Search

A series of high molecular weight polymers were prepared by ring opening polymerization of L-lactide (L-LA), 1,3-trimethylene carbonate (TMC) and glycolide using stannous octoate as catalyst. The resulting polymers were characterized by gel permeation chromatography, (1)H nuclear magnetic resonance, differential scanning calorimeter and tensile tests. All the polymers present high molecular weights. Compared with PLLA and PTLA copolymers, the terpolymers exhibit interesting properties such as improved toughness and lowered crystallinity with only slightly reduced mechanical strength. In vivo degradation was performed by subcutaneous implantation in rats to evaluate the potential of the copolymers as bioresorbable coronary stent material. The results show that all the polymers conserved to a large extent their mechanical properties during the first 90 days, except the strain at break which exhibited a strong decrease. Meanwhile, significant molecular weight decrease and weight loss are detected in the case of terpolymers. Therefore, the PTLGA terpolymers present a good potential for the development of totally bioresorbable coronary stents.

The characterization of the hydrophobicity of polymer compounds in solution remains a challenging issue of importance, especially for biomedical or pharmaceutical applications. To our knowledge, there is no data of polymer hydrophobicity (log D) in the literature. In this work, for the first time, the log D distributions of cationic polymers were characterized using micellar or microemulsion electrokinetic chromatography at physiological pH. The log D distributions of the polymer samples were obtained from the electrophoretic/chromatographic retardation of the polymer derivatives in presence of neutral micelles (or neutral microemulsion), using small cationic molecules for calibration. Separating electrolytes were based on a TRIS–chloride buffer containing a neutral surfactant (polyoxyethyleneglycoldodecyl ether) for the formation of micelles (in water) or microemulsion (in water/n-pentanol mixture).The log D distributions obtained at pH 7.4 using this method were in good agreement with the chemical structures of cationic polypeptides: poly(lys, phe) 1:1 > poly(lys, tyr) 1:1 > poly(lys, trp) 4:1 > poly(lys, ser)3:1 > poly(l-lysine), where x:y represents the molar ratio of each amino acid in the copolymer. Weight average octanol–water log D values and the dispersion of the log D distribution were also defined and determined for each polymer sample.

This paper aims to evaluate the potential of totally bioresorbable composites as cardiovascular stent material. Copolymers were synthesized by ring-opening polymerization of L-lactide (LLA) and 1,3-trimethylene carbonate (TMC) with LLA-TMC ratios of 3/1, 4/1, and 5/1 and characterized by nuclear magnetic resonance (NMR), gel permeation chromatography (GPC), and differential scanning calorimetry (DSC). Wt. 5% of poly( L-lactide)- co-(glycolide) (PLGA) fibers are used to reinforce PTMC-LLA copolymer matrices to prepare totally bioresorbable composites. Heat treatment under vacuum and oxygen plasma treatment are applied to improve the mechanical performance of the composites in terms of eliminating the imperfections inside, enhancing interfacial affinity, surface roughness, and enriching surface oxidative chemical bonds. After plasma treatment, the viscosity and tensile strength of the fibers decrease, but the surface chemical bonds are enriched and surface roughness is increased. The composites with 15-min plasma-treated fibers and 2 h heat treatment exhibit the highest tensile strength of 46 MPa, i.e., very close to that of PLLA (48 MPa), which is usually used as biodegradable stent material. Moreover, the tensile modulus of the above composite is 1711 MPa, which is only 34% of PLLA's modulus (4985 MPa). Therefore, novel composites with sufficient tensile strength and better flexibility are obtained as promising cardiovascular stent material. POLYM. ENG. SCI., 2011. © 2011 Society of Plastics Engineers [ABSTRACT FROM AUTHOR]