Search

In this study, microstructural features direct metal laser melted (DMLM) aluminium–silicon-magnesium (AlSi10Mg) are investigated using advanced transmission electron microscopy (TEM) and high-resolution TEM (HRTEM). The focus is on post-processing by ECAP (Equal Channel Angular Pressing) and its effects on grain refinement, stacking fault formation and dislocation accumulation. In addition, the strength enhancing role of stacking faults is for the first time quantified. The results show that ECAP can increase the yield strength from 294 to 396 MPa, while the elongation increases from 2.4% to 6%. These results show that ECAP processing offers a new approach for producing AlSi10Mg products with improved strength and ductility. [ABSTRACT FROM AUTHOR]

In this work, we used an AlSi10Mg alloy produced by selective laser melting (SLM) to study the effects of build direction and deformation temperature on the grain refinement process. Two different build orientations of 0° and 90° and deformation temperatures of 150 °C and 200 °C were selected to study this effect. Light microscopy, electron backscatter diffraction and transmission electron microscopy were used to investigate the microtexture and microstructural evolution of the laser powder bed fusion (LPBF) billets. Grain boundary maps showed that the proportion of low-angle grain boundaries (LAGBs) dominated in every analysed sample. It was also found that different thermal histories caused by the change in build direction resulted in microstructures with different grain sizes. In addition, EBSD maps revealed heterogeneous microstructures comprising equiaxed fine-grained zones with ≈0.6 μm grain size and coarse-grained zones with ≈10 μm grain size. From the detailed microstructural observations, it was found that the formation of a heterogeneous microstructure is closely related to the increased fraction of melt pool borders. The results presented in this article confirm that the build direction has a significant influence on the microstructure evolution during the ECAP process. [ABSTRACT FROM AUTHOR]

In the selective laser melting process (SLM), the region irradiated by the laser beam is melted and quickly solidified, forming solidification lines (laser scan tracks) with symmetrical shapes. Because of the unique (rapid) crystallization conditions, the subgrain structures, typically observed inside these solidification lines, could also have variable geometric symmetrical patterns, e.g., cellular, pentagonal, or hexagonal cellular. The existence of such distinctive microstructures in SLM-made alloys has a significant impact on their superior mechanical and corrosion properties. Thus, any modification of this symmetrical microstructure (due to post-processing) can degrade or improve the properties of SLM-fabricated alloys. This study presents the experimental results on the effects of heat treatment and ECAP on microstructure modification and corrosion behavior of SLM-fabricated AlSi10Mg alloy. Light microscopy, scanning electron microscopy (SEM), electron backscattered diffraction (EBSD), and X-ray diffraction (XRD) were used for microstructural analysis. The corrosion properties of the given samples were determined using open-circuit potential (OCP), potentiodynamic polarization, and electrochemical impedance spectroscopy (EIS) techniques. EBSD observations showed that the imposed strain resulted in an obvious reduction in grain size to ~1.42 µm and ~0.24 µm after the first and second ECAP passes, respectively. Electrochemical tests revealed that the corrosion resistance of the ECAP-processed AlSi10Mg alloy improved significantly, which was confirmed by a nobler Ecorr and lower Icorr values, and higher polarization resistance. The final results indicated that the strain-induced crystalline defects provided more nucleation sites for the formation of a denser and thicker oxide film, thus enhancing the corrosion resistance of the AlSi10Mg alloy. [ABSTRACT FROM AUTHOR]