Search

The aim of this paper is to investigate the WC-10Co-4Cr coatings reinforced with 5 % and 10 % of yttria-stabilized zirconia (Y2O3/ZrO2; YSZ) nanoparticles deposited on the CA6NM turbine steel by using the high-velocity oxy-fuel (HVOF) thermal spraying technique. In the HVOF technique, the hot jet of the semi-solid particles strikes against the workpiece and creates a layer of coating of varying thickness on the substrate material. The coatings fabricated with HVOF were analyzed by scanning electron microscope (SEM) / energy-dispersive x-ray spectroscopy (EDS). The phase identification of a crystalline material was made with the x-ray diffraction (XRD) technique. The mecha­nical properties in terms of porosity, surface roughness and microhardness of the nanocomposite coatings were also evaluated. The SEM/EDS analysis showed that dense and homogeneous coatings were developed by the reinforcement of YSZ nanoparticles. The peaks of XRD graphs of WC-10Co-4Cr coating reinforced with 5 and 10 % of YSZ nanoparticles revealed that the WC was present as a major phase and W2C, Co3W3C, Co, Co6W6C, Co6W and Y2O3/ZrO2 nanoparticles were observed as a minor phase. The porosity level decreased up to 42 and 56 % by the addition 5 and 10 % of YSZ nanoparticles as compared with conventional WC-10Co-4Cr coating. The surface roughness values for WC-10Co-4Cr conventional coating, 95 % (WC-10Co-4Cr) + 5 % YSZ and 90 % (WC-10Co-4Cr) + 10 % YSZ nanocomposite coated samples were found to be 5.03, 4.89 and 4.28 respectively. The nanocomposite coatings reinforced with 10 % YSZ nanoparticles exhibited the highest microhardness value (1278 HV). The WC-10Co-4Cr coatings reinforced with 10 % of YSZ nanoparticles resulted in low porosity, low surface roughness and high microhardness. During the coating process, the nanoparticles of YSZ flow into the pores and are dispersed in the gaps between the micrometric WC particles and provide a better shield to the substrate material. The WC-10Co-4Cr with 10 % of YSZ nanoparticles showed better results in terms of mecha­nical and microstructural properties during the investigation.

In the present work, 5 and 10 wt.% yttria-stabilized zirconia (YSZ) nanoparticles were reinforced in Ni-20Cr powder and deposited on boiler tube steel using a high-velocity oxy-fuel spraying process. The effect of YSZ reinforcement on microhardness, surface roughness and porosity were investi­ga­ted. The hardness was the highest for nanocomposite coating reinforced with 10 wt.% YSZ and hard­ness was found to increase with a decrease in porosity. The coating microstructure and elements were characterized using field emission scanning electron microscopy (FE-SEM) with an energy dispersive spectroscope (EDS). The constituents of the coating were identified using X-ray diffracto­meter. It was found that the composite coating with 10 wt.% YSZ reinforced nanocomposite coating has the highest microhardness, in the range of 1008-1055 hv. During the coating process, nano YSZ particles were dispersed in the gaps between the micrometric Ni-20Cr particles, providing a better coating matrix than conventional Ni-20Cr. The Ni-20Cr with 10 wt.% of YSZ nanoparticles showed better results in terms of mechanical and microstructural properties during the investigation.