combustion method was adopted to synthesize nanomaterials of single-phase X-type hexagonal ferrites with the composition of Sr 2− x Gd x Ni 2 Fe 28− y Cd y O 46 ( x =0.00, 0.02, 0.04, 0.06, 0.08, 0.10 and y =0, 0.1, 0.2, 0.3, 0.4, 0.5). The structural properties were carried out by XRD analysis and the lattice parameters show variation with the doping of Gd–Cd. The average particle size measured by TEM was in the range of 8–10 nm which is beneficial in obtaining suitable signal-to-noise ratio in recording media and biomedical applications. The room temperature resistivity enhanced with the increase of the dopant concentration. The increase in resistivity indicates that the synthesized materials can be considered good for the formation of the multilayer chip inductors (MLCIs) as well as for the reduction of eddy current losses. The dielectric constant decreased with the increase in the frequency which is the general reported trend of the hexagonal ferrites and can be explained on the basis of Koop׳s theory and Maxwell–Wagner polarization-model. The abnormal dielectric behavior indicates the formation of small polarons in the material. The maximum value of tangent loss at low frequencies reflects the application of these materials in medium frequency devices (MF). [ABSTRACT FROM AUTHOR]

A series of single phase spinel ferrites having chemical formula Mg 0.5 Zn 0.5 Pr x Fe 2− x O 4 ( x =0.00, 0.05, 0.10, 0.15, 0.20, 0.25) were prepared using the sol–gel technique after sintering at 700 °C. The thermal decomposition behavior of an as prepared powder was investigated by means of DTA/TGA analyses. The sintered powders were then characterized by Fourier transform infrared spectroscope, X-ray diffraction, scanning electron microscope, energy dispersive X-ray spectroscope and vibrating sample magnetometer. X-ray diffraction patterns confirm the single phase spinel structure of prepared ferrites without the presence of any impurity phase. The value of lattice parameter ( a ) increases with the increase of Pr contents ( x ) into the spinel lattice. The grain size estimated from electron microscope images is in the range of 2.75–5.4 µm which confirms the spinel crystalline nature of the investigated samples. The saturation magnetization ( M s ) decreases whereas coercivity ( H c ) increases with the increase of Pr contents ( x ). The measured parameters suggest that these materials are favorable for high frequency applications and as core materials. [ABSTRACT FROM AUTHOR]

Abstract: The magnetic and microwave characterization of single phase hexaferrites of entirely new composition Ba1-x Sr x Co2AlFe15O27 (x=0.2–1.0) for application in a microwave absorber, have been reported. The samples synthesized by sol–gel method were investigated by differential thermal analyzer, Fourier transform infrared spectroscope, X-ray diffractometer, field emission gun scanning electron microscope, vibrating sample magnetometer and vector network analyzer. Platelet grains exhibit well defined hexagonal shape which is a better shape for microwave absorption. M–H loops for a selected sample were measured for a temperature range of 4.2–400K. Moreover M–H loops for all Sr-substituted samples were also measured at room temperature up to a maximum applied field of 9T. Saturation magnetization values were calculated by the law of approach to saturation. The room temperature coercivity for all the samples is found to be a few hundred oersteds which is necessary for electromagnetic materials and makes these ferrites ideal for microwave devices, security, switching and sensing applications. The complex permittivity, permeability and reflection losses of a selected ferrite–epoxy composite were also investigated over a frequency range of 0.5–13GHz. [Copyright &y& Elsevier]

Abstract: A series of single phase W-type Sr3−x Ce x Fe16O27 (x=0, 0.02, 0.04, 0.06, 0.08, 0.10) hexagonal ferrites prepared by the Sol–Gel method was sintered at 1050°C for 5h. The X-ray diffraction analysis reveals that all the samples belong to the family of W-type hexagonal ferrites. The c/a ratio falls in the range of W-type hexagonal ferrites. The grain size was measured by SEM varies from 0.7684 to 0.4366μm which shows that the Ce3+ substituted samples have smaller grain size than pure ferrite Sr3Fe16O27 which results from the difference in ionic radii of Ce3+ (1.034Å) and Sr2+ (1.12Å). The room temperature resistivity of the present samples varies from 6.5×108 to 272×108 Ω-cm. The coercivity increases from 1370 to 1993Oe which is consistent with the decrease in grain size. The coercivity values indicate that the present samples fall in the range of hard ferrites. The large value of H c may be due to domain wall pinning at the grain boundaries. [Copyright &y& Elsevier]