Search

The effects of 63 MeV proton and 60Co gamma irradiation on the operation of 4.3 μm cutoff nBn photodetectors are demonstrated separately, and both are shown to yield a total ionizing dose (TID) effect. The effect is shown here in an InAsSbBi nBn detector and has been observed in other bulk alloy nBn detectors, and is unusual as it is notably absent in superlattice nBn detectors. The non-antireflection coated detectors exhibit a pre-radiation quantum efficiency of 17% at 3.3 μm wavelength and a dark current density of 50 μA/cm2, or roughly 300× the Rule 07 expectation, at their ideal operating voltage of −0.4 V bias at 150 K. Step-wise proton irradiation and in situ measurement indicate that the dark current increases to about 400× Rule 07 at the highest proton dose level of 150 krad(Si) (9.10 × 1011 p+/cm2), while the quantum efficiency is degraded at a relatively faster rate than the majority of analogous detectors characterized by our lab. Both the photocurrent and dark current are also shown to exhibit a turn-on voltage magnitude reduction of 100 mV following either gamma or proton irradiation, a trend which is attributable to negative trapped charge at the barrier interface (TID effect). This theory is further supported by an observed capacitance density magnitude reduction with dose and affirmed with Silvaco TCAD simulations. Following both proton exposure and subsequent anneal and gamma exposure and subsequent anneal; dark current, photocurrent, and CV all approach their pre-radiation baseline values. [ABSTRACT FROM AUTHOR]

The effect of majority carrier concentration and minority carrier lifetime on the performance of mid-wave infrared ( λ cutoff = 5.5 μ m) nBn detectors with variably doped InGaAs/InAsSb type-II superlattice absorbers is investigated. The detector layer structures are grown by molecular beam epitaxy such that their absorbing layers are either undoped, uniformly doped with a target density of 4 × 1015 cm−3, or doped with a graded profile, and variable-area mesa detector arrays are fabricated. Each material's temperature-dependent minority carrier lifetime is determined by time-resolved photoluminescence, and majority carrier concentration is extracted from capacitance–voltage measurements. Detector performance is evaluated with dark current and photocurrent measurements, from which quantum efficiency and shot-noise-limited noise-equivalent irradiance are calculated. The two doped detectors have lower dark current densities compared to their undoped counterpart due to the reduction in diffusion current as well as suppression of depletion current. Although both intentionally doped devices exhibit lower minority carrier lifetimes relative to the undoped device, the device with graded doping maintains a comparable quantum efficiency to the undoped device. Ultimately, the graded doping structure exhibits the highest sensitivity with a shot noise-limited noise-equivalent irradiance of 6.3 × 1010 photons/cm2 s in low-background light conditions, within a factor of 4× of an infrared detector pixel with Rule 07 dark current density and unity quantum efficiency. A detailed analysis of the dark current, quantum efficiency, and minority carrier lifetime provides insight into the material and device design factors that must be considered to realize a device with optimal sensitivity. [ABSTRACT FROM AUTHOR]