Search

Herein, a scheme of Sr2+/Ca2+ ion substitution was employed to simultaneously regulate the defect and intervalence charge transfer (IVCT) state of Sr2−xCaxNb2O7:Pr3+ phosphors, resulting in a dual-modulation strategy for enhancing phosphor thermal stability. [ABSTRACT FROM AUTHOR]

Praseodymium (Pr3+) ion and the transition metal vanadium (V5+) ion with d0 electronic configuration can form an intervalence charge transfer (IVCT) band, which can function both as a compensatory channel for its red emission and as a quenching channel, thus affecting the luminescence thermal stability of the phosphors. Research studies reveal that the emission of Pr3+ in the YVO4 matrix can be quenched by the IVCT mechanism, thereby limiting the application of phosphors. As such, the present contribution is based on the solid solution replacement strategy to inhibit the constitutent of the IVCT quenching channel and thus improve thermal stability. Therefore, phosphonium (P5+) with a valence state matching V5+ and a similar ion radius was selected for the V/P substitution. It lacks a d0 electron configuration, preventing the formation of an IVCT band with Pr3+ and thereby inhibiting the construction of the quenching channels to enhance thermal stability. While the empirical formula of IVCT indicates a decrease in the IVCT energy level from 3.32438 to 3.06251 eV upon the introduction of P5+, the PLE spectra demonstrate a sharp reduction in IVCT intensity, i.e., weakening of the quenching channel. The thermal stability of the phosphors at different excitation locations was enhanced with the rise of P5+ concentration. When excited at the 3P2 level, the Y0.995PO4:0.5%Pr3+ phosphor demonstrated highly stable red emission from 303 to 523 K, with a luminescence integrated intensity ranging from 95.5% to 105.3% compared to that at 303 K. This research provides a novel approach for inhibiting the IVCT quenching channel and broadens the commercial value of YVO4:Pr3+ phosphor for various applications. [ABSTRACT FROM AUTHOR]

Most praseodymium-doped red-emitting phosphors need high-temperature synthesis conditions with a reducing atmosphere. The niobate matrix selected in this work provides a sufficient electron-rich-site environment for praseodymium through charge migration, and praseodymium can be self-reduced in air atmosphere, which is safe and environmentally friendly. By building the [NbO6] group → Pr3+ energy transfer and finely modifying the doping concentration of Pr3+ ions, we constructed a dual-luminescence-system of the [NbO6] group and Pr3+. Thereby, optical temperature measurement based on fluorescence intensity ratio (FIR) technology of Pr3+ ions and [NbO6] groups was carried out using non-thermal coupling pairs, through the Boltzmann fitting and integral calculation, the maximum Sr and Sa values were 2.25% K−1 and 0.0049 K−1 at 403 K and 443 K, respectively, the Sr value is four times that obtained from the thermal coupling of Pr3+ ions, which exceeded most values previously reported for the fluorescence powder. Accordingly, we also studied the thermal sensitivity of Er3+ ions and Eu3+ ions mono-doped CaNb2O6 substrates. Results reveal that CaNb2O6:Pr3+/Er3+/Eu3+ phosphors have splendid temperature sensitivity and have far-reaching application prospects in the field of temperature measurements. [ABSTRACT FROM AUTHOR]