Search

Transistors and ICs built in several different captive and commercial facilities were exposed to moisture, irradiated, and annealed. The moisture exposures were performed using highly accelerated stress test (HAST) at 130degC and 85% relative humidity. Irradiation of n-channel transistors exposed to HAST followed by a long-term anneal resulted in some increase in interface-trap and oxide-trapped charge buildup. However, exposing p-channel transistors to HAST preirradiation resulted in extremely large and unexpected voltage shifts immediately following irradiation. They were observed for devices with either doped oxide or nitride final chip passivation. Because of this, nitride passivation may not be sufficient to prevent H2O from causing enhanced radiation-induced degradation over long time periods in some devices (e.g., commercial devices with nitride final chip passivation packaged in plastic packages). The smaller voltage shifts for the n-channel transistors may be related to the formation of phosphosilicate glass (PSG) overlying the sources and drains of the n-channel transistors impeding the diffusion of moisture to the gate oxides. It is shown that, the large radiation-induced voltage shifts for the p-channel transistors can lead to enhanced IC parametric degradation and functional failure at lower radiation levels. Large increases in radiation-induced field oxide leakage current were also observed for transistors exposed to HAST preirradiation. Transistors were also annealed (prior to irradiation) and irradiated in H2. Approximately the same level of radiation-induced degradation was observed for n- and p-channel transistors suggesting that the diffusion kinetics for H2 diffusion are considerably different than for H2O diffusion. These results raise the concern that exposure of devices to moisture or hydrogen can lead to long-term radiation-induced aging effects. [ABSTRACT FROM PUBLISHER]

Eliminating radiation-induced parasitic leakage paths in integrated circuits (ICs) is key to improving their total dose hardness. Semiconductor manufacturers can use a combination of design and/or process techniques to eliminate known radiation-induced parasitic leakage paths. However, unknown or critical radiation-induced parasitic leakage may still exist on fully processed ICs and it is extremely difficult (if not impossible) to identify these leakage paths based on radiation induced parametric degradation. We show that light emission microscopy can be used to identify the location of radiation-induced parasitic leakage paths in ICs. This is illustrated by using light emission microscopy to find radiation-induced parasitic leakage paths in partially-depleted silicon on insulator static random-access memories (SRAMs). Once leakage paths were identified, modifications were made to the SRAM design to improve the total dose radiation hardness of the SRAMs. Light emission microscopy should prove to be an important tool for the development of future radiation hardened technologies and devices. [ABSTRACT FROM AUTHOR]

Presents a study that compared single-event transient waveforms in bipolar linear circuits generated with an ion microbeam, laser light and circuit simulation. Background on several hardness assurance approaches; Analysis of the significance of pulsed laser in the development of accurate circuit models; Investigation of the circuit simulations in the study; Implications for radiation hardness assurance in bipolar linear circuits.