Aims: The aim of this study was to compare the influence of operators on the microhardness and compressive strength of mineral trioxide aggregate (MTA)., Materials and Methods: Forty dental specialists were asked to prepare a series of MTA samples. The tested material was ProRoot MTA (DentsplyMaillefer, Switzerland). Each participant prepared one sample to a consistency they considered acceptable for use in practice (improvised group) and another one according to the manufacturer's recommended water-to-powder (WP) ratio (pre-weighed group). The samples were incubated at 37°C and 95% humidity for 4 days. Parameters evaluated in this study were microhardness and compressive strength., Results: Operators mixed MTA samples with varying WP ratios. However, there was no significant difference between the microhardness and compressive strength values of MTA samples between the improvised, the pre-weighed and the control groups. MTA was mixed in a thicker consistency than the manufacturers recommended ratio (0.33) by 62.5% of the operators., Conclusion: According to the results of this study, even though the WP ratios that were utilized in the clinical setting vary, microhardness and compressive strength values of MTA was not significantly affected., Competing Interests: None

Objective: The objective of this study was to analyze the microstructure and crystalline structures of ProRoot MTA, Biodentine, CEM Cement, and Retro MTA when exposed to phosphate-buffered saline, butyric acid, and blood., Methods and Materials: Mixed samples of ProRoot MTA, Biodentine, CEM Cement, and Retro MTA were exposed to either phosphate-buffered saline, butyric acid, or blood. Scanning electron microscope (SEM) and energy-dispersive X-ray spectroscopic (EDX) evaluations were conducted of specimens. X-ray diffraction (XRD) analysis was also performed for both hydrated and powder forms of evaluated calcium silicate cements., Results: The peak of tricalcium silicate and dicalcium silicate detected in all hydrated cements was smaller than that seen in their unhydrated powders. The peak of calcium hydroxide (Ca(OH) 2 ) in blood- and acid-exposed ProRoot MTA, CEM Cement, and Retro MTA specimens were smaller than that of specimens exposed to PBS. The peak of Ca(OH) 2 seen in Biodentine™ specimens exposed to blood was similar to that of PBS-exposed specimens. On the other hand, those exposed to acid exhibited smaller peaks of Ca(OH) 2 ., Conclusion: Exposure to blood or acidic pH decreased Ca(OH) 2 crystalline formation in ProRoot MTA, CEM Cement and Retro MTA. However, a decrease in Ca(OH) 2 was only seen when Biodentine™ exposed to acid., Clinical Relevance: The formation of Ca(OH) 2 which influences the biological properties of calcium silicate cements was impaired by blood and acid exposures in ProRoot MTA, CEM Cement, and Retro MTA; however, in the case of Biodentine, only exposure to acid had this detrimental effect.

The aim of this study was to investigate the effect of human blood exposure on the compressive strength of various calcium silicate-based cements. Two hundred and eighty-eight customised cylindrical moulds were randomly divided into three groups according to material used: ProRoot MTA, Biodentine or CEM cement (n = 96). Each group was divided into two subgroups according to exposure conditions: PBS or blood. Then, the compressive strength of the specimens was measured after 6 h, 24 h, 72 h and 7 days. The compressive strength of CEM cement could not be measured after 6 and 24‏ h regardless of the exposure conditions nor could the compressive strength of 6 h blood-exposed ProRoot MTA. The compressive strength of blood-exposed ProRoot MTA was only significantly lower after 6 h, but no difference was seen at other time intervals. Blood exposed did adversely affected the compressive strength of Biodentine. The compressive strength of all groups significantly increased over time (P < 0.005)., (© 2017 Australian Society of Endodontology Inc.)

Introduction: A lack of information exists regarding the efficacy of RetroMTA (BioMTA, Seoul, Korea) directly applied on the pulp in vital pulp therapy. This study was designed to examine the clinical efficacy of RetroMTA compared with ProRoot mineral trioxide aggregate (MTA) (Dentsply Tulsa Dental, Tulsa, OK) for partial pulpotomy., Methods: Partial pulpotomy was performed in 22 healthy human maxillary and mandibular third molars planned for extraction. The teeth were randomly divided into 2 groups (n = 11) and underwent partial pulpotomy with RetroMTA and ProRoot MTA as the control. The teeth were then restored with glass ionomer cement. Clinical and electric pulp tests were performed after 1 and 8 weeks. The teeth were radiographed and extracted at 8 weeks. Histologic sections were prepared and analyzed for pulp inflammation and dentinal bridge formation. Data were analyzed using the Mann-Whitney U test., Results: Clinical examination after 1 and 8 weeks showed no sensitivity to heat, cold, or palpation in the ProRoot MTA and RetroMTA groups. Periapical radiographs taken before the extraction of teeth showed no evidence of periapical pathology. Electric pulp testing revealed no sensitivity. Data comparisons using the Mann-Whitney U test showed no significant difference between the materials with regard to the pulp inflammation type, intensity and extension (P = .3), or bridge continuity (P = .12). However, these data revealed a significant difference between the 2 materials in pulp morphology (P < .05) and bridge thickness (P < .01)., Conclusions: This is the first work to evaluate a RetroMTA histologic outcome in partial pulpotomy in human permanent teeth. It shows pulp disorganization, an absence of inflammation, and discontinuous mineralization, which may represent a potential drawback with RetroMTA in this indication., (Copyright © 2018 American Association of Endodontists. Published by Elsevier Inc. All rights reserved.)

Objectives: Dentine replacement materials are often placed over caries affected dentine (CAD). The aim of this study was to compare the bonding characteristics and interactions of selected hydraulic calcium silicate-based dentine replacement materials to CAD and sound dentine., Methods: Three hydraulic calcium silicate-based dentine replacement materials were assessed: Retro MTA, Biodentine and Theracal LC. Material characterization was done by scanning electron microscopy and X-ray diffraction analyses. Blocks of sound and CAD were prepared and standardized by Vickers microhardness testing. Half of the affected and sound dentine blocks were pretreated with 5.25% NaOCl prior to material placement. The materials were stored either for 1 week or 24 weeks in 37°C in fully saturated conditions. Shear bond strength was assessed at both time periods. Radiopacity of the interfacial dentine was also evaluated to assess the remineralization potential of the dentine replacement materials., Results: The reaction of Theracal was slower than that of the water-based materials. The bond strengths of different materials did not differ after 1 week (P>0.05). The bond strength of Biodentine and Retro MTA increased over time but no change was observed for Theracal. NaOCl pre-treatment deteriorated the bond strength to sound dentine but improvement was observed in affected dentine. Radiopacity changes were observed after 24 weeks., Significance: Biodentine and Retro MTA showed better bonding to CAD. Pretreatment with NaOCl improved the bond strength of dentine replacement materials to CAD., (Copyright © 2018 The Academy of Dental Materials. Published by Elsevier Inc. All rights reserved.)

Objectives: The aim of this study was to evaluate the effect of various mixing techniques as well as the effect of ultrasonic placement on hydration of mineral trioxide aggregate (MTA) using X-ray diffraction (XRD) analysis., Materials and Methods: One gram of ProRoot MTA and MTA Angelus powder was mixed with a 0.34-g of distilled water. Specimens were mixed either by mechanical mixing of capsules for 30 s at 4500 rpm or by manual mixing followed by application of a compaction pressure of 3.22 MPa for 1 min. The mixtures were transferred into the XRD sample holder with minimum pressure. Indirect ultrasonic activation was applied to half of the specimens. All specimens were incubated at 37 °C and 100% humidity for 4 days. Samples were analyzed by XRD. Phase identification was accomplished by use of search-match software utilizing International Centre for Diffraction Data (ICDD)., Results: All specimens comprised tricalcium silicate, calcium carbonate, and bismuth oxide. A calcium hydroxide phase was formed in all ProRoot specimens whereas among MTA Angelus groups, it was found only in the sample mixed mechanically and placed by ultrasonication., Conclusions: Mechanical mixing followed by ultrasonication did not confer a significant disadvantage in terms of hydration characteristics of MTA., Clinical Relevance: Clinicians vary in the way they mix and place MTA. These variations might affect their physical characteristics and clinical performance. For ProRoot MTA, the mixing and placement methods did not affect its rheological properties, whereas for MTA Angelus, mechanical mixing combined with ultrasonic placement enhanced the calcium hydroxide phase formation.

Introduction: Questions exist regarding the efficacy of resin-containing materials such as TheraCal directly applied on the pulp. This study sought to investigate the clinical efficacy of TheraCal as compared with Biodentine and ProRoot mineral trioxide aggregate (MTA) for partial pulpotomy., Methods: In this clinical trial, partial pulpotomy was performed for 27 sound human maxillary and mandibular third molars scheduled for extraction. The teeth were randomly divided into 3 groups (n = 9) and underwent partial pulpotomy with TheraCal, Biodentine, and ProRoot MTA. The teeth were then restored with glass ionomer cement. Clinical and electric pulp tests were performed after 1 and 8 weeks. The teeth were radiographed and extracted at 8 weeks. Histologic sections were prepared and analyzed for pulp inflammation and dentinal bridge formation. Data were analyzed by using one-way analysis of variance., Results: Clinical examination showed no sensitivity to heat, cold, or palpation in ProRoot MTA and Biodentine groups. Two patients in TheraCal group (20%) reported significant pain at 1 week. Periapical radiographs showed no periapical pathology, and electric pulp test revealed a normal pulp response with no hypersensitivity. Inflammation was absent with all materials at 8 weeks. Normal pulp organization was seen in 33.33% of the teeth in ProRoot MTA, 11.11% in TheraCal, and 66.67% in Biodentine group (P = .06). Biodentine group showed complete dentinal bridge formation in all teeth, whereas this rate was 11% and 56% in TheraCal and ProRoot MTA groups, respectively (P = .001)., Conclusions: Overall, Biodentine and MTA performed better than TheraCal when used as partial pulpotomy agent and presented the best clinical outcomes., (Copyright © 2017 American Association of Endodontists. Published by Elsevier Inc. All rights reserved.)

Objectives: The aim of this study is to compare the effect of treated dentine matrix (TDM) and tricalcium phosphate (TCP) scaffolds on odontogenic differentiation and mineralization of dental pulp stem cells (DPSCs) in furcation perforations created in the pulp chamber floor of premolar teeth in dogs., Material and Methods: DPSCs were isolated and cultured from the dental pulp of the maxillary left second and third premolars of dogs. The DPSCs were loaded on TCP (SC+TCP) and TDM (SC+TDM) scaffolds and inserted into intentionally perforated pulp chamber floors of premolars in dogs; six teeth were used for each group. Three more groups of six specimens were created, and mineral trioxide aggregate (MTA), TDM, and TCP were inserted into the perforations to act as controls. An intact premolar and no treatment in the perforation site were used as positive and negative controls respectively. After 3 months, the animals were sacrificed and the type of inflammation, presence of dentine, continuation and type of cementum, type of connective tissue, and presence of foreign body reaction were evaluated, and significant differences were between groups determined using the Fisher's exact test. The evaluation of the amount of inflammation and the percentage of new bone formation was evaluated using the Mann-Whitney U test., Results: The negative control group was associated with severe inflammation and granulation tissue formation. In the positive control group, intact periodontal tissues and no inflammation were observed. Dentine bridge formation was not seen in specimens of any group. The specimens in the SC+TDM group were associated with significantly more bone formation than other groups (P < 0.001). The amount of inflammation was less than 10 % in specimens of all groups with the exception of three specimens in the TCP group that were categorized as 10-30 %. Chronic inflammation without foreign body reactions was the major pattern of inflammation in groups. Formation of cementum with a cellular and continuous appearance was seen in all specimens., Conclusions: SC+TDM was associated with significantly more bone formation when used to repair uninfected furcation perforations in the premolar teeth of dogs., Clinical Relevance: Application of TDM as a biological scaffold in combination with DPSCs may offer an advantage during the repair of root perforation defects.

Introduction: Biodentine (Septodont, Saint Maur des Fossés, France), OrthoMTA (BioMTA, Seoul, Korea), and EndoSequence Root Repair Material (ERRM; Brasseler, Savannah, GA) have been developed to overcome the shortcomings of mineral trioxide aggregate (MTA). The purpose of this study was to compare tooth discoloration after the application of ProRoot MTA (Dentsply Tulsa Dental Products, Tulsa, OK) and 3 recently introduced calcium silicate-based cements in the presence and absence of blood., Methods: In total, 104 human anterior teeth were prepared; 96 were randomly divided into 2 groups (blood and saline contamination). Each group was subdivided into 4 experimental subgroups (n = 12) of ProRoot MTA, Biodentine, OrthoMTA, and ERRM that were used to fill the pulp chambers. The remaining 8 teeth served as the saline and blood groups. Color analysis of tooth crowns was performed using a spectroradiometer before the application of materials and at 24 hours, 1 month, and 6 months after application. Repeated measures analysis of variance was used to evaluate the effects of blood, material, and time on color change (ΔE*)., Results: Tooth color change in all experimental groups increased over time (P < .05). Blood contamination significantly increased ΔE* (P < .05), but no significant difference occurred between the 4 groups in this respect in the presence of blood. However, in the absence of blood, the ΔE* of Biodentine and ERRM was significantly less than that of OrthoMTA (P < .05)., Conclusions: There was no significant difference between tooth discolorations with materials in the presence of blood. However, in the absence of blood, Biodentine and ERRM exhibited less tooth discoloration than OrthoMTA., (Copyright © 2016 American Association of Endodontists. Published by Elsevier Inc. All rights reserved.)

Introduction: The purpose of this study was to compare the compressive strength of mineral trioxide aggregate (MTA) when mixed with 2 different water-to-powder (WP) proportions using either hand or ultrasonic placement., Methods: Tooth-colored ProRoot MTA (Dentsply Maillefer, Ballaigues, Switzerland) and white MTA Angelus (Angelus Soluçoes Odontologicas, Londrina, Brazil) were investigated. One gram of each MTA powder was mixed with either 0.34 or 0.40 g distilled water. The 4 groups were further divided into 2 groups of 5 specimens for each of the following techniques: conventional (ie, hand placement) and placement using indirect ultrasonic activation for 30 seconds. All specimens were subjected to compressive strength testing after 4 days. The results were statistically analyzed with multivariate analysis of variance and Tukey Honestly Significant Difference tests at a significance level of P < .05., Results: The mean compressive strength values of ProRoot MTA (84.17 ± 22.68) were significantly greater than those of MTA Angelus (47.71 ± 14.29) (P < .01). Specimens mixed with the 0.34 WP ratio had higher compressive strength values (72.85 ± 25.77) than those mixed with the 0.40 WP ratio (56.69 ± 24.85) (P < .05). The highest compressive strength values were recorded for ProRoot MTA specimens that were mixed in the 0.34 WP ratio, and then the samples were placed with ultrasonic activation (mean = 91.35 MPa). The lowest values were recorded for MTA Angelus samples that were mixed in the 0.40 WP ratio, and the specimens were placed without ultrasonic activation (mean = 36.36 MPa). Ultrasonic activation had no significant difference in terms of compressive strength., Conclusions: When using ProRoot MTA and MTA Angelus, higher WP ratios resulted in lower compressive strength values. Ultrasonication had no significant effect on the compressive strength of the material regardless of the WP ratio that was used. Therefore, adherence to the manufacturer's recommended WP ratio when preparing MTA for use in dental applications is advised., (Copyright © 2015 American Association of Endodontists. Published by Elsevier Inc. All rights reserved.)

Aim: To assess the effect of bismuth oxide (Bi2 O3 ) on the chemical characterization and physical properties of White mineral trioxide aggregate (MTA) Angelus., Methodology: Commercially available White MTA Angelus and White MTA Angelus without Bi2 O3 provided by the manufacturer especially for this study were subjected to the following tests: Rietveld X-ray diffraction analysis (XRD), energy-dispersive X-ray analysis (EDX), scanning electron microscopy (SEM), compressive strength, Vickers microhardness test and setting time. Chemical analysis data were reported descriptively, and physical properties were expressed as means and standard deviations. Data were analysed using Student's t-test and Mann-Whitney U test (P = 0.05)., Results: Calcium silicate peaks were reduced in the diffractograms of both hydrated materials. Bismuth particles were found on the surface of White MTA Angelus, and a greater amount of particles characterized as calcium hydroxide was observed by visual examination on White MTA without Bi2 O3 . The material without Bi2 O3 had the shortest final setting time (38.33 min, P = 0.002), the highest Vickers microhardness mean value (72.35 MPa, P = 0.000) and similar compressive strength results (P = 0.329) when compared with the commercially available White MTA Angelus containing Bi2 O3 ., Conclusion: The lack of Bi2 O3 was associated with an increase in Vickers microhardness, a reduction in final setting time, absence of Bi2 O3 peaks in diffractograms, as well as a large amount of calcium and a morphology characteristic of calcium hydroxide in EDX/SEM analysis., (© 2013 International Endodontic Journal. Published by John Wiley & Sons Ltd.)

Introduction: The aim of this study was to compare the surface microhardness of BioAggregate, ProRoot MTA, and CEM Cement when exposed to an acidic environment or phosphate-buffered saline (PBS) as a synthetic tissue fluid., Methods: Ninety cylindrical molds made of polymethyl methacrylate with an internal diameter of 6 mm and height of 4 mm (according to ASTM E384 standard for microhardness tests) were fabricated and filled with BioAggregate (n = 30), tooth-colored ProRoot MTA (n = 30), or CEM Cement (n = 30). Each group was then divided into 3 subgroups of 10 specimens consisting of those exposed to distilled water, exposed to PBS (pH = 7.4), or exposed to butyric acid (pH = 5.4). After 1 week the Vickers surface microhardness test was performed. Statistical analysis included 2-way analysis of variance, followed by post hoc Dunnett T3 in cases with lack of homoscedasticity and Tukey honestly significant difference in cases with homoscedasticity., Results: The indentations obtained from the CEM Cement specimens exposed to an acidic pH were not readable because of incomplete setting. There was a significant difference between the microhardness of the materials regardless of the environmental conditions (P < .001). In all the environmental conditions, MTA had significantly higher and CEM Cement had significantly lower microhardness values (P < .001). All experimental cements had significantly higher microhardness values when exposed to PBS (P < .001) and had significantly lower microhardness values when exposed to butyric acid (P < .001)., Conclusions: The surface microhardness of BioAggregate, ProRoot MTA, and CEM Cement was reduced significantly by exposure to butyric acid and increased significantly by exposure to PBS. In all environmental conditions, MTA had significantly higher microhardness values., (Copyright © 2014 American Association of Endodontists. All rights reserved.)

Introduction: The aim of this study was to evaluate the effect of mechanical and manual mixing as well as the effect of ultrasonic agitation during placement on the flexural strength and porosity of mineral trioxide aggregate (MTA)., Methods: White ProRoot MTA and white MTA Angelus were used. One gram of each powder was mixed with a 0.34-g aliquot of distilled water. Specimens were mixed either by mechanical mixing of capsules for 30 seconds at 4500 rpm or by a saturation technique and application of a condensation pressure of 3.22 MPa for 1 minute. The mixed slurries of all materials were loaded into 2 × 2 × 25 mm molds for testing flexural strength and 3 × 4 mm molds for evaluation of porosity. Half of the specimens were placed in the stainless steel molds by using indirect ultrasonic activation. All specimens were incubated for 4 days. Micro-computed tomography was used to determine the porosity of each specimen, and a 3-point bending test was used to evaluate flexural strength. Tukey honestly significant difference and independent t tests were carried out to compare the means at a significance level of P < .05., Results: Irrespective of mixing and placement techniques applied, the flexural strength values of ProRoot MTA were significantly greater than those of MTA Angelus (P < .05). A medium negative correlation was found between flexural strength values and total porosity percentage., Conclusions: Although mechanical mixing of encapsulated cements was quicker and provided more consistent mixes, this technique along with ultrasonic agitation was not associated with a significant advantage in terms of flexural strength and total porosity over manual mixing., (Copyright © 2014 American Association of Endodontists. All rights reserved.)

Introduction: The purpose of this study was to evaluate the effect of acid etching on the compressive strength of 4 calcium silicate-based cements., Methods: One gram of each corresponding powder of ProRoot MTA (Dentsply Tulsa Dental, Johnson City, TN), MTA Angelus (Angelus, Londrina, PR, Brazil), and CEM cement (BioniqueDent, Tehran, Iran) and a 0.33-g aliquot of liquid were placed in a plastic mixing capsule that was then mechanically mixed for 30 seconds at 4500 rpm in an amalgamator. For the preparation of Biodentine (Septodont, Saint Maur-des-Fossés, France), the liquid provided was added to the powder within the plastic capsule supplied by the manufacturer and then mechanically mixed for 30 seconds at 4500 rpm using the amalgamator. The resulting slurries were then placed incrementally into 40 cylindrical molds to give a total of 160 specimens that were incubated at 37°C for a week. Twenty specimens of each material were then subjected to the acid etch procedure. The compressive strength of the samples was then calculated in megapascals using a universal testing machine. The results were then subjected to 2-way analysis of variance analysis of variance followed by the Tukey post hoc test., Results: The application of acid etch significantly reduced (P < .0001) the compressive strength of Angelus MTA and CEM cement; however, it did not reduce the compressive strength of ProRoot MTA or Biodentine. Regardless of the acid etch application, Biodentine showed significantly higher compressive strength values than the other materials (P < .0001), whereas CEM cement had the lowest compressive strength values. There was no significant difference between CEM cement and MTA Angelus. The compressive strength of ProRoot MTA was significantly lower (P < .0001) than Biodentine but significantly higher (P < .0001) than MTA Angelus and CEM cement in both the test and control groups., Conclusions: When the application of acid etchants is required, Biodentine and ProRoot MTA seem to be better options than MTA Angelus or CEM cement., (Copyright © 2013 American Association of Endodontists. All rights reserved.)

Introduction: The aim of this study was to evaluate the effect of various mixing techniques including mechanical and manual mixing as well as the effect of ultrasonic agitation during placement on the compressive strength of mineral trioxide aggregate (MTA)., Methods: Tooth-colored ProRoot MTA (Dentsply Maillefer, Ballaigues, Switzerland) and white MTA Angelus (Angelus Soluções Odontologicas, Londrina, Brazil) were used. One gram of each powder was mixed with a 0.34-g aliquot of distilled water. Specimens were mixed either by mechanical mixing of capsules for 30 seconds at 4,500 rpm or by a saturation technique and the application of a condensation pressure of 3.22 MPa for 1 minute. Half of the specimens were placed in stainless steel molds and agitated using indirect ultrasonic activation. All specimens were subjected to compressive strength testing after 4 days., Results: The compressive strength values of ProRoot MTA were significantly greater than those of MTA Angelus (P < .05). The highest compressive strength values were recorded from ProRoot MTA samples that were mixed mechanically and placed using ultrasonic activation (mean = 101.71 MPa), whereas the lowest values were recorded for MTA Angelus samples that were mixed manually and placed without ultrasonic activation (mean = 53.47 MPa). Ultrasonically agitated groups had higher compressive strength values (P < .001). The specimens mixed mechanically had higher compressive strength values than those mixed manually (P < .05)., Conclusions: The compressive strength values of ProRoot MTA were significantly greater than those of MTA Angelus. Mechanical mixing enhanced the compressive strength of the material. Regardless of the mixing techniques applied, ultrasonic agitation improved the compressive strength of the material., (Copyright © 2013 American Association of Endodontists. Published by Elsevier Inc. All rights reserved.)

Aim: Mineral trioxide aggregate (MTA) is the material of choice for apical barrier techniques during root canal treatment of teeth with open apices. However, the precise control of MTA during the placement of an apical plug is challenging. This article describes the outcomes of unintentional extrusion of MTA into the periradicular tissue during apical barrier treatment in three cases., Summary: Three cases of maxillary central incisors in adult patients with open apices were referred for treatment. After conventional access and canal preparation, MTA was placed into the apical portion of the root canals to act as an apical barrier/plug. A large increment of MTA was extruded in all cases. In Case 1, after a 4-year follow-up, the extruded MTA had resorbed and the periradicular lesion had healed. In Cases 2 and 3, after follow-up, the patients remained symptomatic and were scheduled for periradicular surgery. In Case 2, soft unset particles of MTA were present in the lesion and were curetted. In Case 3, the extruded MTA had set hard but was sandwiched between the oral mucosa and bone; its removal relieved the pain experienced on buccal palpation., Key Learning Points: Extruded MTA may not harden and may be associated with ongoing periapical irritation; Extruded set MTA when encapsulated in the mucosa and not surrounded by bony matrix may act as a mechanical irritant on palpation; Mineral trioxide aggregate should be confined to the root canal system; Teeth where MTA has been extruded beyond the foramen should be followed-up to monitor the outcome., (© 2012 International Endodontic Journal.)

Aim: To test the hypothesis that blood contamination has a detrimental effect on the chemical properties of Mineral trioxide aggregate (MTA)., Methodology: The effects of whole, fresh human blood on the microstructure and elemental chemistry of MTA were evaluated using scanning electron microscopy and energy-dispersive X-ray analysis, respectively. The phase compositions of contaminated and uncontaminated MTA were also analysed using X-ray diffraction analysis., Results: The hydration state of specimens partially mixed with blood were more complete than those mixed entirely with blood and less than those entirely mixed with water. Acicular crystals, characteristic of ettringite, were abundant in specimens mixed entirely with water and absent from specimens mixed partially or entirely with blood. Calcium hydroxide crystals were absent in specimens contaminated entirely with blood and the unhydrated MTA powder, but present in the other groups., Conclusion: Mixing MTA with blood resulted in the lack of formation of the crystalline calcium hydroxide in the early stage of the hydration process., (© 2011 International Endodontic Journal.)

Aim: Short-term and long-term evaluation of the effect of whole human blood or serum contamination on the surface microhardness value and microstructure of white and grey mineral trioxide aggregate (MTA)., Methodology: Three groups of 10 samples for each type of MTA were prepared. The first group was mixed with and exposed to fresh whole human blood. The second and third groups were mixed with distilled water and exposed to fresh whole human blood or human serum, respectively. The control group samples were mixed with and exposed to distilled water. During preparation, 1 g of MTA was triturated with 0.33 g of the selected liquid using an amalgamator and placed inside borosilicate cylindrical moulds. The samples were treated with ultrasonic energy. Vickers surface microhardness values were compared after 4 and 180 days. Scanning electron microscopy (SEM) analysis was performed after 4 days., Results: White MTA had a greater microhardness value than grey MTA in all groups. There was a significant difference between the control and the experimental groups (P < 0.00001). There was no significant difference between the microhardness values obtained after 4 and 180 days, apart from grey MTA mixed with blood or exposed to serum (P < 0.00001). SEM analysis showed the contaminated samples were devoid of acicular crystals that were prominent in the control groups., Conclusion: Blood contamination had a detrimental effect on the surface microhardness of MTA in the short and long term. If blood or serum contamination is unavoidable under clinical conditions, it might be preferable to use white MTA., (© 2010 International Endodontic Journal.)

Aim: To investigate the effects of whole, fresh human blood contamination on compressive strength and surface microstructure of grey and tooth-coloured mineral trioxide aggregate (MTA)., Methodology: The materials investigated were grey ProRoot MTA Original (Dentsply Tulsa Dental, Johnson City, TN, USA) and tooth-coloured ProRoot MTA (Dentsply Tulsa Dental). Three groups of 10 custom-made cylindrical moulds (internal dimensions 6 +/- 0.1 mm length and 4 +/- 0.1 mm diameter) were filled with tooth-coloured MTA. In the control group, MTA was mixed with water and exposed to water. In the second group, MTA was mixed with water and exposed to whole, fresh human blood. In the third group, MTA was mixed with and exposed to whole, fresh human blood. These three groups were then duplicated using grey MTA, creating a total of 60 samples. A predetermined amount of MTA and appropriate liquid were triturated in a plastic mixing capsule then subjected to ultrasonic energy after placement in the moulds. After 4 days of incubation, specimens were subjected to compressive strength testing. The surface microstructure of one extra specimen in each group was examined using scanning electron microscopy. Data were subjected to a two-way anova., Results: Regardless of MTA type, the mean compressive strength values of both experimental groups, which were in contact with blood, were significantly less than that of the control groups (P < 0.0001). In experimental groups in which MTA was mixed with water and exposed to blood, there was a significant difference (P < 0.0001) in compressive strength between tooth-coloured MTA (30.37 +/- 10.16 MPa) and grey MTA (13.92 +/- 3.80 MPa)., Conclusion: When blood becomes incorporated into MTA, its compressive strength is reduced. In clinical situations in which blood becomes mixed with MTA, its physical properties are likely to be compromised.

Introduction: Reduced surface microhardness and decreased sealing ability have been shown after the placement of mineral trioxide aggregate (MTA) in an acidic environment. In this study, the effect of an acidic environment on the push-out strength of MTA was evaluated., Methods: Eighty root dentin slices from freshly extracted single-rooted human teeth were sectioned and their lumen instrumented to achieve a diameter of 1.3 mm. One gram of tooth-colored ProRoot MTA (Dentsply Tulsa Dental, Johnson City, TN) was mixed with 0.33 g of distilled water and introduced into the canals of the root-dentin slices and treated with ultrasonic energy. The specimens were then randomly divided into four groups (n = 20) and wrapped in pieces of gauze soaked in phosphate buffer saline solution (pH = 7.4) and butyric acid buffered at pH values of 4.4, 5.4, or 6.4, respectively. They were then incubated for 4 days at 37 degrees C. The push-out bond strengths were then measured using a universal testing machine. The slices were examined under a light microscope at x40 magnification to determine the nature of the bond failure. The data were analyzed using one-way analysis of variance and the Tamhane post hoc test., Results: The greatest mean push-out bond strength (7.28 +/- 2.28 MPa) was observed after exposure to a pH value of 7.4. The values decreased to 2.47 +/- 0.61 MPa after exposure to a pH value of 4.4. There were significant differences between the groups (p < 0.001). Inspection of the samples revealed the bond failure to be predominantly adhesive., Conclusion: The force needed for displacement of MTA was significantly lower in samples stored at lower pH values., (Copyright (c) 2010 American Association of Endodontists. All rights reserved.)

Aim: To evaluate the influence of various mixing procedures including ultrasonic vibration, trituration of customized encapsulated mineral trioxide aggregate (MTA) and condensation on the Vickers surface microhardness of MTA., Methodology: ProRoot MTA Original, ProRoot MTA (white), MTA-Angelus (grey) and MTA White Angelus (white) were prepared using several mixing techniques including ultrasonic vibration, trituration of customized encapsulated MTA and conventional condensation. Twelve experimental groups (four materials: three techniques) were evaluated, each with 35 samples. All samples were incubated after preparation and subjected to Vickers surface microhardness testing after 4 and 28 days. Data was were subjected to a two-way anova., Result: At 28 days, the surface microhardness value was significantly greater for all experimental groups compared to 4 days after mixing (P < 0.00001). The application of ultrasonic energy to MTA produced significantly higher surface microhardness values compared to the other mixing techniques at both 4 and 28 days (P < 0.0001). However, no significant difference existed between condensation and trituration techniques at both time intervals. Regardless of the mixing technique employed, a significant difference (P < 0.0001) was observed in surface microhardness value between all types of MTA apart from between Angelus grey and ProRoot white at both 4 and 28 days, both of which produced the highest values., Conclusion: Compared to trituration and condensation techniques, the application of ultrasonic energy to MTA produced a significantly higher surface microhardness value at both 4 and 28 days. Irrespective of mixing technique, ProRoot white and Angelus grey had the highest surface microhardness values. Trituration of encapsulated, premeasured MTA and water provides a standardiszed method of mixing that produces MTA slurries with more controllable handling characteristics.

Aim: To evaluate the effect of acid-etch procedures on the compressive strength and surface microhardness of tooth-coloured mineral trioxide aggregate (MTA)., Methodology: White ProRoot MTA (Dentsply Tulsa Dental) was mixed and packed into cylindrical tubes of 4 mm in diameter and 6 mm in height. Three groups, each of 15 specimens were subjected to an acid-etch procedure either 4, 24 or 96 h after mixing. The compressive strength was measured and compared with unetched control groups. Differences between groups were analysed using the Kruskall-Wallis test. A further batch of cylindrical specimens of 6 mm in diameter and 12 mm in height were prepared for testing surface microhardness. Three groups of 15 specimens were subjected to the acid-etch procedure at either 4, 24 or 96 h following mixing. Data were subjected to one-way anova. Changes in the surface microstructure before and after the acid-etch procedures were analysed using a scanning electron microscope (SEM)., Results: There was a general trend for the compressive strength and surface microhardness of specimens to increase with time. In terms of compressive strength, the increase was significant between 4 h and the other time periods for both experimental and control groups (P < 0.0001); however, there was no significant difference between 24 and 96 h. The increase in surface microhardness was significant between 4, 24 and 96 h (P < 0.0001). In addition, there was a significant difference between experimental and control groups at all time periods (P < 0.0001). SEM examination revealed morphological differences between the intact and the etched MTA surfaces., Conclusions: Acid-etch procedures affected the compressive strength and surface microhardness of ProRoot MTA. This indicates that it may be better to postpone restorative procedures for at least 96 h after mixing MTA. Etching created surface changes that might have the potential to enhance bonding of resinous materials.

Aim: To evaluate the surface microhardness of mineral trioxide aggregate (MTA) specimens following exposure of their surface to a range of acidic environments during hydration. In addition, the morphological microstructure features of samples were studied by scanning electron microscopy (SEM)., Methodology: White ProRoot MTA (Dentsply Tulsa Dental, Johnson City, TN, USA) was mixed and packed into cylindrical polycarbonate tubes. Four groups, each of 10 specimens, were formed using a pressure of 3.22 MPa and exposed to pH 4.4, 5.4, 6.4 and 7.4, respectively, for 4 days. Vickers microhardness of the surface of each specimen was measured after exposure. Four groups of two specimens were prepared and treated in the same way prior to qualitative examination by SEM. Data were subjected to one-way anova and post hoc Tukey's test., Result: The greatest mean surface hardness values (53.19 +/- 4.124) were observed following exposure to pH 7.4 with the values decreasing to 14.34 +/- 6.477 following exposure to pH 4.4. The difference between these values at the 95% CI (33.39-44.30) was statistically significant (P < 0.0001). There were no distinct morphological differences between groups in terms of the internal microstructure. However, a trend was observed that the more acidic the solution, the more extensive the porosity of the specimens., Conclusion: Under the conditions of this study, surface hardness of MTA was impaired in an acidic environment.

Aim: To examine the effect of condensation pressure on surface hardness, microstructure and compressive strength of mineral trioxide aggregate (MTA)., Methodology: White ProRoot MTA (Dentsply Tulsa Dental, Johnson City, TN, USA) was mixed and packed into cylindrical polycarbonate tubes. Six groups each of 10 specimens were subjected to pressures of 0.06, 0.44, 1.68, 3.22, 4.46 and 8.88 MPa respectively. The surface hardness of each specimen was measured using Vickers microhardness. Cylindrical specimens of 4 mm in diameter and 6 mm in height were prepared in polycarbonate cylindrical moulds for testing the compressive strength. Five groups of 10 specimens were prepared using pressures of 0.06, 0.44, 1.68, 3.22 or 4.46 MPa. Data were subjected to one-way anova. The microstructure was analysed using a scanning electron microscope (SEM) after sectioning specimens with a scalpel., Result: A trend was observed for higher condensation pressures to produce lower surface hardness values. A condensation pressure of 8.88 MPa produced specimens with significantly lower values in terms of surface hardness than other groups (P<0.001). A condensation pressure of 1.68 MPa conferred the maximum compressive strength; however, it was not statistically different. Higher condensation pressures resulted in fewer voids and microchannels when analysed with SEM. In specimens prepared with lower condensation pressures distinctive crystalline structures were observed. They tended to appear around microchannels., Conclusion: Condensation pressure may affect the strength and hardness of MTA. Use of controlled condensation pressure in sample preparation for future studies is suggested.