Search

Correction for ‘Infrared nonlinear optical properties of lithium-containing diamond-like semiconductors Li2ZnGeSe4 and Li2ZnSnSe4’ by Jian-Han Zhang et al., Dalton Trans., 2015, 44, 11212–11222. [ABSTRACT FROM AUTHOR]

Two new lithium-containing diamond-like semiconductors, Li2ZnGeSe4 and Li2ZnSnSe4, have been prepared by high-temperature, solid-state synthesis. Single crystal X-ray diffraction reveals that both compounds adopt the wurtz–kesterite structure type, crystallizing in the noncentrosymmetric space group Pn. X-ray powder diffraction coupled with Rietveld refinement indicates the high degree of phase purity in which the materials are prepared. Both compounds display optical bandgaps around 1.8 eV, wide optical transparency windows from 0.7 to 25 μm and type-I phase matched second harmonic generation starting at 2500 nm and persisting deeper into the infrared. Using the Kurtz powder method, the second-order nonlinear optical coefficient, χ(2), was estimated to be 19 and 23 pm V−1 for Li2ZnGeSe4 and Li2ZnSnSe4, respectively. Using a 1064 nm incident laser beam with a pulse width (τ) of 30 ps both compounds exhibit a laser damage threshold of 0.3 GW cm−2, which is higher than that of the AgGaSe2 reference material measured under identical conditions. Differential thermal analysis shows that the title compounds are stable up to 684 and 736 °C, respectively. These properties collectively demonstrate that Li2ZnGeSe4 and Li2ZnSnSe4 have great potential for applications in tunable laser systems, especially in the infrared and even up to the terahertz regime. Electronic structure calculations using a plane-wave pseudopotential method within density functional theory provide insight regarding the nature of the bandgap and bonding. [ABSTRACT FROM AUTHOR]

High-temperature, solid-state synthesis in the Li 2 MnSnS 4 system led to the discovery of two new polymorphic compounds that were analyzed using single crystal X-ray diffraction. The α-polymorph crystallizes in Pna 2 1 with the lithium cobalt (II) silicate, Li 2 CoSiO 4 , structure type, where Z =4, R 1=0.0349 and wR 2=0.0514 for all data. The β - polymorph possesses the wurtz-kesterite structure type, crystallizing in Pn with Z =2, R 1=0.0423, and wR 2=0.0901 for all data. Rietveld refinement of synchrotron X-ray powder diffraction was utilized to quantify the phase fractions of the polymorphs in the reaction products. The α/β-Li 2 MnSnS 4 mixture exhibits an absorption edge of ∼2.6–3.0 eV, a wide region of optical transparency in the mid- to far-IR, and moderate SHG activity over the fundamental range of 1.1–2.1 μm. Calculations using density functional theory indicate that the ground state energies and electronic structures for α- and β - Li 2 MnSnS 4 , as well as the hypothetical polymorph, γ-Li 2 MnSnS 4 with the wurtz-stannite structure type, are highly similar. [ABSTRACT FROM AUTHOR]

• Cu 4 ZnGe 2 Se 7 is a new diamond-like semiconductor with the Cu 4 NiSi 2 S 7 structure type. • CZGSe and Cu 4 ZnGe 2 Se 7 possess optical bandgaps of 1.38 and 0.91 eV, respectively. • CZGSe and Cu 4 ZnGe 2 Se 7 are air stable and have wide windows of optical transparency. • CZGSe exhibits a strong second harmonic generation response at λ = 2900 nm. • CZGSe is an excellent candidate for low-powered infrared nonlinear optical devices. [Display omitted] In this study, two quaternary diamond-like semiconductors (DLSs) in the Cu-Zn-Ge-Se system, the known Cu 2 ZnGeSe 4 (also referred to as CZGSe) and the new Cu 4 ZnGe 2 Se 7 , are compared in terms of their crystal structures, electronic structures and physicochemical properties. Both compounds were prepared by high-temperature, solid-state synthesis at 800 °C. Single crystal X-ray diffraction was used to determine the structure of Cu 4 ZnGe 2 Se 7. The structures of both Cu 2 ZnGeSe 4 and Cu 4 ZnGe 2 Se 7 can be considered as derivatives of cubic diamond. Cu 4 ZnGe 2 Se 7 , with a reduced symmetry due to the cation ordering pattern, adopts the Cu 4 NiSi 2 S 7 structure type, with space group C 2. The corner-sharing tetrahedra in Cu 4 ZnGe 2 Se 7 are slightly distorted because the charge for some of the S2- anions is not compensated by the first-nearest-neighbor cations. Rietveld refinements using synchrotron X-ray powder diffraction data were used to assess the phase purity of the samples and confirm the bulk structural behavior. Diffuse reflectance UV/Vis/NIR spectroscopy shows that Cu 2 ZnGeSe 4 and Cu 4 ZnGe 2 Se 7 have direct optical bandgaps of 1.38 and 0.91 eV, respectively. Electronic structure calculations implementing density functional theory confirm the direct bandgap for Cu 4 ZnGe 2 Se 7 , with a calculated value of 0.62 eV. Both compounds are air stable, thermally stable up to relatively high temperatures, undergo phase transitions and have wide windows of optical clarity. The Kurtz-Perry powder technique was used to determine the second harmonic generation (SHG) responses using a commercial AgGaSe 2 standard. While Cu 4 ZnGe 2 Se 7 displays a weak SHG response, Cu 2 ZnGeSe 4 exhibits a response that is greater than several benchmark materials, with a large SHG coefficient, χ (2) , of 43 ± 6 pm/V at λ = 2900 nm. [ABSTRACT FROM AUTHOR]