Search

In this approach, polyelectrolyte film-coated nanofibrous silk fibroin (SF) nonwovens were prepared from the alternate deposition of positively charged polyethylenimine (PEI) and negatively charged SF using electrostatic layer-by-layer (LBL) self-assembled technology. The composite membranes were characterized by scanning electron microscopy (SEM) and Fourier transform infrared (FTIR) spectrometer. The SF-PEI multilayer-assembled nanofibers (less than five layers) were fine and uniform with the fiber diameter from 400 nm to 600 nm, and had very large surface area and high porosity (more than 70%). The amino groups of PEI were proved to be deposited onto SF nonwovens, which granted the coated nonwovens with potential applicability for copper ions adsorption. The PEI films coated SF substrate showed much higher copper ions adsorption capacity than that of ethanol treated SF nanofibers. Adding the number of PEI coated could enhance the Cu 2+ adsorption capacity significantly. The maximum milligrams per gram of copper ions adsorbed reached 59.7 mg/g when the SF substrate was coated with 5 bilayers of SF-PEI. However, the copper ions adsorption capacity had no obvious change as the number of PEI continued to increase. These results suggest potential for PEL film-coated nanofibrous nonwovens as a new adsorbent for metal ions. [ABSTRACT FROM AUTHOR]

Mesoporous particles have attracted considerable attention in drug delivery system, because they can offer fast mass transport and overcome the diffusion restriction as occurred in micro/nano- porous particles. Conventional mesoporous particles are generally dominated by inorganic compounds, little concern has been raised over biodegradable organic polymers, especially silk fibroin. Here, we show that Antheraea pernyi (A. pernyi) silk fibroin, rich in Arg-Gly-Asp (RGD) moiety, can be developed into mesoporous particles via self-assembly in a direct and eco-friendly (without any organic solvents) manner for sustained release of 5-fluorouracil (5-FU). By cultivating a mild condition at 40 ℃, a mesoporous structure was successfully achieved without any foreign organic solvents. The self-assembled mesoporous particles were quasi-spherical in shape with an average diameter of 1.58 µm. Mesopores ran through the entire particles to construct a divergent structure with external pore diameters ranging from 30 to 60 nm and internal pore width of 6.225 nm. The mesoporous particles were predominated by β -sheet conformation (∼45%), which effectively reduced the weight-loss ratio to 2.6%. 5-FU was encapsulated into the mesoporous particles by hydrogen bonding and van der Waals force as well as ionic interactions. Drug loading efficiency and encapsulation efficiency were found to be 26.24% and 50.36%, respectively. The mesoporous particles enabled sustained drug release, with approximately 90% release after 110 h. After a small burst release (20%) of the surface-bound 5-FU, a slower linear release dominated by Fickian-diffusion occurred. These features together with the excellent biocompatibility of A. pernyi silk indicated that the self-assembled mesoporous particles would be an ideal carrier for sustained drug release to meet critical requirements of biomaterials. Furthermore, without any foreign materials, this one-step strategy may offer new green chemistry approaches as well as options to load bioactive drugs. [Display omitted] • Mesoporous Antheraea pernyi particle was fabricated in a direct and eco-friendly way. • Mesopores ran through the entire particles to construct a divergent structure. • The mesoporous particles were predominated by β -sheet conformation. • The mesoporous particles enabled sustained release of 5-FU. [ABSTRACT FROM AUTHOR]