Search

With its excellent properties such as high thermal conductivity, strong radiation resistance and high electron mobility, diamond has become one of the most suitable materials for radiation detectors. Detector-grade diamond requires low impurity content, low dislocation density and other defects. However, it is very difficult to keep low impurities and low dislocations simultaneously in the actual crystal growth process. In this study, microwave plasma chemical vapor deposition (MPCVD) method was used to grow diamond layer on two high-quality HPHT diamond substrates with the previously optimized process conditions. The nitrogen impurity content and structure of the HPHT substrate and growth layer were characterized and analyzed. The results show that, the content of nitrogen impurity on two HPHT substrates are 7. 1 x 10-6% and 4. 04 x 10-8%, respectively, whereas in their epitaxial diamond layers, the nitrogen impurity content are 2. 1 x 10-7% and 5 x 10-8%, respectively. The full width at half-maximum of the rocking curve shows that the dislocation density of the MPCVD growth layer is comparable to the HPHT substrate, though some dislocations were introduced into the MPCVD growth layer, which increases the stress. Overall, the dislocations in the HPHT substrate and epitaxial layer of single crystal diamond are in the same order of magnitude. The high-purity single crystal diamond prepared in this work may be used in nuclear radiation detection and semiconductor fields. [ABSTRACT FROM AUTHOR]

Oxygen evolution reaction (OER) is critical in water splitting for green hydrogen gas production due to its sluggish kinetics; however, commercial OER catalysts commonly suffer from high cost, low catalytic activity and poor stability. Herein, we developed a C+ ion implantation method to modify single crystal diamond, and the resultant surface amorphous layer not only raised the active site number but also increased the content of the C=O group, thus significantly improving the OER activity. The C+ ion implanted high-temperature and high-pressure (C+-HTHP) and chemical vapor deposition (C+-CVD) diamonds both exhibit low OER overpotential with η 10 of 317 mV and 325 mV respectively, superior to those of HTHP diamond (360 mV), CVD diamond (395 mV) and RuO 2 (364 mV). The potentiostatic testing shows that the C+ implanted diamonds almost didn't undergo the rise of OER overpotential upon catalysis for more than 12 h at a current density of 10 mA cm−2, suggesting a high catalytic stability, owing to the strong bonding between single crystal diamond and amorphous carbon layer. For the first time, we utilized carbon ion implantation to prepare diamond-based high-performance OER catalyst, which broadens the understanding of carbon-based materials in OER catalysis. [ABSTRACT FROM AUTHOR]

The demand of small-angle x-ray scattering (SAXS) windows for in-situ characterization of materials nano-structures in a heated vacuum environment has been increased dramatically. High-quality diamond prepared by chemical vapor deposition (CVD) has become the preferred window material due to its excellent optical and mechanical properties. However, impurities and defects in diamonds may lead to the strong X-ray scattering especially in the heating process, affecting the testing accuracy of the object. In this work, single-crystal diamond (SCD) and polycrystalline diamond (PCD) films with different quality were prepared, and their SAXS properties were investigated at room temperature and heating under vacuum. The results show that the scattering intensity of the undoped high-quality SCD is small and uniform, while that of the SCD window doped with a small amount of nitrogen increases, mainly due to the nitrogen atoms and vacancy clusters scattering. While for the PCDs, the grain boundaries and the dark features lead to strong scattering background. As the temperature rises from room temperature to 280 °C, although the phonon vibration of diamonds exhibits the obvious temperature dependence, the coherent scattering of diamonds with X-ray hardly changes, indicating no new scatterers with the changed gyration radius were generated in the heating process. SCD and PCD windows were successfully applied in an in-situ heating SAXS cell. [ABSTRACT FROM AUTHOR]