Search

Summary: In this work, sulfonated diblock copolymers (SDBCs) were prepared by polycondensation of sulfonated poly(ether‐ether‐ketone) (SPEEK) and hydrophobic oligomer, which were combined with sintered anatase titanium oxide (S‐An‐TiO2) to create a hybrid membrane for apply in proton exchange membrane fuel cells (PEMFCs) operating with low relative humidity (RH). Then, a series of composite membranes (SDBC/S‐An‐TiO2) were prepared by varying the wt% of S‐An‐TiO2 blended with SDBC. The results showed that appropriate quantity (ie, 15 wt%) of S‐An‐TiO2 can significantly improve the proton conductivity and physiochemical properties of prepared composite membrane, as well as the PEMFC performance and durability under 20% RH. The 1.5 wt% of SDBC/S‐An‐TiO2 offers high current output, power output, and durability values at 60°C under 20% RH, which are 0.207 A cm−2, 0.074 W cm−2 and over 90 hours, respectively. These results can be attributed to the good interfacial compatibility between S‐An‐TiO2 and SDBC. [ABSTRACT FROM AUTHOR]

The development of potential and novel proton exchange membranes (PEMs) is imperative for the further commercialization of PEM fuel cells (PEMFCs). In this work, phosphotungstic acid (PWA) and graphene oxide (GO) were integrated into sulfonated poly(arylene ether) (SPAE) through a solution casting approach to create a potential composite membrane for PEMFC applications. Thermal stability of membranes was observed using thermogravimetric analysis (TGA), and the SPAE/GO/PWA membranes exhibited high thermal stability compared to pristine SPAE membranes, owing to the interaction between SPAEK, GO, and PWA. By using a scanning electron microscope (SEM) and atomic force microscope (AFM), we observed that GO and PWA were evenly distributed throughout the SPAE matrix. The SPAE/GO/PWA composite membrane comprising 0.7 wt% GO and 36 wt% PWA exhibited a maximum proton conductivity of 186.3 mS cm−1 at 90 °C under 100% relative humidity (RH). As a result, SPAE/GO/PWA composite membrane exhibited 193.3 mW cm−2 of the maximum power density at 70 °C under 100% RH in PEMFCs. [ABSTRACT FROM AUTHOR]

A series of anion exchange membranes composed of partially fluorinated poly(arylene ether sulfone)s (PAESs) multiblock copolymers bearing quaternary ammonium groups were synthesized with controlled lengths of the hydrophilic precursor and hydrophobic oligomer via direct polycondensation. The chloromethylation and quaternization proceeded well by optimizing the reaction conditions to improve hydroxide conductivity and physical stability, and the fabricated membranes were very flexible and transparent. Atomic force microscope images of quaternized PAES (QN-PAES) membranes showed excellent hydrophilic/hydrophobic phase separation and distinct ion transition channels. An extended architecture of phase separation was observed by increasing the hydrophilic oligomer length, which resulted in significant improvements in the water uptake, ion exchange capacity, and hydroxide conductivity. Furthermore, the open circuit voltage (OCV) of QN-PAES X10Y23 and X10Y13 was found to be above 0.9 V, and the maximum power density of QN-PAES X10Y13 was 131.7 mW cm−2 at 60 °C under 100% RH. [ABSTRACT FROM AUTHOR]

Sulfonated poly(arylene biphenylether sulfone)-poly(arylene ether) (SPABES-PAE) block copolymers by controlling the molar ratio of SPABES and PAE oligomers were successfully synthesized, and the performances of SPABES-PAE (1:2, 1:1, and 2:1) membranes were compared with Nafion 212. The prepared membranes including fluorinated hydrophobic units were stable against heat, nucleophile attack, and physio-chemical durability during the tests. Moreover, the polymers exhibited better solubility in a variety of solvents. The chemical structure of SPABES-PAEs was investigated by 1H nuclear magnetic resonance (1H NMR), Fourier transform infrared spectroscopy (FT-IR), and gel permeation chromatography (GPC). The membrane of SPABES-PAEs was fabricated by the solution casting method, and the membranes were very flexible and transparent with a thickness of 70–90 μm. The morphology of the membranes was observed using atomic force microscope and the ionic domain size was proved by small angle X-ray scattering (SAXS) measurement. The incorporation of polymers including fluorinated units allowed the membranes to provide unprecedented oxidative and dimensional stabilities, as verified from the results of ex situ durability tests and water uptake capacity, respectively. By the collective efforts, we observed an enhanced water retention capacity, reasonable dimensional stability and high proton conductivity, and the peak power density of the SPABES-PAE (2:1) was 333.29 mW·cm−2 at 60 °C under 100% relative humidity (RH). [ABSTRACT FROM AUTHOR]