In this paper, the electrical properties different diodes were reported. Pure and Al-doped ZnO thin films of different concentrations (Al: 1, 2 and 3 wt.%) were deposited by sol-gel dip-coating onto p-Si substrate to form heterojunctions. Zinc acetate dehydrate, Hexahydrate aluminum chloride, ethanol and ethanolamine were used as a starting material, doping, solvent and stabilizer, respectively. The dip-coating process with drying was repeated 6 times to obtain multilayer films. The morphological and electrical properties of the thin films as a function of Al concentration have been investigated using atomic force microscopy (AFM) and current-voltage (I-V) measurements at room temperature. AFM images revealed that grain sizes and surface roughness increase with increasing Al concentration. I-V characteristics of the diodes exhibited high and low currents under forward and reverse bias, respectively. The ideality factors (n), rectification ratio (RR) and barrier heights (BH) were found to range from 1.97 to 8.34, 0.84 to 5958 and 0.80 to 0.86 eV for different Al doping concentrations, respectively. These findings showed no monotonic behaviour of the calculated parameters with varying Al doping concentrations. The best electrical characteristic was obtained for the sample n-ZnO: 2 % Al/p-Si, with an ideality factor of 1.97 eV, reverse saturation current of 1.69 ± 10– 8 A, rectification ratio of 5958 at ± 2 V, and barrier height of 0.85 eV. [ABSTRACT FROM AUTHOR]

• The present work is an important issue to optimize the CZTS solar cell performance. • We've first make an experimental study of the CZTS thin film which it's prepared by sol gel dip coating technique. • Used of the experimental parameters obtained by the experience on the numerical study. • By Scaps-1D we study the effect of the active layer thickness on the performance of the studied cell, and also the effect of, shallow acceptor density and work temperature. This work aims to study the basic Characteristics of CZTS thin films produced by chemical solution process in addition to a numerical study of the CZTS-based solar cells. In this context, eco-friendly and cost effective thin films of CZTS were coated on glass substrates by sol–gel dip-coating method. This method is used to grow crystalline CZTS thin films without sulfidation processes. The structural and optical properties have been carried out by X-ray Diffraction (XRD) and UV/Visible spectroscopy. The oxidation states of CZTS thin film have been studied by, X-ray photoelectron spectroscopy XPS analysis. The performance of CZTS solar cells has been investigated with the simulator SCAPS-1 D. The impact of different parameters like the CZTS absorber layer thickness, the carrier doping density and the operation temperature has been studied to get better understanding of the properties of our cells. [ABSTRACT FROM AUTHOR]