The influence of the ultrafine crystallinity of commercial purity grade 2 (as-received) titanium and titanium modified by equal channel angular pressing (modified titanium) on bacterial attachment was studied. A topographic profile analysis of the surface of the modified titanium revealed a complex morphology of the surface. Its prominent micro- and nano-scale features were 100-200-nm-scale undulations with 10-15 microm spacing. The undulating surfaces were nano-smooth, with height variations not exceeding 5-10 nm. These surface topography characteristics were distinctly different from those of the as-received samples, where broad valleys (up to 40-60 microm) were detected, whose inner surfaces exhibited asperities approximately 100 nm in height spaced at 1-2 microm. It was found that each of the three bacteria strains used in this study as adsorbates, viz. Staphylococcus aureus CIP 68.5, Pseudomonas aeruginosa ATCC 9025 and Escherichia coli K12, responded differently to the two types of titanium surfaces. Extreme grain refinement by ECAP resulted in substantially increased numbers of cells attached to the surface compared to as-received titanium. This enhanced degree of attachment was accompanied with an increased level of extracellular polymeric substances (EPS) production by the bacteria.

Abstract: We discuss the effect of extreme grain refinement in the bulk of commercial purity titanium (CP, Grade-2) on bacterial attachment to the mechano-chemically polished surfaces of the material. The ultrafine crystallinity of the bulk was achieved by severe plastic deformation by means of equal channel angular pressing (ECAP). The chemical composition, wettability, surface topography and roughness of titanium surfaces were characterized using X-ray photoelectron spectroscopy (XPS) and water contact angle (WCA) measurements, as well as atomic force microscopy (AFM) with 3D interactive visualization of the titanium surface morphology. It was found that physico-chemical surface characteristics of the as-received and the ECAP-modified CP titanium did not differ in any significant way, while the surface roughness at the nano-scale did. Optical profilometry performed on large scanning areas of approximately 225 μm × 300 μm showed that there was no significant difference between the roughness parameters R a and R q for surfaces in the two conditions, the overall level of roughness being lower for the ECAP-processed one. By contrast, topographic profile analysis at the nano-scale by AFM did reveal a difference in these parameters. This difference was sensitive to the size of the scanned surface area. A further two surface roughness parameters, skewness (R skw) and kurtosis (R kur), were also used to describe the morphology of titanium surfaces. It was found that the bacterial strains used in this study as adsorbates, viz. Staphylococcus aureus CIP 65.8 and Pseudomonas aeruginosa ATCC 9025, showed preference for surfaces of ECAP-processed titanium. S. aureus cells were found to have a greater propensity for attachment to surfaces of ECAP-modified titanium, while the attachment of P. aeruginosa, while also showing some preference for the ECAP-processed material, was less sensitive to the ECAP processing. [Copyright &y& Elsevier]