Search

In practical engineering applications, silt is prone to liquefaction and quicksand. This paper mainly studies the improvement effects of urease, lignin and their mixture on the strength and liquefaction resistance of silt. Based on the results and phenomena of an unconfined compressive strength and dynamic triaxial test, the improvement effects of the compressive strength, deformation resistance and liquefaction resistance of silt under different improvement schemes are analyzed, and the optimal values of the cement or lignin when enzyme-induced calcium carbonate precipitation (EICP) technology, lignin alone or EICP and lignin are obtained. The results show that the optimum concentration of the constant temperature and humidity sample (referred to as the constant humidity sample) and the constant temperature immersion sample (referred to as the soaking sample) of urease in the unconfined compressive strength test is 1.0 mol/L, and the compressive strength of the soaking sample is 4.9 MPa, which is 1.56 times that of the constant humidity sample; the optimum addition ratio of the lignin-improved constant humidity sample is 3%, and its compressive strength is 2.07 Mpa; the optimum addition ratio of the samples immersed at constant temperature is 4%, and the compressive strength is 3.05 MPa; when urease combines with lignin to improve silt, 4% is the best lignin addition ratio, the compressive strength of the constant humidity sample reaches 1.57 Mpa and the compressive strength of the soaking sample reaches 3.75 MPa; in the dynamic triaxial multi-stage cyclic load test, all samples were cured at constant humidity sample, and in the urease modified silt scheme, 1.0 mol/L was the optimal cement concentration; in the scheme of improving silt with lignin, 3% is the optimal addition ratio; when 1.25 mol/L cementation solution plus urease crude extract is combined with different ratios of lignin in the experimental scheme, 3% is the best lignin addition ratio. [ABSTRACT FROM AUTHOR]

At present, in the field of geotechnical engineering and agricultural production, with increasingly serious pollution an environmentally friendly and efficient means is urgently needed to improve the soil mass. This paper mainly studied the microbial induced calcium carbonate precipitation (MICP) technology and the combined effect of MICP technology and lignin on the improvement of silt in the Beijing area. Through unconfined compressive strength and dynamic triaxial test methods, samples improved by microorganisms were studied to obtain the optimal values of cement concentration and lignin under these two test schemes. The results show that after the incubation time of Sporosarcina pasteurii reached 24 h, the OD600 value was 1.7–2.0 and the activity value (U) was 930–1000 mM ms/min. In the unconfined static pressure strength test, after MICP treatment the optimal concentration of cementitious solution for constant temperature and humidity samples and constant-temperature immersion samples was 1.25 mol/L. The compressive strength of the constant temperature and humidity sample was 1.73 MPa, and the compressive strength of the constant-temperature immersion sample was 3.62 Mpa. At the concentration of 1.25 mol/L of cement solution, MICP technology combined with lignin could improve the constant temperature and humidity silt sample. The optimal addition ratio of lignin was 4%, and its compressive strength was 1.9 MPa. The optimal lignin addition ratio of the sample soaked at a constant temperature was 3%, and the compressive strength was 4.84 MPa. In the dynamic triaxial multi-stage cyclic load test, the optimal concentration of cementation solution for the constant temperature and humidity sample after MICP treatment was 1.0 mol/L, and the failure was mainly inclined cracks. However, in the condition of joint improvement of MICP and lignin, the sample mainly had a drum-shaped deformation, the optimal lignin addition ratio was 4%, and the maximum axial load that the sample could bear was 306.08 N. When the axial dynamic load reached 300 N, the strain accumulation of the 4% group was only 2.3 mm. In this paper, lignin, an ecofriendly material, was introduced on the basis of MICP technology. According to the failure shape and relevant results of the sample, the addition of lignin was beneficial for the improvement of the compressive strength of the sample. [ABSTRACT FROM AUTHOR]