Search

Prediction studies of advanced (bio)degradable polymeric materials are crucial when their potential applications as compostable products with long shelf-life is considered for today's market. The aim of this study was to determine the effect of the polylactide (PLA) content in the blends of PLA and poly(butylene adipate-co-terephthalate) (PBAT); specifically how the material's thickness corresponded to changes that occurred in products during the degradation process. Additionally, the influence of talc on the degradation profile of all samples in all environments was investigated. It was found that, differences in the degradation rate of materials tested with a similar content of the PLA component could be caused by differences in their thickness, the presence of commercial additives used during processing or a combination of both. The obtained results indicated that the presence of talc may interfere with materials behavior towards water and consequently alter their degradation profile., (Copyright © 2018 Elsevier Ltd. All rights reserved.)

The public awareness of the quality of environment stimulates the endeavor to safe polymeric materials and their degradation products. The aim of the forensic engineering case study presented in this paper is to evaluate the aging process of commercial oxo-degradable polyethylene bag under real industrial composting conditions and in distilled water at 70°C, for comparison. Partial degradation of the investigated material was monitored by changes in molecular weight, thermal properties and Keto Carbonyl Bond Index and Vinyl Bond Index, which were calculated from the FTIR spectra. The results indicate that such an oxo-degradable product offered in markets degrades slowly under industrial composting conditions. Even fragmentation is slow, and it is dubious that biological mineralization of this material would occur within a year under industrial composting conditions. The slow degradation and fragmentation is most likely due to partially crosslinking after long time of degradation, which results in the limitation of low molecular weight residues for assimilation. The work suggests that these materials should not be labeled as biodegradable, and should be further analyzed in order to avoid the spread of persistent artificial materials in nature., (Copyright © 2017 Elsevier Ltd. All rights reserved.)

This paper presents a forensic engineering study on the biodegradation behaviour of prototype packaging thermoformed from PLA-extruded film and plain PLA film under industrial composting conditions. Hydrolytic degradation in water was conducted for reference. The effects of composting duration on changes in molar mass, glass transition temperature and degree of crystallinity of the polymeric material were monitored using gel permeation chromatography (GPC) and differential scanning calorimetry (DSC). The chemical structure of water soluble degradation products of the polymeric material was determined using nuclear magnetic resonance (NMR) and electrospray ionization mass spectrometry (ESI-MS). The results show that the biodegradation process is less dependent on the thermoforming process of PLA and more dependent on the composting/degradation conditions that are applied. The increase in the dispersity index, leading to the bimodal molar mass distribution profile, suggests an autocatalytic hydrolysis effect at the early stage of the composting process, during which the bulk hydrolysis mechanism dominantly operates. Both the prototype PLA-packaging and PLA rigid film samples were shown to have a gradual increase in opacity due to an increase in the degree of crystallinity., (Copyright © 2016 Elsevier Ltd. All rights reserved.)

The aim of the present study was to determine the degradability of aliphatic polyurethanes, based on a different amount of synthetic, atactic poly[(R,S)-3-hydroxybutyrate] (a-PHB), in hydrolytic (phosphate buffer) and oxidative (H2O2/CoCl2) solutions. The soft segments were built with atactic poly[(R,S)-3-hydroxybutyrate] and polycaprolactone or polyoxytetramethylenediols, whereas hard segments were the reaction product of 4,4′-methylenedicyclohexyl diisocyanate and 1,4-butanediol.The selected properties - density and morphology of polymer surfaces - which could influence the sensitivity of polymers to degradation processes - were analyzed.The analysis of molecular mass (GPC), thermal properties (DSC) and the sample weight changes were undertaken to estimate the degree of degradability of polymer samples after incubation in environments studied.Investigated polyurethanes were amorphous with the very low amount of crystalline phases of hard segments.The polyurethane synthesized with a poly[(R,S)-3-hydroxybutyrate] and polyoxytetramethylenediol at a molar ratio of NCO:OH=3.7:1 (prepolymer step) appeared as the most sensitive for both degradative solutions. Its weight and molecular mass losses were the highest in comparison to other investigated polyurethanes.It could be expected that playing with the amount of poly[(R,S)-3-hydroxybutyrate] in polyurethane synthesis the rate of polyurethane degradation after immersion in living body would be modeled. [ABSTRACT FROM AUTHOR]

New conjugated poly(ketanil)s, i.e. polymers containing ketimine groups in their main chain, have been synthesized from 1,4-phenylenediamine (or benzidine) and five different diketones via polycondensation with the goal to obtain new materials of tunable luminescent properties. It is demonstrated that both the absorption and photoluminescence spectra can be modified not only by changing the ratio of conjugated to non-conjugated segment in the polymer main chain but also via acid–base doping involving the protonation of ketimine groups. By combining these two methods, it is possible to precisely tune the emission spectra of poly(ketanil)s in the spectral range of 520–580 nm. The use of bifunctional protonating agents, containing plasticizing groups, for example 1,2-(di-2-ethylhexyl)ester of 4-sulfophthalic acid (DEHEPSA), in addition to the modification of the luminescent spectra, leads to a lowering of the glass transition temperature (Tg) of the polymers studied by approximately 100–150 K. Thus, the majority of the polymers studied exhibit, in their doped state, the Tg below room temperature leading to flexible films of good mechanical properties. [Copyright &y& Elsevier]