Search

In this work, a series of BaSrGd4O8:xBi3+ blue phosphors was synthesized employing the high-temperature solid-state method. Phase purity of the samples was verified by X-ray diffraction and Rietveld refinement. Time-resolved photoluminescence spectra revealed the existence of two distinct Bi sites. Subsequent optimization of dopant types and doping levels in the batch led to an almost twofold increase in quantum efficiency. The introduction of Eu3+ into the phosphors facilitated the construction of an energy transfer pathway. As the concentration of Eu3+ was increased, the emission color changed from blue to purple and finally to red. In addition, the thermal stability and potential applications of the phosphors were extensively investigated. Finally, two WLED devices were successfully fabricated with color rendering indices of 96.27 and 92.18, and correlated color temperatures of 5198 and 2475 K. This underscores the prospective application of these phosphors in the field of high-quality warm WLEDs. [ABSTRACT FROM AUTHOR]

A series of LaCaGaO4:xBi3+,yEu3+ (x = 0.002–0.04, y = 0.02–0.45) phosphors with adjustable emission colors were synthesized by high‐temperature solid‐state reaction. The samples were identified as pure phases by X‐ray diffraction and Rietveld refinement, and the crystal structures were analyzed in detail. The LaCaGaO4:xBi3+ phosphor shows an intense blue emission under near‐ultraviolet excitation, originating from the 3P1 → 1S0 transition. The spectrum analysis reveals that the Bi3+ ions occupy two luminescence centers in the LaCaGaO4 host and that energy transfer can occur. A model of the energy transfer between the Bi3+ and Eu3+ ions was also created and studied in detail. As the Eu3+‐concentration increased, the emission color of the LaCaGaO4:0.005Bi3+,yEu3+ phosphor changed from blue to pink to red. In addition, the fluorescence lifetime, quantum yield, thermal stability, and other properties of the phosphors were characterized and analyzed. Finally, two white light‐emitting diode devices with Ra values of 96.6 and 95 and correlated color temperatures of 4578 and 3324 K were fabricated, indicating the potential of phosphors for warm white lighting applications. [ABSTRACT FROM AUTHOR]

Na2MgScF7 (NMSF) was experimentally obtained for the first time by combining hydrothermal and high-temperature solid-state reactions. X-ray powder diffraction (XRD) combined with Rietveld refinement confirms that NMSF is crystallized in the space group Imma with the cell parameters a = 10.40860(18), b = 7.32804(12) and c = 7.52879(11) Å, α = β = γ = 90° and V = 574.256(24) Å3. Through doping with Tb3+ or Eu3+ ions, downshifting yellow-green or red emission could be achieved in NMSF-based phosphors, respectively. Upconversion emission could also be designed by doping with Yb3+–Er3+, Yb3+–Tm3+, Yb3+–Ho3+ or Er3+. Moreover, the NMSF:Er3+ phosphor exhibited green upconversion emission upon excitation at 980 nm, and it exhibited red emission upon excitation at 1532 nm. Finally, recognizable patterns were obtained under excitation at 254, 365 and 980 nm, indicating that the as-prepared phosphors can be applied to multicolor anti-counterfeiting. Moreover, our synthesis strategy opens up new avenues for the synthesis of novel fluorides. [ABSTRACT FROM AUTHOR]