A two-step heating strategy was proposed to fabricate transparent MgAlON ceramics by solid-state reaction of MgAl 2 O 4 and AlON powders via pressureless sintering. By dwelling 60 min at 1700 ℃ followed by 150 min at 1880 ℃, highly infrared transparent MgAlON ceramics with transmittance up to 80.4 % were successfully fast prepared. The phase transformation and microstructure evolution during heating from 1400 ℃ to 1800 ℃ and dwelling at 1700 ℃ for 0–90 min was thoroughly studied to reveal the solid-state reaction and densification mechanism of MgAlON by two-step heating. Surprisingly, it was found that the grown grains could break during dwelling at 1700 ℃. This secondary massive fragmentation of grown grains resulted in the minimized grain size and improved moveability of grains, which in turn prompted fast and high densification with pore free in the following sintering step. The grain breakage at 1700 ℃ could be attributed to the decomposition of AlON and formation of MgAlON. [ABSTRACT FROM AUTHOR]

Based on the reaction sequence during synthesis of MgAlON powder by solid-state reaction, a two-step heating strategy is proposed to low-temperature fabricate fine MgAlON powder of high sinterability by using MgAl 2 O 4 as Mg source, respectively together with AlON and Al 2 O 3 +AlN. By introduction of an additional dwelling at 1550 °C to the first heating step, more α-Al 2 O 3 dissolve into the solid solution at this temperature. By this way, overlarge particles of Al 2 O 3 by agglomeration could be avoided in the next heating step to enable fast full reaction at a lower temperature. By dwelling 30 min at 1550 °C followed by 60 min at 1700 °C, single phase MgAlON powders were successfully prepared by solid-state reaction of all the two batches. The fine MgAlON powder synthesized by MAS+Al 2 O 3 +AlN batch exhibited high sinterability as the MgAlON ceramics pressureless sintered by this powder at 1880 °C without dwelling showed a transmittance up to 68.3%. The phase assemblage and morphology evolution of the mixture during solid-state reaction were monitored, which verified the effectiveness of the proposed two-step heating strategy. The low synthesis temperature of the two-step heating scheme benefits to prepare pure MgAlON powder with small particle size. [ABSTRACT FROM AUTHOR]